通过集气实验、极化曲线和电化学阻抗谱等方法研究了碱土金属离子与乙二胺四乙酸(EDTA)对纯铝在4mo·lL-1KOH溶液中的协同缓蚀作用.实验结果表明铝在含0.02mol·L-1EDTA和饱和Ca(OH)2、Sr(OH)2的溶液中具有最小的腐蚀速率.EDAX分析表明碱土金属离子和EDTA没有参与到铝表面氧化膜的组成中,说明缓蚀剂是通过吸附在铝表面起作用的,这表明它们是界面型缓蚀剂而非相间型缓蚀剂.
The cooperative effects of alkaline earth metal ions and EDTA （ethylenediamine tetraacetic acid） on the corrosion inhibition of pure aluminum in 4 mol·L^-1 KOH solution were investigated by hydrogen collection, polarization curve and electrochemical impedance spectroscopy（EIS）. It was found that aluminum exhibits minimum corrosion rate in 4 mol·L^-1 KOH solution containing 0.02 mol·L^-1 EDTA, saturated Ca（OH）2 and saturated Sr（OH）2, EDAX analysis showed that alkaline earth metal ions and EDTA have no contribution to the formation of the surface film on aluminum. Therefore the inhibition effect may be caused by the adsorption of the inhibitor on aluminum surface, This fact indicates that these two ions act as interface inhibitors rather than inter-phase ones.
出处
《物理化学学报》
SCIE
CAS
CSCD
北大核心
2006年第3期312-315,共4页
Acta Physico-Chimica Sinica
基金
国家自然科学基金(50571091)
中国博士后科学基金(2004036151)资助
关键词
纯铝
碱性溶液
腐蚀
碱土金属
EDTA
缓蚀剂
Pure aluminum, Alkaline solution, Corrosion, Alkaline earth metal, EDTA, Inhibitc,r