以氯化锌和草酸铵为原料,通过沉淀反应制得前驱物二水合草酸锌,再经过热分解,得到20～80nm类球形和立方形的纳米氧化锌·分析了沉淀反应温度、时间、Zn2+初始浓度,以及热分解反应温度、时间对纳米氧化锌粒度和形貌的影响规律·结果表明:增加沉淀反应时间、热分解反应温度和时间,产品粒度均有不同程度的增大,而沉淀反应温度提高,产品粒度先减小后增大·Zn2+初始浓度在0 5mol/L以下时,对粒度影响不大(25nm左右),当达到0 7mol/L时,平均粒径提高到80nm左右·
Sphere-like and cubic ZnO nanoparticles were synthesized using ZnCl_2 and oxammite as raw materials by way of the precipitation reaction through which the precursor ZnC_2O_4·2H_2O was obtained and then pyrolyzed. TEM and XRD results showed that they are of crystalline zincite with grain size 25～80nm. The TG-DTA test was carried out for the precursor. It was revealed that increasing the reaction time and pyrolysis time/temperature will increase the size of primary particles. On the other hand, increasing reaction temperature (below 90℃) will take opposite effect. When the original concentration of Zn^(2+) is below 0.5mol/L the size of the particles change little (25nm), but when it reaches 0.7mol/L the size ascends to 80nm.
出处
《东北大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2005年第6期585-587,共3页
Journal of Northeastern University(Natural Science)
基金
国家自然科学基金资助项目(50374021)
关键词
纳米氧化锌
前驱物
草酸锌
沉淀
热分解
ZnO nanoparticle
precursor
zinc oxalate
precipitation
pyrolysis