摘要
The sub-micron sized YAG ： Ce phosphors were synthesized via a modified sol-gel method by peptizing nano-pesudoboehmite particulate. It is found that YAG phase from the dried gel powders appears at 1000 ℃ then the pure YAG phase exists at a relatively lower sintering temperature of 1400 ℃. The smaller sizes of phosphors in the ranges of 1 - 3 μm are obtained due to the contribution of seeding effects of nano-sized alumina particles to strengthen each step of the processes. Both the excitation and emission spectra of photoluminescence of the phosphor obtained at 1400 ℃ meet well with the spectroscopic requirements of the WLED phosphors.
The sub-micron sized YAG ： Ce phosphors were synthesized via a modified sol-gel method by peptizing nano-pesudoboehmite particulate. It is found that YAG phase from the dried gel powders appears at 1000 ℃ then the pure YAG phase exists at a relatively lower sintering temperature of 1400 ℃. The smaller sizes of phosphors in the ranges of 1 - 3 μm are obtained due to the contribution of seeding effects of nano-sized alumina particles to strengthen each step of the processes. Both the excitation and emission spectra of photoluminescence of the phosphor obtained at 1400 ℃ meet well with the spectroscopic requirements of the WLED phosphors.
基金
ProjectsupportedbytheNationalNaturalScienceFoundationofChina(50364002),NaturalScienceFoundationofTianjin(033601111,06YFJMJC02300)andNaturalScienceFoundationofTianjinUniversityofTechnology(Lg04032)