摘要
本文主要研究了Fe73.5Cu1Nb3Si13.5B9纳米晶带材在不同的热处理工艺和压应力条件下的软磁性能变化情况。结果表明:带材在550℃×1h热处理工艺时将晶化成纳米晶材料,此时带材软磁性能最好;纳米晶带材的|μ|,受压应力影响大,尤其是在小于0.2MPa压应力作用下,软磁性能变化非常敏感,|μ|随压力增加而迅速下降;带材Q值在小于0.2MPa压应力作用下变化非常敏感,Q值随压力增加而迅速下降。当压应力大于0.2MPa时,Q值随压应力变化不明显,压应力不影响带材Q值随频率的变化规律。
The influence of heat treatment process and pressure on soft magnetic properties and magnetoelastic properties of Fe73.5Cu5Nb3Si13.5B9 nanocrystalline ribbons is studied. The results show that soft magnetic properties, such as saturation magnetic induction intensity, are most excellent when anneal process is at 550℃ for 1h and ribbons are nano-crystalled. There is a sensitivity zone at pressure, The amorphous ribbon is sensitive at 0 to 0. 2MPa. At first, the original magneto-conductivity is rapidly reduced with the increase of pressure in sensitivity zone. The sensitivity of Q value of ribbons is also very high and Q is urgently reduced with the increase of pressure in 0 to 0.2MPa sensitvity zone. Pressure doesn＇t effect the change law of Q with frequency.
出处
《金属功能材料》
CAS
2007年第1期12-15,共4页
Metallic Functional Materials
基金
江西省科技攻关项目(2004-3)
关键词
纳米晶
软磁性能
压磁性能
nano-crystal
soft magnetic properties
magnetoelastic properties