氧化锆增韧HA/ZrO_2功能梯度涂层的TEM分析 被引量:1

TEM study on HA/ZrO_2 functional gradient coatings reinforenced by ZrO_2
在线阅读 下载PDF
导出
摘要 利用净能量控制的PRAXAIR4500型等离子喷涂系统,在钛合金基体上制备出HA/ZrO2功能梯度涂层,采用HTEM、XRD、SEM等对涂层过渡层ZrO2相的结构特征进行分析。结果表明:(1)富锆的过渡层存在ZrO23种晶型,主要以四方氧化锆为主,含有少量的立方氧化锆及微量的单斜氧化锆和CaZrO3,单斜氧化锆的出现说明材料内发生了四方氧化锆向单斜氧化锆马氏体相变,这种马氏体相变有利于提高HA材料的韧性;(2)生物活性功能涂层的富锆过渡层致密,与钛合金基体结合紧密,纯羟基磷灰石的表面层具有典型的多孔结构特征,整个涂层沿垂直基体方向从过渡层致密结构向表面层多孔结构过渡;涂层的这种结构特征有利于改善功能梯度涂层的综合性能,提高涂层与基体的结合强度,其结合强度达到48.6MPa。 The HA/ZrO2 functional gradient coatings were fabricated by net-energy-controlled plasma spraying equipment PRAXAIR 4500. The microstructure and phase of the Zr-riched gradient layer of the functional gradient coatings were investigated by H TEM, XRD, SEM. Experimental results showed, (1)there were three type of ZrO2 crystals in the Zr-riched gradient layer,including t-ZrO2 ,c-ZrO2 ,and m-ZrO2, which suggested the occurrence of a martensitic phase transformation from t-ZrO2 to c-ZrO2. The which martensitic phase transformation were responsible for the toughening of the TZP- reinforced HA/ZrO2 functional gradient coatings. (2)The Zrriched gradient layer of the coating was relative dense and adhered firmly Ti alloy. In contrast,the top-layer of the coating was relative porous with different-sized micropores. The texture of the coating was gradiently changed from dense gradient layer to the porous top layer. According to ASTM C633-79 standard,the bioactive functionally gradient coatings was 48.6MPa.
出处 《功能材料》 EI CAS CSCD 北大核心 2006年第3期405-407,414,共4页 Journal of Functional Materials
基金 国家自然科学基金资助项目(59932050 50272021) 广东省自然科学基金资助项目(980551)
关键词 ZRO2 功能梯度涂层 TEM 等离子喷涂 ZrO2 functionally gradient coatings TEM plasma spraying
  • 相关文献

参考文献8

  • 1Fu L,Khor K,Peng J.[J].Surface and Coating Technology,2000,127:66-75.
  • 2Dong Z,Khor K,Quek C,et al.[J].Biomaterials,2003,24:97-105.
  • 3Lee T,Yang C,Chang E,et al.[J].J Biomed Mater Res,2004,15 (4):652-660.
  • 4Chou B,Chang E.[J].Biomaterials,1999,20(19):1823-1832.
  • 5Heimann R,Itiravivong P,Promasa A.[J].J Med Assoc Thai,2003,86 (2):S422-431.
  • 6Gu Y,Khor K,Cheang P.[J].Biomaterials,2003,24(9):1603-1611.
  • 7Khor K,Fu L,Lim V,et al.[J].Materials Science and Engineering,2000,A276:160-166.
  • 8Claussen N.[J].Materials Science and Engineering,1985,71:21-38.

同被引文献27

  • 1吴振军,何莉萍,陈宗璋.含钙阳极氧化铝的制备及其体外性能[J].中国有色金属学报,2005,15(10):1572-1576. 被引量:3
  • 2孔祥荣,彭鹏,孙桂香,郑文君.二氧化钛纳米管的研究进展[J].化学通报,2007,70(1):8-13. 被引量:15
  • 3DIAO J,REN D,JAMES R,LEE K.A surface modification strategy on silicon nitride for developing biosensors[J].Anal Biochem,2005,343(2):322-328.
  • 4BESSUEILLE F,DUGAS V,VIKULOV V,CLOAREC J,SOUTEYRAND E,MARTIN J.Assessment of porous silicon substrate for well-characterised sensitive DNA chip implement[J].Biosensors and Bioelectronics,2005,21(6):908-916.
  • 5ARCHER M,CHRISTOPHERSEN M,FAUCHET P M.Electrical porous silicon chemical sensor for detection of organic solvents[J].Sensors and Actuators B,2005,106(1):347-357.
  • 6ZAURIA S,MARTELET C,JAFFREZIC R,MGAIETH R,MAAREF H,LAMARTINE R.Porous silicon a transducer material for a high-sensitive biochemical sensor:Effect of a porosity,pores morphologies and a large surface area on a sensitivity[J].Thin Solid Films,2001,383(1/2):325-327.
  • 7BHARAT B,DHARMA R T,MATTHEW T K,STEPHEN C L.Morphology and adhesion of biomolecules on silicon based surfaces[J].Acta Biomater,2005,1(3):327-341.
  • 8SUET P L,WILLIAMS K A,CANHAM L T,NICOLAS H V.Evaluation of mammalian cell adhesion on surface-modified porous silicon[J].Biomaterials,2006,27(6):4538-4546.
  • 9DING Yan-jun,LIU Jia,WANG Hua,SHEN Guo-li,YU Ru-qin.A piezoelectric immunosensor for the detection of α-fetoprotein using an interface of gold/hydroxyapatite hybrid nanomaterial[J].Biomaterials,2007,28(12):2147-2154.
  • 10LIU X Y,FU R K,POON R W,CHEN P,CHU P K,DING C X.Biomimetic growth of apatite on hydrogen-implanted silicon[J].Biomaterials,2004,25(25):5575-5581.

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部