采用置换-扩散法制备了储氢材料Mg2NiH4,用XRD,ICP和DSC-TG方法对其结构进行了表征.用热分析法(DSC)研究了Mg2NiH4对高氯酸铵(AP)热分解过程的影响.研究结果表明,Mg2NiH4对AP热分解过程有较大影响.Mg2NiH4可以显著促进AP的低温热分解过程,降低高温热分解温度,使DSC表观分解热明显增大.随着加入量的增加,Mg2NiH4对AP热分解的催化促进作用增强,当Mg2NiH4加入的质量分数为30%时,DSC表观分解热最大.吸氢量越大,储氢材料对AP的催化促进作用越强.Mg2NiH4催化促进AP分解过程的作用机理为:Mg2NiH4分解释放的H2及Mg和Ni与AP分解产物发生反应.
Magnesium-based hydrogen storage material Mg2NiH4 was prepared with replacement-diffusion method and its structure was determined by XRD, ICP and DSC-TG. The thermal decomposition behavior of ammonium perchlorate（AP） was investigated in the presence of Mg2NiH4 by the method of DSC. The results show that Mg2NiH4 had obvious influence on the thermal decomposition of AP. Mg2NiH4 showed an evident catalytic effect on the lower temperature thermal decomposition of AP, and the higher thermal decomposition temperature of AP was decreased by Mg2NiH4, with a clear increase at DSC heat release. The catalytic effect of Mg2NiH4 on the thermal decomposition of AP was enhanced with the increase in content, and the DSC heat release was at its biggest value when the content of Mg2NiH4 was 30% （mass fraction）. With the increase of hydrogen storage, the catalytic effect became stronger. The mechanism of catalyzing the thermal decomposition of AP is as follows ： HE released from Mg2 NiH4 and Mg, Ni reacted with the decomposed product of AP.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2007年第8期1420-1423,共4页
Chemical Journal of Chinese Universities
基金
国家自然科学基金(批准号:50306008)资助
关键词
镁基储氢材料
制备
高氯酸铵
热分解
催化性能
Magnesium-based hydrogen storage material
Preparation
Ammonium perchlorate
Thermal decomposition
Catalysis property