High-quality oxide semiconductor ZnO thin films were prepared on single-crystal sapphire and baAlO3 substrates by pulsed laser deposition （PLD） in the mixture gas of hydrogen and argon. Low resistivity n-type ZnO thin films with smoother surface were achieved by deposition at 600℃ in 1Pa of the mixture gas. in addition, ferromagnetism was observed in Co-doped ZnO thin films and rectification Ⅰ - Ⅴ curves were found in p-GaN/n-ZnO and p-CdTe/n-ZnO heterostructure junctions. The results indicated that using mixture gas of hydrogen and argon in PLD technique was a flexible method for depositing high-quality n-type oxide semiconductor films, especially for the multilayer thin film devices.
High-quality oxide semiconductor ZnO thin films were prepared on single-crystal sapphire and baAlO3 substrates by pulsed laser deposition （PLD） in the mixture gas of hydrogen and argon. Low resistivity n-type ZnO thin films with smoother surface were achieved by deposition at 600℃ in 1Pa of the mixture gas. in addition, ferromagnetism was observed in Co-doped ZnO thin films and rectification Ⅰ - Ⅴ curves were found in p-GaN/n-ZnO and p-CdTe/n-ZnO heterostructure junctions. The results indicated that using mixture gas of hydrogen and argon in PLD technique was a flexible method for depositing high-quality n-type oxide semiconductor films, especially for the multilayer thin film devices.
基金
Project supported by the National Natural Science Foundation of China （Grant No 19974001） and the National Key Basic Research Special Foundation of China （Grant No NKBRSF G1999064604 and G2000036505）.