The Disc Acceleration e Xperiment(DAX)is one of the most recent experimental methods of performance characterization of new energetic materials.A cylindrical explosive charge accelerates a thin metallic disc and its v...The Disc Acceleration e Xperiment(DAX)is one of the most recent experimental methods of performance characterization of new energetic materials.A cylindrical explosive charge accelerates a thin metallic disc and its velocity is measured continuously using photonic Doppler velocimetry.The detonation velocity is measured simultaneously.The DAX test can be used to obtain the Chapman-Jouguet(CJ)detonation pressure and to describe detonation products expansion using reduced amount of explosive.A series of DAX tests was performed at various charge diameters and disc thicknesses with Semtex 1 A plastic bonded explosive and sensitized nitromethane.The DAX-like evaluation was also applied to previously measured data of Semtex 1A and A-IX-1 explosives.The optimum disc thickness is determined by the disc to explosive mass ratio of 0.01-0.08.The repeatability of the Semtex 1 A detonation pressure results is about four times lower compared to the pressed and liquid explosives.展开更多
Preparation of cast double-propellant grains depends on the ability of nitrocellulose powder to swell and coalesce into a coherent mass when treated with a suitable solvent.The cast double-base process has been develo...Preparation of cast double-propellant grains depends on the ability of nitrocellulose powder to swell and coalesce into a coherent mass when treated with a suitable solvent.The cast double-base process has been developed into a highly versatile technique for manufacturing solid rocket charges.Propellants manufactured by this process provide a wide range of energies and burning rates.Successful preparation of cast double-base propellant grains has been performed using compatible casting liquid with the casting powder.BuNENA was used as an energetic plasticizer for manufacturing of casting powder.Burning rate measurements have been performed using closed bomb SV-2to investigate the burning behavior along a wide range of operating pressure.Plateau burning had been detected in pressure range(50-70)×105 Pa for the composition included BuNENA.DTA and TGA thermal analysis were conducted to evaluate the thermal behavior of the prepared cast double-base propellants.Results from DTA were used to calculate the apparent activation energy.展开更多
文摘The Disc Acceleration e Xperiment(DAX)is one of the most recent experimental methods of performance characterization of new energetic materials.A cylindrical explosive charge accelerates a thin metallic disc and its velocity is measured continuously using photonic Doppler velocimetry.The detonation velocity is measured simultaneously.The DAX test can be used to obtain the Chapman-Jouguet(CJ)detonation pressure and to describe detonation products expansion using reduced amount of explosive.A series of DAX tests was performed at various charge diameters and disc thicknesses with Semtex 1 A plastic bonded explosive and sensitized nitromethane.The DAX-like evaluation was also applied to previously measured data of Semtex 1A and A-IX-1 explosives.The optimum disc thickness is determined by the disc to explosive mass ratio of 0.01-0.08.The repeatability of the Semtex 1 A detonation pressure results is about four times lower compared to the pressed and liquid explosives.
文摘Preparation of cast double-propellant grains depends on the ability of nitrocellulose powder to swell and coalesce into a coherent mass when treated with a suitable solvent.The cast double-base process has been developed into a highly versatile technique for manufacturing solid rocket charges.Propellants manufactured by this process provide a wide range of energies and burning rates.Successful preparation of cast double-base propellant grains has been performed using compatible casting liquid with the casting powder.BuNENA was used as an energetic plasticizer for manufacturing of casting powder.Burning rate measurements have been performed using closed bomb SV-2to investigate the burning behavior along a wide range of operating pressure.Plateau burning had been detected in pressure range(50-70)×105 Pa for the composition included BuNENA.DTA and TGA thermal analysis were conducted to evaluate the thermal behavior of the prepared cast double-base propellants.Results from DTA were used to calculate the apparent activation energy.
