摘要
The 〈 110 〉 -oriented TTb0.3Dy0.7Fe1.95 polycrystalline alloy was magnetically annealed, and its influence on jump effect of magnetostriction was investigated. In the vacuum superconductive high magnetic field equipment, 〈 110 〉 -oriented Tb0.3Dy0.7Fe1.95 polycrystalline alloy of the directional solidification was annealed at 623 and 723 K for 5 min under the magnetic field vertical to specimen axis. It is found that magnetic annealing can enhance the jump effect under compressive stress, and increase the saturated magnetostriction coefficient λs, the λs of the magnetic annealing specimens at 623 K under 8.1 MPa is attained to 1950 × 10^-6, Magnetic annealing increases the maximum of dynamic magnetostriction coefficient, d33^max, as well as the magnetic field for d33^max under 8.1 MPa.
The 〈 110 〉 -oriented TTb0.3Dy0.7Fe1.95 polycrystalline alloy was magnetically annealed, and its influence on jump effect of magnetostriction was investigated. In the vacuum superconductive high magnetic field equipment, 〈 110 〉 -oriented Tb0.3Dy0.7Fe1.95 polycrystalline alloy of the directional solidification was annealed at 623 and 723 K for 5 min under the magnetic field vertical to specimen axis. It is found that magnetic annealing can enhance the jump effect under compressive stress, and increase the saturated magnetostriction coefficient λs, the λs of the magnetic annealing specimens at 623 K under 8.1 MPa is attained to 1950 × 10^-6, Magnetic annealing increases the maximum of dynamic magnetostriction coefficient, d33^max, as well as the magnetic field for d33^max under 8.1 MPa.