用溶胶-凝胶(Sol-Gel)法制备了不同二氧化硅含量的PVA/S iO2杂化纺丝液,将其电纺成纤维膜.XRD结果表明,杂化电纺纤维膜的结晶度较纯PVA电纺纤维膜小;FTIR证实了PVA的羟基与正硅酸乙酯水解后的羟基发生了缩合反应,杂化电纺纤维膜是以网络结构形式相结合的;FESEM表明,PVA/S iO2质量比为4∶1时,纤维光滑,分散比较均匀.随着二氧化硅含量的增加,纤维直径变细,纺锤形珠节结构增多.加入金属盐NaC l和MgC l2后,纤维直径变细,圆形珠节增多.从理论上分析了纤维膜结构形态的形成机理.
The spin solutions of poly （vinyl alcohol）/silica hybrid materials with different silica contents were prepared by sol-gel method, then fiber membranes were obtained by electrospinning. XRD result indicated that the degree of crystallinity of hybrid electrospun fiber membranes declined comparing with pure PVA electrospun fiber membrane. FFIR showed that hydroxyl in PVA condensed with hydroxyl of hydrolyzing tetraethoxysilane, the fiber material with a network configuration existed. SEM revealed that when PVA/SiO2 mass ratio was 4： 1, the fibers smoothed and uniformed. With increasing of silica content, fiber diameter became fine and spindly beads increased. The fiber diameter became fine and round beads increased after adding electrolyte NaCl and MgCl2. The forming mechanism of the fiber structure morphology was analyzed theoretically.
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2005年第12期2373-2376,共4页
Chemical Journal of Chinese Universities
基金
国家自然科学基金(批准号:50373010)资助