The Ni-base single crystal superalloy was bonded by the transient liquid phase (TLP) bonding, using a Ni-base flexible metal cloth as an insert alloy. TLP bonding of superalloy was carried out at 1473-1523 K for 0.5-2...The Ni-base single crystal superalloy was bonded by the transient liquid phase (TLP) bonding, using a Ni-base flexible metal cloth as an insert alloy. TLP bonding of superalloy was carried out at 1473-1523 K for 0.5-24 h in vacuum. The [001] orientation of each test specimen was aligned perpendicular to the joint interface. The bonded region was observed by optical microscopy, and the microstructural and compositional analyses across the bonded interlayer were performed by using a scanning electron microscopy (SEM). The electron back scattering diffraction (EBSD) method was applied to determine the crystallographic orientation. The results indicated that the chemical homogeneity across the bonded region can be achieved, and γ' phase both in the bonded interlayer and in the superalloy substrate is almost identical, while the bonded interlayer had almost matched the crystallographic orientation of the bonded substrates.展开更多
The pure intermetallic compounds (Tb1-x;Dyx)Fe2 are super-magnetostriction materials, which were produced from DyFe2 and TbFe2 in this paper. The thermodynamic possibility and kinetic feasible conditions for DyFe2 and...The pure intermetallic compounds (Tb1-x;Dyx)Fe2 are super-magnetostriction materials, which were produced from DyFe2 and TbFe2 in this paper. The thermodynamic possibility and kinetic feasible conditions for DyFe2 and TbFe2 preparation by reduction-diffusion in Ca-Dy2O3-Fe and Ca-Tb4O7-Fe systems were analyzed and the products of DyFe2 and TbFe2 were confirmed by XRD. The contracting core model was applied to describe the reduction-diffusion process in which the diffusion is a rate-controlled step. The apparent activation energies of DyFe2 and TbFe2 processes are 45 and 39 kJ/mol respectively.展开更多
Based on hot rolling production line of strip steel, the off-line in-house software, termed as ROLLAN (Rolling Analysis), is developed. The code is mainly used to predict the evolution of temperature, rolling force, f...Based on hot rolling production line of strip steel, the off-line in-house software, termed as ROLLAN (Rolling Analysis), is developed. The code is mainly used to predict the evolution of temperature, rolling force, fraction and grain size of recrystallization, fraction and grain size of phase transformation and final mechanical properties. Almost all the processing parameters affecting microstructure and mechanical properties in the schedule from reheating to the coiling process are considered in detail. Self-learning coefficient is adopted to adjust the deviation between predicted and measured temperatures, such as roughing exit temperature (RT2), finishing exit temperature (FT7) and coiling temperature (CT). Due to the application of low-speed-threading, increasing-speed-rolling and decreasing-speed-delivery process during finishing rolling and different cooling condition, after coiling the thermal-mechanical history of different position, along strip longitudinal direction is different resulting in inhomogeneous mechanical properties. So the segments are divided along longitudinal direction to identify the variation of microstructure and mechanical properties. An example of plain carbon strip steel Q235 with various thickness is used to compare the calculated mechanical properties with measured ones. For the specific grade of Q235 , the maximum deviation of tensile strength is less than 10.3 MPa, the yield strength is less than 13.2 MPa, and elongation is less than 1.99%. Further work will focus on the on-line application and consider the effect of macrosegregation and sulfur content of cast slab.展开更多
There are inherent vulnerabilities that are not easily preventable in the mobile Ad-Hoc networks.To build a highly secure wireless Ad-Hoc network,intrusion detection and response techniques need to be deployed;The int...There are inherent vulnerabilities that are not easily preventable in the mobile Ad-Hoc networks.To build a highly secure wireless Ad-Hoc network,intrusion detection and response techniques need to be deployed;The intrusion detection and cluster-based Ad-Hoc networks has been introduced,then,an architecture for better intrusion detection based on cluster using Data Mining in wireless Ad -Hoc networks has been shown.A statistical anomaly detection approach has been used.The anomaly detection and trace analysis have been done locally in each node and possibly through cooperation with clusterhead detection in the network.展开更多
A model based on Avrami equation and Scheil's additivity rule was proposed to simulate the phase transformation in plain carbon steels during continuous cooling in hot strip mill. In this model, a wide range of co...A model based on Avrami equation and Scheil's additivity rule was proposed to simulate the phase transformation in plain carbon steels during continuous cooling in hot strip mill. In this model, a wide range of composition, cooling rate, primary austenite grain size and retained strain has been taken into account. It can be used to calculate the phase fraction transformed at different temperatures during continuous cooling. The phase equilibrium and transformation starting temperature can be determined by using Thermo-Calc and DICTRA. The simulated results containing the transformation at starting and finishing temperatures, Ae1, Ae3 and the maximum volume fraction for Q235B, were obtained. The calculated phase volume fractions are in good agreement with .the experimental results.展开更多
文摘The Ni-base single crystal superalloy was bonded by the transient liquid phase (TLP) bonding, using a Ni-base flexible metal cloth as an insert alloy. TLP bonding of superalloy was carried out at 1473-1523 K for 0.5-24 h in vacuum. The [001] orientation of each test specimen was aligned perpendicular to the joint interface. The bonded region was observed by optical microscopy, and the microstructural and compositional analyses across the bonded interlayer were performed by using a scanning electron microscopy (SEM). The electron back scattering diffraction (EBSD) method was applied to determine the crystallographic orientation. The results indicated that the chemical homogeneity across the bonded region can be achieved, and γ' phase both in the bonded interlayer and in the superalloy substrate is almost identical, while the bonded interlayer had almost matched the crystallographic orientation of the bonded substrates.
