摘要
Inwall shot blasting is a method of improving the surface hardness and high temperature oxidation resistance of the S30432 high-pressure boiler tube.The differences on residual stress,sub-grain size,micro-hardness and structure between the S30432 inwall shot-blasting tube produced by Baosteel with six technological process parameters and the imported super 304H were studied systematically by contrast test research.It has been demonstrated that the S30432 obtains a higher residual stress,a deeper distributed layer and a better sub-grain size of the inwall field shot-blasting layer;the martensite content of the shot-blasting surface was low;and micro-hardness and structure refinement were better.After 2000 h’oxidation test under the 650℃/26MPa steam condition,steam oxidation resistance of the Baosteel steel tube shot-blasting surface was higher,the oxide layer was thinner,and was well combined with bulk material.