When raw materials were preheated to 1000-1300 ℃ by electricity and microwave was inputted for 1 min 5 s-4 mins, then alunminate clinkers were obtained. The f-CaO contents,XRD patterns and lithofacies analysis show that the microwave processing accelerates the clinkering reaction,and Fe_2O_3 is contributed to the aluminate cement clinkering. The appearance of liquid phase in process of microwave heating increases the microwave absorbability of materials greatly.
When raw materials were preheated to 1000-1300 ℃ by electricity and microwave was inputted for 1 min 5 s-4 mins, then alunminate clinkers were obtained. The f-CaO contents,XRD patterns and lithofacies analysis show that the microwave processing accelerates the clinkering reaction,and Fe_2O_3 is contributed to the aluminate cement clinkering. The appearance of liquid phase in process of microwave heating increases the microwave absorbability of materials greatly.