摘要
针对厚度为12mm的纯铝板材,采用自动双丝焊技术进行焊接工艺试验。试验结果表明:采用自动双丝焊技术焊接12mm厚纯铝板可一次性成形,单面焊双面成形。焊接过程稳定、焊缝成形好,焊接接头具有优良的焊接质量和力学性能。
Aiming at the pure aluminum plate in thickness of 12 mm, the welding technology test was carried out by adopting the automatic double-wire welding technique. The results indicated that the once welidng depth of penetration was 12 mm and one-side welding with back formation was realized. The welding process was stable and the shaping of the joints was good. The welding quality and mechanical properties of the joints were excellent.