摘要
Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established. The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB. Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured. The micro-morphology and composition of Zn-Cr coming were analyzed through SEM, XPS, EDS and XRD. The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated. It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection. The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.
Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established. The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB. Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured. The micro-morphology and composition of Zn-Cr coming were analyzed through SEM, XPS, EDS and XRD. The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated. It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection. The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.
基金
ProjectsupportedbytheScienceandTechnologyFoundationofEducationMinistryofHebeiProvince(2002123)
Projectsup-portedbytheDoctoralFoundationofYanshanUniversity(B41)
ProjectsupportedbytheScienceandTechnologyFoundationofYanshanUniversity(YDJJ0169)