采用阳极氧化法在钛片上制备了TiO2纳米管阵列光电极,利用扫描电子显微镜(SEM)和X射线衍射仪(XRD)对TiO2纳米管的形貌和结构进行了表征,详细考察了氧化工艺参数对纳米管阵列形貌的影响,并通过稳态光电响应技术对TiO2纳米管电极的光电化学性能进行了研究．结果表明,在1wt％HF电解液中,控制氧化电压为20V,反应30min后,在Ti表面获得了垂直导向的TiO2纳米管阵列,孔径约为90nm,管壁厚度约为10nm．经600℃退火处理后,TiO2纳米管阵列为锐钛矿型与金红石型的混晶结构,此时电极的光电性能最佳,与TiO2纳米多孔膜电极相比,光电性能大幅提高．
TiO2 nanotube arrays photoelectrodes were fabricated by anodic oxidation on a pure titanium sheet. The morphology and structure of the nanotube arrays were characterized by SEM and XRD. Oxidation parameters for preparation were investigated. The photoelectrochemical properties of the TiO2 nanotube arrays electrodes were evaluated by steady-state photocurrent response. The results show that the vertical oriented TiO2 nanotube arrays can be obtained at 20V for 30min in lwt% HF solution. And the aperture size of nanotubes is about 90nm and the thickness of tube wall is about 10nm. The structure of nanotube arrays is a mixture of anatase and rutile through annealed at 600℃. The results of photoelectric testing show that photoelectrochemical properties of TiO2 nanotube arrays electrode annealed at 600℃ are optimum. Compared with TiO2 nanoporous films, the properties of the TiO2 nanotube arrays are enhanced remarkably.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2007年第2期349-353,共5页
Journal of Inorganic Materials
基金
国家自然科学基金(50271046)
国家教育部博士点基金(20030056034)