The amount of Cu coating by chemical plating was investigated based on quadratic regression orthogonal experimental design being adapted to the variation law of temperature, pH value and Ni2+ concentration, and the relevant regression equation was expressed as y=2.1609+0.5295×10-3T2-0.0342P2-0.0265N2+0.0023TP+0.0020TH+0.0199PN-0.0959T+0.3814P-0.2073N. The results showed that the deposition rate augmented with the increasing in temperature, pH value and Ni2+ concentration. The experimental parameters of the optimal coating were temperature 75 °C, pH value 8.5 and Ni2+ concentration 1.2 g/L. The electrochemical tests indicated that the cycle stability increased from 60.66% to 75.58%, indicating that the treated alloy exhibited better corrosion resistance.
The amount of Cu coating by chemical plating was investigated based on quadratic regression orthogonal experimental design being adapted to the variation law of temperature, pH value and Ni2+ concentration, and the relevant regression equation was expressed as y=2.1609+0.5295×10-3T2-0.0342P2-0.0265N2+0.0023TP+0.0020TH+0.0199PN-0.0959T+0.3814P-0.2073N. The results showed that the deposition rate augmented with the increasing in temperature, pH value and Ni2+ concentration. The experimental parameters of the optimal coating were temperature 75 °C, pH value 8.5 and Ni2+ concentration 1.2 g/L. The electrochemical tests indicated that the cycle stability increased from 60.66% to 75.58%, indicating that the treated alloy exhibited better corrosion resistance.
基金
Project supported by the National Natural Science Foundation of China (50974042)
Scientific Research Special Foundation of Doctor Subject of Chinese Universities (20090042120015)
the Fundamental Research Funds for the Central Universities (N090302007)