对球墨铸铁表面激光重熔过程中的重熔层开裂倾向及影响因素进行了详细的研究,通过对基体分别进行正火、淬火+回火后进行激光表面重熔的对比试验,考察了在相同的激光重熔工艺参数条件下进行表面重熔处理,发现球铁激光重熔处理前的预处理工艺对重熔过程中的重熔层开裂倾向影响很大。试验结果表明,预处理可以改变激光重熔时热影响区的大小、相变产物的显微组织形态,从而导致对重熔层相变应力的分布与大小,进而影响到激光重熔层的开裂倾向。为制定球铁激光重熔预处理的最佳工艺规范提供依据。
The remehed layer cracking susceptibility and its influencing factor during laser remelting the spheroidal graphite iron surface have been studied in detail. The contrast test was carried out for laser surface remehing varying substrate preheating. One is normaliz, the other is quench and temper. The surface remelting process with the same laser remelting processing parameters have been investigated. It was found that the effect of the spheroidal graphite iron preheating on cracking susceptibility of remehed layer was very great. The results were shown that the preheating is able to change the size of the heat-affected zone which was ：formed during laser remelting and the microstructure of the phase transformation product. The distribution and the size of the phase transformation stress in the remelted layer are changed. And it affects the cracking susceptibility of the remehed layer. Then it provided the best adjustment rule of the processing parameters.
出处
《长春工业大学学报》
CAS
2006年第2期87-90,共4页
Journal of Changchun University of Technology
基金
吉林省杰出青年基金资助项目(20030128)
吉林省工业引导基金资助项目(20030331)
关键词
球墨铸铁
激光表面重熔
预处理
spheroidal graphite iron
laser surface remelting
preheating treatment.