摘要
利用红外光谱对不同比例条件下制备的PP PE共混物进行了研究 ,通过对PP ,PE的特征吸收峰的分析 ,发现聚丙烯 (PP)特征峰峰面积与聚乙烯 (PE)特征峰峰面积的比值与PP/PE共混物的质量比之间存在较好的对应关系。利用特征吸收峰面积之比 ,借助红外成像技术对PP纤维热压在PE薄膜上制备的样品的研究得到了复合共混物的分布信息 ,发现其成像结果与偏光显微镜的结果有很好的吻合。实验研究结果表明采用红外成像技术 ,利用特征吸收峰面积之比可以进行对聚合物共混物的分相行为的研究。
The polypropylene/polyethylene(PP/PE) blends with different weight ratio were studied by FTIR spectroscopy. The characteristic absorption bands of PP and PE in different blends were compared. It was found that the ratio of the characteristic absorption peak areas of PP to those of PE is correlated with the weight ratio of PP to PE in the blends. Based on the above results, FTIR mapping technique was applied to characterize the samples prepared by embedding PP fiber into molten PE film, and the distribution of PP and PE in the blends can be obtained from the ratio of the characteristic peak areas of PP to PE. Good agreements have been observed between the IR mapping image and the image obtained using polarized optical microscope. These results indicated that FTIR mapping technique is an effective tool to investigate the phase separation behavior of polymer blends based on the ratio of the characteristic peak areas of different polymers.
出处
《光谱学与光谱分析》
SCIE
EI
CAS
CSCD
北大核心
2004年第7期803-805,共3页
Spectroscopy and Spectral Analysis
基金
国家自然科学基金 (599530 0 1 )
中国科学院知识创新工程重大项目 (KJCXI Y 0 3)
高分子物理与化学国家重点实验室基金资助项目