文摘The pure intermetallic compounds (Tb1-x;Dyx)Fe2 are super-magnetostriction materials, which were produced from DyFe2 and TbFe2 in this paper. The thermodynamic possibility and kinetic feasible conditions for DyFe2 and TbFe2 preparation by reduction-diffusion in Ca-Dy2O3-Fe and Ca-Tb4O7-Fe systems were analyzed and the products of DyFe2 and TbFe2 were confirmed by XRD. The contracting core model was applied to describe the reduction-diffusion process in which the diffusion is a rate-controlled step. The apparent activation energies of DyFe2 and TbFe2 processes are 45 and 39 kJ/mol respectively.
基金The project was supported by the National 863 Fund(No.2001AA339030).The authors wish to sincerely acknowledge all assistance from colleagues and the institute.
文摘Based on hot rolling production line of strip steel, the off-line in-house software, termed as ROLLAN (Rolling Analysis), is developed. The code is mainly used to predict the evolution of temperature, rolling force, fraction and grain size of recrystallization, fraction and grain size of phase transformation and final mechanical properties. Almost all the processing parameters affecting microstructure and mechanical properties in the schedule from reheating to the coiling process are considered in detail. Self-learning coefficient is adopted to adjust the deviation between predicted and measured temperatures, such as roughing exit temperature (RT2), finishing exit temperature (FT7) and coiling temperature (CT). Due to the application of low-speed-threading, increasing-speed-rolling and decreasing-speed-delivery process during finishing rolling and different cooling condition, after coiling the thermal-mechanical history of different position, along strip longitudinal direction is different resulting in inhomogeneous mechanical properties. So the segments are divided along longitudinal direction to identify the variation of microstructure and mechanical properties. An example of plain carbon strip steel Q235 with various thickness is used to compare the calculated mechanical properties with measured ones. For the specific grade of Q235 , the maximum deviation of tensile strength is less than 10.3 MPa, the yield strength is less than 13.2 MPa, and elongation is less than 1.99%. Further work will focus on the on-line application and consider the effect of macrosegregation and sulfur content of cast slab.
文摘There are inherent vulnerabilities that are not easily preventable in the mobile Ad-Hoc networks.To build a highly secure wireless Ad-Hoc network,intrusion detection and response techniques need to be deployed;The intrusion detection and cluster-based Ad-Hoc networks has been introduced,then,an architecture for better intrusion detection based on cluster using Data Mining in wireless Ad -Hoc networks has been shown.A statistical anomaly detection approach has been used.The anomaly detection and trace analysis have been done locally in each node and possibly through cooperation with clusterhead detection in the network.
基金This work was financially supported by the National Key Foundational Research Project(grant No.G1998061512).
文摘A model based on Avrami equation and Scheil's additivity rule was proposed to simulate the phase transformation in plain carbon steels during continuous cooling in hot strip mill. In this model, a wide range of composition, cooling rate, primary austenite grain size and retained strain has been taken into account. It can be used to calculate the phase fraction transformed at different temperatures during continuous cooling. The phase equilibrium and transformation starting temperature can be determined by using Thermo-Calc and DICTRA. The simulated results containing the transformation at starting and finishing temperatures, Ae1, Ae3 and the maximum volume fraction for Q235B, were obtained. The calculated phase volume fractions are in good agreement with .the experimental results.