The nonwoven composites have sandwich structure, with the first and third layers being nonwovens and the middle layer of woven fabric. On the basis of tests of the single rip tearing strength and drawing out resistances of both the nonwoven composites and the woven fabric, the single rip tearing failure mechanism of the composites were analyzed. Then theoretical calculation model for the single rip tearing strength was established, which indicates that the breaking strength of warp and weft yams in the nonwoven composites, the density of warp and weft yarns and drawing out resistances are the main influencing factors. In the end, experimental verification was made, which shows that theoretical values conform to the measured values well.
The nonwoven composites have sandwich structure, with the first and third layers being nonwovens and the middle layer of woven fabric. On the basis of tests of the single rip tearing strength and drawing out resistances of both the nonwoven composites and the woven fabric, the single rip tearing failure mechanism of the composites were analyzed.Then theoretical calculation model for the single rip tearing strength was established, which indicates that the breaking strength of warp and weft yarns in the nonwoven composites, the density of warp and weft yarns and drawing out resistances are the main influencing factors. In the end,experimental verification was made, which shows that theoretical values conform to the measured values well.