The effects of Ta on the characteristics of the Zr-base BMG (bulk metallic glass) were investigated. Zr55Al10Ni5Cu30-xTax (x=1, 2,4) bulk metallic glasses (BMGs) with 3.5 mm diameter and 70 mm length were successfully...The effects of Ta on the characteristics of the Zr-base BMG (bulk metallic glass) were investigated. Zr55Al10Ni5Cu30-xTax (x=1, 2,4) bulk metallic glasses (BMGs) with 3.5 mm diameter and 70 mm length were successfully prepared by using combined jet and copper mold casting. A small amount of Ta addition does not change the glass transition temperature, crystallization temperature, and supercooled liquid region obviously, but Ta promotes composition separation and two-stage crystallization. The stable crystalline phases include Zr2Ni, CuZr2, Al2Zr3 intermetallic compounds and Ta-rich solid solution after annealing the Zr-Al-Ni-Cu-Ta alloys at 753 K. Zr55Al10Ni5Cu30-xTax (x=1,2,4) bulk glassy alloys exhibit a better compressive strength. The stress-strain curve shows a zigzag feature, and the fracture surface shows intersecting of shear bands. It may correlate with the inhomogeneous feature of amorphous structure.展开更多
The apparent activation energies and frequency factors of thedouble reversible transformations occurring in heating CuZnAlMnNIshape memory alloy (SMA) were deduced as ΔE_x→M = 62. 597 8 KJ/mol, ΔE_M → A = 153. 92 ...The apparent activation energies and frequency factors of thedouble reversible transformations occurring in heating CuZnAlMnNIshape memory alloy (SMA) were deduced as ΔE_x→M = 62. 597 8 KJ/mol, ΔE_M → A = 153. 92 KJ/Mol, A_x→M = 5.2232 × 10~9S^-1, andA_ M → A = 2.3251 × 10~23 S^-1, respectively. The kinetic equationsof the two transformations due- Ing heating were establishedsimultaneously.展开更多
Microstructures of a CuZnAlMnNi shape memory alloy in the as-quenched andlong-term aged conditions were investigated by transmission electron microscopy. Aged for one yearin martensite phase, an equilibrium α-phase w...Microstructures of a CuZnAlMnNi shape memory alloy in the as-quenched andlong-term aged conditions were investigated by transmission electron microscopy. Aged for one yearin martensite phase, an equilibrium α-phase with fcc structure was observed in the M18R martensitematrix, accompanied by the appearance of a novel diffraction pattern. By analysis, it was suggestedthat the novel pattern results from the α-phase and the martensite matrix remaining in seven fineplates which produce intense secondary diffraction effect when the diffraction beams enter from onephase into another.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No.50171005 and 50171006) the National Hi-tech Research and Development Program of China (No.2001AA331010) the National Major Basic Research Project of China (No.G2000 67201-3) the Major Science and Technology Program of Beijing (No.H020420030320).
文摘The effects of Ta on the characteristics of the Zr-base BMG (bulk metallic glass) were investigated. Zr55Al10Ni5Cu30-xTax (x=1, 2,4) bulk metallic glasses (BMGs) with 3.5 mm diameter and 70 mm length were successfully prepared by using combined jet and copper mold casting. A small amount of Ta addition does not change the glass transition temperature, crystallization temperature, and supercooled liquid region obviously, but Ta promotes composition separation and two-stage crystallization. The stable crystalline phases include Zr2Ni, CuZr2, Al2Zr3 intermetallic compounds and Ta-rich solid solution after annealing the Zr-Al-Ni-Cu-Ta alloys at 753 K. Zr55Al10Ni5Cu30-xTax (x=1,2,4) bulk glassy alloys exhibit a better compressive strength. The stress-strain curve shows a zigzag feature, and the fracture surface shows intersecting of shear bands. It may correlate with the inhomogeneous feature of amorphous structure.
基金the Natural Science Foundation of Shandong Province, Y2001F06.]
文摘The apparent activation energies and frequency factors of thedouble reversible transformations occurring in heating CuZnAlMnNIshape memory alloy (SMA) were deduced as ΔE_x→M = 62. 597 8 KJ/mol, ΔE_M → A = 153. 92 KJ/Mol, A_x→M = 5.2232 × 10~9S^-1, andA_ M → A = 2.3251 × 10~23 S^-1, respectively. The kinetic equationsof the two transformations due- Ing heating were establishedsimultaneously.
基金This project is financially supported by the Natural Science Foundation of Shandong Province ( Y2001F06) and the Fund for Outstanding Young Researcher of Shandong Province
文摘Microstructures of a CuZnAlMnNi shape memory alloy in the as-quenched andlong-term aged conditions were investigated by transmission electron microscopy. Aged for one yearin martensite phase, an equilibrium α-phase with fcc structure was observed in the M18R martensitematrix, accompanied by the appearance of a novel diffraction pattern. By analysis, it was suggestedthat the novel pattern results from the α-phase and the martensite matrix remaining in seven fineplates which produce intense secondary diffraction effect when the diffraction beams enter from onephase into another.