Hydrogels have been synthesized from 10%, 20%, 30%, 40%, 50% and 60% aqueous solutions of acrylamide monomer by gamma radiation employing doses in the range of 0.2-30 kGy from a Co-60 source. The effect of solution co...Hydrogels have been synthesized from 10%, 20%, 30%, 40%, 50% and 60% aqueous solutions of acrylamide monomer by gamma radiation employing doses in the range of 0.2-30 kGy from a Co-60 source. The effect of solution concentration, γ-ray dose, pH and time was studied in order to observe the optimizing conditions in the characterization of hydrogels. Gel fraction increases with dose for all concentrations indicating hundred-percentage conversion of gel at doses 5 kGy for homogenous solutions in the range of 20%-50% concentration. On the other hand, 10% solution provides conversion less than 86% even at 30 kGy, whereas 60% monomer makes an inhomogeneous solution which stile gives about 100% gel fraction. Swelling of hydrogels under water with respect to time varies with both the doses and concentrations due to the change of crosslinking density in the gels. The maximum volume change of hydrogels during swelling and water desorption mainly occurs within 24 h. Swelling is also enhanced with the rise of pH due to change of ionic content of the solvent. Considering the amount of gel fraction and the properties of hydrogel, the samples prepared from 20% solution at 5 kGy show better results. Moreover, the effect of bacteria on hydrogel was found to be nil, suggesting a prohibition of growth of microorganism in it.展开更多
The formation of polymer and hydrogel from aqueous solutions having 20, 30 and 40% concentrations ofacrylamide monomer by γ-ray irradiation processing in the dose range 0.06-30 kGy using a Co-60 source and theirchara...The formation of polymer and hydrogel from aqueous solutions having 20, 30 and 40% concentrations ofacrylamide monomer by γ-ray irradiation processing in the dose range 0.06-30 kGy using a Co-60 source and theircharacterization have been observed. Polymer conversion and gel fraction are found to depend on radiation doses. Polymerconversion increases with the increase of dose, depending on the solution concentration, where maximum conversion isachieved at 0.18, 0.16 and 0.10 kGy for 20%, 30% and 40% concentrations, respectively. On the other hand, gel fractionincreases with dose from the gel point (0.12 kGy) for all concentrations, where 100% conversion of gel occurs at doses≥5 kGy. Tensile strength, viscosity and molecular weight (M_w) of polymer samples increase with both the dose and theconcentration, showing a high value of M_w up to≈10~8. Swelling of hydrogels under water with respect to time varies due tothe variation of cross-linking density formed in the gels and the maximum swelling mainly occurs within 24 h. A remarkable change of surface morphology reveals characteristic features of monomer, polymer and hydrogel films.展开更多
文摘Hydrogels have been synthesized from 10%, 20%, 30%, 40%, 50% and 60% aqueous solutions of acrylamide monomer by gamma radiation employing doses in the range of 0.2-30 kGy from a Co-60 source. The effect of solution concentration, γ-ray dose, pH and time was studied in order to observe the optimizing conditions in the characterization of hydrogels. Gel fraction increases with dose for all concentrations indicating hundred-percentage conversion of gel at doses 5 kGy for homogenous solutions in the range of 20%-50% concentration. On the other hand, 10% solution provides conversion less than 86% even at 30 kGy, whereas 60% monomer makes an inhomogeneous solution which stile gives about 100% gel fraction. Swelling of hydrogels under water with respect to time varies with both the doses and concentrations due to the change of crosslinking density in the gels. The maximum volume change of hydrogels during swelling and water desorption mainly occurs within 24 h. Swelling is also enhanced with the rise of pH due to change of ionic content of the solvent. Considering the amount of gel fraction and the properties of hydrogel, the samples prepared from 20% solution at 5 kGy show better results. Moreover, the effect of bacteria on hydrogel was found to be nil, suggesting a prohibition of growth of microorganism in it.
文摘The formation of polymer and hydrogel from aqueous solutions having 20, 30 and 40% concentrations ofacrylamide monomer by γ-ray irradiation processing in the dose range 0.06-30 kGy using a Co-60 source and theircharacterization have been observed. Polymer conversion and gel fraction are found to depend on radiation doses. Polymerconversion increases with the increase of dose, depending on the solution concentration, where maximum conversion isachieved at 0.18, 0.16 and 0.10 kGy for 20%, 30% and 40% concentrations, respectively. On the other hand, gel fractionincreases with dose from the gel point (0.12 kGy) for all concentrations, where 100% conversion of gel occurs at doses≥5 kGy. Tensile strength, viscosity and molecular weight (M_w) of polymer samples increase with both the dose and theconcentration, showing a high value of M_w up to≈10~8. Swelling of hydrogels under water with respect to time varies due tothe variation of cross-linking density formed in the gels and the maximum swelling mainly occurs within 24 h. A remarkable change of surface morphology reveals characteristic features of monomer, polymer and hydrogel films.
