摘要
The volatilization behavior of Cu, Pb, Sn, Sb, Ni, Zn, Mn, Co, Cr, Cd during pyrolysis of waste printed circuit boards was investigated in a bench-scale fixed-bed pyrolysis system. It was found that volatility of heavy metals increases with operating temperature elevating, and bromine and vacuum have an obvious promoting effect on volatility of most of heavy metals. Over 99% weight of Cu and Ni are still remained in solid residue after pyrolysis, about 20% weight of Sb, Zn and Cd are transfered into liquid and gas during a pyrolysis process at 600 ℃, volatilization fractions of Pb, Sn, Mn, Co, Cr are less than 10% at the same conditions. The contents of heavy metals in liquid and gas products depend on not only volatility of metals, but also their initial contents in printed circuit boards, pyrolysis liquid and gas are primarily contaminated by Cu, Pb, Sn, Sb and Zn, their contents in liquid vary from 10^2 to 10^3 pg/mL, Mn, Co, Cr, Cd were detected only at very low level, less than 10 μg/mL.
<正> The volatilization behavior of Cu, Pb, Sn, Sb, Ni, Zn, Mn, Co, Cr, Cd during pyrolysis of waste printed circuit boards was investigated in a bench-scale fixed-bed pyrolysis system. It was found that volatility of heavy metals increases with operating temperature elevating, and bromine and vacuum have an obvious promoting effect on volatility of most of heavy metals. Over 99% weight of Cu and Ni are still remained in solid residue after pyrolysis, about 20% weight of Sb, Zn and Cd are transfered into liquid and gas during a pyrolysis process at 600℃, volatilization fractions of Pb, Sn, Mn, Co, Cr are less than 10% at the same conditions. The contents of heavy metals in liquid and gas products depend on not only volatility of metals, but also their initial contents in printed circuit boards, pyrolysis liquid and gas are primarily contaminated by Cu, Pb, Sn, Sb and Zn, their contents in liquid vary from 10~2 to 10~3 μg/mL, Mn, Co, Cr, Cd were detected only at very low level, less than 10 μg/mL.
基金
Supported by Science Technology Research Project of Guangdong Province(2003e32104)