The aluminum coating layer was formed on a copper substrate with lacal strain region by using the electrodeposited method. It was found that the particle shape of the coating deposited on the copper substrate is very sensitive to the strain extent of substrate. The large needle-like aluminum particles were observed on the substrate region with large local strain, indicating that substrate local strain may affect the shape of the deposited particles and promote the nucleation and growth of the deposited particles.
The aluminum coating layer was formed on a copper substrate with lacal strain region by using the electrodeposited method. It was found that the particle shape of the coating deposited on the copper substrate is very sensitive to the strain extent of substrate. The large needle-like aluminum particles were observed on the substrate region with large local strain, indicating that substrate local strain may affect the shape of the deposited particles and promote the nucleation and growth of the deposited particles.