ZnO single crystals were grown by the innovated hydrothermal method. The crystal surfaces were polished, and then studied by atom force microscope （AFM） and wet-chemical etching （WCE）. It was found that the Zn pol...ZnO single crystals were grown by the innovated hydrothermal method. The crystal surfaces were polished, and then studied by atom force microscope （AFM） and wet-chemical etching （WCE）. It was found that the Zn polar plane was smoother than O polar plane under the same polishing conditions. The etch pit density of Zn polar plane is 4.3×10^3 cm^-2, which is consistent with the previous report, while the density of etch pit of O polar plane is more than 103cm^-2. After annealing treatment, the density of etch pit of Zn plane reduces to 5.8×102 cm^2 and is superior to the current report. This investigation reveals that the high quality ZnO single crystals with fine Zn polar plane can be obtained by the innovated hydrothermal method.展开更多
Circularly polarized luminescence(CPL)and two-photon absorption(TPA)materials have garnered considerable attentions due to their minimal energy loss and superior optical penetration[1,2].However,the current challenge ...Circularly polarized luminescence(CPL)and two-photon absorption(TPA)materials have garnered considerable attentions due to their minimal energy loss and superior optical penetration[1,2].However,the current challenge lies in the absence of well-developed strategies for designing materials that combine these two exceptional optical properties.展开更多
基金Supported by the Knowledge Innovation Program of the Chinese Academy of SciencesSpecial Project on Science and Technology of Fujian Province (2005HZ1023)+4 种基金Knowledge Innovation Project of the Chinese Academy of Sciences (KJCX2.YW.W01)Outstanding Youth Fund (50625205)Youth Talent of Fujian Province (2006F3140)Fujian Engineering Research Center for Optoelectronic Materials (2007K02, 2005DC105003)the National Key Project of China for Basic Research (2007CB936703)
文摘ZnO single crystals were grown by the innovated hydrothermal method. The crystal surfaces were polished, and then studied by atom force microscope （AFM） and wet-chemical etching （WCE）. It was found that the Zn polar plane was smoother than O polar plane under the same polishing conditions. The etch pit density of Zn polar plane is 4.3×10^3 cm^-2, which is consistent with the previous report, while the density of etch pit of O polar plane is more than 103cm^-2. After annealing treatment, the density of etch pit of Zn plane reduces to 5.8×102 cm^2 and is superior to the current report. This investigation reveals that the high quality ZnO single crystals with fine Zn polar plane can be obtained by the innovated hydrothermal method.
基金supported by NSFC(22271282)the Self-deployment Project Research Program of Haixi Institutes,Chinese Academy of Sciences with the grant number of CXZX-2022-JQ04.
文摘Circularly polarized luminescence(CPL)and two-photon absorption(TPA)materials have garnered considerable attentions due to their minimal energy loss and superior optical penetration[1,2].However,the current challenge lies in the absence of well-developed strategies for designing materials that combine these two exceptional optical properties.