Effects of hot plastic deformation on microstructures and tensile propertiesof AZ91 alloy were investigated. Compared with as-T4 microstructures, the as-extruded samples ofAZ91 alloy with fine grains exhibit better st...Effects of hot plastic deformation on microstructures and tensile propertiesof AZ91 alloy were investigated. Compared with as-T4 microstructures, the as-extruded samples ofAZ91 alloy with fine grains exhibit better strength and ductility due to dynamic recrystallization.The succeeded rotation forging also provides finer grains while the strength increases, but theelongation decreases. Simultaneously, wrought AZ91 alloy shows more balance properties than as-T4condition ones. An interesting elongation of 228.5% is attained in the as-extruded AZ91 alloy inspite of the coarse grains with the size of 85 μm. The two-step method enhances the superplasticproperty of AZ91 alloy. The microstructure is still keeping the same scale of grains aftersuperplastic testing.展开更多
基金This project is financially supported by China Postdoctoral Science Foundation (No. 2003033090)
文摘Effects of hot plastic deformation on microstructures and tensile propertiesof AZ91 alloy were investigated. Compared with as-T4 microstructures, the as-extruded samples ofAZ91 alloy with fine grains exhibit better strength and ductility due to dynamic recrystallization.The succeeded rotation forging also provides finer grains while the strength increases, but theelongation decreases. Simultaneously, wrought AZ91 alloy shows more balance properties than as-T4condition ones. An interesting elongation of 228.5% is attained in the as-extruded AZ91 alloy inspite of the coarse grains with the size of 85 μm. The two-step method enhances the superplasticproperty of AZ91 alloy. The microstructure is still keeping the same scale of grains aftersuperplastic testing.