摘要
A new type of zeolite La-USL （ultra stable zeolite L （zeolite USL） modified by La）, which has superior activity, stability and selectivity in catalytic cracking of hydrocarbons and thus can be used as an active catalyst component, is reported in this paper. The zeolite L with relative crystallinity of above 90% was synthesized by the hydrothermal crystallization method under optimum conditions and characterized by means of XRD, NH3-TPD and isotherm adsorption techniques. The in-situ synthesized zeolite L with a SiO2/Al2O3 mole ratio of 5-6 was modified by cation ion exchange, hydrothermal dealumination and chemical modifications with La in order to prepare La-containing USL with a higher framework SiO2/Al2O3 mole ratio of 15-30. The modified zeolite La-USL was used as an active additive component of fluid catalytic cracking （FCC） catalyst and the resulting catalysts were evaluated by microactivity test （MAT） and fixed-fluidized bed （FFB） experiments using heavy oil as feedstock. The influence of La content in La- USL on cracking product distribution, gasoline group composition and research octane number （RON） was investigated. The results showed that when La content in La-USL was 0.8 wt%, the addition of the corresponding La-USL could result in a FCC catalyst that produced significant improvement in product distribution and gasoline quality.
A new type of zeolite La-USL （ultra stable zeolite L （zeolite USL） modified by La）, which has superior activity, stability and selectivity in catalytic cracking of hydrocarbons and thus can be used as an active catalyst component, is reported in this paper. The zeolite L with relative crystallinity of above 90% was synthesized by the hydrothermal crystallization method under optimum conditions and characterized by means of XRD, NH3-TPD and isotherm adsorption techniques. The in-situ synthesized zeolite L with a SiO2/Al2O3 mole ratio of 5-6 was modified by cation ion exchange, hydrothermal dealumination and chemical modifications with La in order to prepare La-containing USL with a higher framework SiO2/Al2O3 mole ratio of 15-30. The modified zeolite La-USL was used as an active additive component of fluid catalytic cracking （FCC） catalyst and the resulting catalysts were evaluated by microactivity test （MAT） and fixed-fluidized bed （FFB） experiments using heavy oil as feedstock. The influence of La content in La- USL on cracking product distribution, gasoline group composition and research octane number （RON） was investigated. The results showed that when La content in La-USL was 0.8 wt%, the addition of the corresponding La-USL could result in a FCC catalyst that produced significant improvement in product distribution and gasoline quality.