摘要
Transformation induced plasticity （TRIP） and twinning induced plasticity （TWlP） effects had been widely studied in single austenite steel. But in duplex γ ＆ α（δ） phase, such as welding materials of stainless steel, they had been less studied. Tensile shear loading experiment of resistance spot welding specimens prepared with 2 mm 301L sheets, was carried out at 15℃ and -50℃. Optical microscopy and scanning electron microscopy （SEM） as well as X-ray diffraction （XRD） were used to investigate the microstructure of weld nugget, and specimens fracture surface. The results showed that the initial weld nugget was composed of 8.4% α（δ） ferrite and 91.6% austenite. Tensile shear load bearing capacity of spot welding specimen at -50℃ was 24.8 kN, 17.7% higher than that at 15℃. About 78.5 vol. pct. martensite transformation was induced by plastic deformation at -50℃, while about 67.9 vol. pct transformation induced at 15℃. The plasticity of spot welding joint decreased with the decline of experimental temperature.
Transformation induced plasticity （TRIP） and twinning induced plasticity （TWlP） effects had been widely studied in single austenite steel. But in duplex γ ＆ α（δ） phase, such as welding materials of stainless steel, they had been less studied. Tensile shear loading experiment of resistance spot welding specimens prepared with 2 mm 301L sheets, was carried out at 15℃ and -50℃. Optical microscopy and scanning electron microscopy （SEM） as well as X-ray diffraction （XRD） were used to investigate the microstructure of weld nugget, and specimens fracture surface. The results showed that the initial weld nugget was composed of 8.4% α（δ） ferrite and 91.6% austenite. Tensile shear load bearing capacity of spot welding specimen at -50℃ was 24.8 kN, 17.7% higher than that at 15℃. About 78.5 vol. pct. martensite transformation was induced by plastic deformation at -50℃, while about 67.9 vol. pct transformation induced at 15℃. The plasticity of spot welding joint decreased with the decline of experimental temperature.