利用辉光等离子表面冶金技术在Nb521合金表面制备了Mo合金层,研究了渗Mo过程中的扩散行为:主要分析了渗金属温度,保温时间对渗层厚度和扩散速率的影响。采用扫描电子显微镜(SEM)观察渗层表面、截面形貌,X射线能谱仪(EDS)检测渗层界面元素分布。实验结果表明,渗层由扩散层和沉积层组成,且组织致密,颗粒细小,无明显显微裂纹等缺陷,与基体结合良好。温度是影响扩散速率的最主要因素,随着温度的升高,扩散速率逐渐增加,而保温时间对扩散速率的影响不大。最佳工艺下,渗层厚度可达26.5μm,扩散层厚度可达6.89μm,扩散速率可达1.73μm.h-1,Mo元素含量从表面到心部呈梯度分步,在涂层与基体的界面处,钼铌原子发生了不同程度的互扩散。最后依据传统扩散理论计算得到了Mo在不同实验温度下的扩散系数,并拟合得到了离子轰击作用下Mo在Nb521合金中的扩散激活能为292 k.Jmol-1。
A molybdenizing layer on the surface of Nb521 was prepared by glow plasma surface metallurgy technique.Diffusion behavior in the process of molybdenizing was studied and the effect of processing temperature and processing time on the layer thickness and diffusion rate were mainly analyzed.The microstructure and element distribution of the coating were investigated by scanning electric microscopy(SEM) and energy dispersive X-ray spectroscopy(EDS).The experimental results showed that the coating was consisted...
出处
《稀有金属》
EI
CAS
CSCD
北大核心
2010年第6期839-843,共5页
Chinese Journal of Rare Metals
关键词
Nb521
辉光等离子
渗Mo
扩散系数
扩散激活能
Nb521
glow plasma
molybdenizing
diffusion coefficient
diffusion activation energy