合成了一种新型可降解阳离子聚(氨乙酰氧乙基天冬酰胺)盐酸盐(PAAEA.HCl),并由PAAEA.HCl与羧甲基纤维素钠(NaCMC)水溶液通过静电相互作用得到纳米级聚电解质复合物.同时,研究了该聚电解质溶液浓度、性质、离子强度对复合物粒径和ξ-电位的影响.结果表明,在蒸馏水中,聚电解质浓度为1.0 mmol/L、电荷比n+/n-为2制备得到的聚电解质复合物纳米粒子平均粒径为110 nm,ξ-电位为35 mV,其溶液在4℃时可以稳定保存一周.
A novel polycation, poly（a was prepared starting from L-aspartic acid. minoacetyloxyethylaspartamide） hydrochloride （PAAEA · HCI） The polyelectrolyte complex nanoparticles were ξ-ormed via the electrostatic interaction between poly （aminoacetyloxy-ethylaspartamide） hydrochloride and sodium carboxymethylcellulose. The effects of polyion concentration, solution properties, solution ionic strength on the sizes and zeta potentials of the formed nanoparticles were investigated. The size and ξ-potential of nan oparticles, prepared from a solution of poly（aminoacetyloxyethylaspartamide） hydrochloride in water （1.0 mmol/L） and a solution of sodium carboxymethylcellulose in water （1.0 mmol/L） at n＋/n- =2, are 110 nm and 35 mV, respectively. Thus obtained nanoparticles are stable within one week at 4 ℃.
出处
《武汉大学学报（理学版）》
CAS
CSCD
北大核心
2006年第4期385-390,共6页
Journal of Wuhan University:Natural Science Edition
基金
国家自然科学基金资助项目(20204009
20474045)
教育部留学回国人员基金资助项目(20315)
湖北省新型反应器与绿色化学工艺重点实验室开放课题资助项目
关键词
聚阳离子
羧甲基纤维素钠
聚电解质复合物
纳米粒子
polycation
sodium carboxymethylcellulose
polyelectrolyte complex （PEC）
nanoparticles