摘要
对高韧性管线用钢控轧控冷工艺制度、力能参数和产品质量的控制进行了测定、研究，并得出，此种管线用钢的轧制工艺制度为，出炉温度在１１５０℃左右，终轧温度为８００℃左右，卷取温度为６００℃左右，加速冷却速度为１５℃／Ｓ左右。
Measurement and study of controlled rolling and cooling technical procedure, force and power parameters as well as quality control about high toughness pipeline steel were taken. It is found that the better rolling technical procedure for this kind of steel is that temperature of delivery furnace is about 1150 ℃, finishing rolling temperature is about800 ℃, coiling temperature is about 600 ℃, accelerated cooling speed is about 15 ℃ /s.
出处
《轧钢》
1996年第3期11-15,共5页
Steel Rolling
关键词
控制轧制
控制冷却
管线钢
Pipeline steel, controlled rolling, controlled cooling