摘要
研究制备具有高饱和磁化强度和低剩磁的Fe -Co -Ni系软磁合金 ,实验结果表明 ,当成分设计使合金同时含有bcc相和fcc相 ,其中bcc相占 90 %左右时 ,合金饱和磁感应强度Bs>1.8T ,同时表现较低的饱和磁致伸缩系数 ,通过横向磁场热处理其剩磁值降低到 0 .2 5T左右。
ThesoftmagneticalloywithhighsaturationmagnetizationandlowremanenceinFe -Co -Nialloysystemisinvestigated .Theex perimentalresultsshowthatwhenthealloycompositionsitesinthezoneofbccandfccdualphase ,andbccphaseisdominatedandcoveredabout 90 percent ,thealloyexhibitsgoodperformance :thesaturationmagnetizationofalloycanreachabove 1.8T ,saturationmagnetostric tionisaroundzeroandinitialpermeabilitykeepsahighlever .Afterthealloyisheat-treatedundertransversemagneticfield ,theremanencecanbedownto 0 .2 5T .