The mechanism of penetration depth increased by activating flux in activating tungsten inert gas(A-TIG)weldingwas studied by measuring the distribution of trace element Bi in the weld and monitoring the change of arc voltageduring A-TIG welding of stainless steel 0Crl8Ni9 with fluxes SiO_(2)and TiO_(2).The results show that the mechanismof penetration depth in A-TIG welding depends on the sort of flux used.The weld pool convection after coating theflux SiO_(2)and flux TiO_(2)is changed inversely compared with convectional TIG welding without flux.The arc voltageis increased by flux SiO_(2)whilst flux TiO_(2)does not have effect on the arc voltage.The reason of penetration depthincrease for SiO_(2)is due to the constriction of arc plasma and the change of surface tension gradient.The increaseof weld penetration depth with TiO_(2)only ascribes to the change of surface tension gradient.
基金
This work was supported by the National High Technology Research and Developrment Program of China under grant Nc.200AA331160
the Scientifc Research Foundation of Harbin Institute of Technology under grant No.H.IT.2001.20.