The laser surface remelting (LSR) treatment was performed to Al-2.0 wt% Fe alloy with a 2 kW Yb-fiber laser (IPG YLR-2000S). The substrate and laser-treated material characterization were executed using different tech...The laser surface remelting (LSR) treatment was performed to Al-2.0 wt% Fe alloy with a 2 kW Yb-fiber laser (IPG YLR-2000S). The substrate and laser-treated material characterization were executed using different techniques. Among them, the microstructure was analyzed by optical microscope, SEM, low-angle X-ray diffraction (LAXRD) and the corrosion test was made in aerated solution of 0.1 M H2SO4 at a temperature of 25°C ± 0.5°C. As result was shown, the micrograph of LSR-treated material displaying can be a fine cellular structure and the existence of certain nano-porosities and a similar to a nano-dendritic growth was observed too. The characteristic of melted zone was constituted of metastable phases according to the result of x-rays and the behavior corrosion as a result of the LSR-treated sample, which it was shown to be more resistant to corrosion than the untreated sample. A comparative study was carried out of the cyclic polarization of the laser-treated and untreated samples, demonstrating that the reduction and oxidation reverse peaks were not observed and being the cyclic polarization behavior was of irreversible character in both samples, however, the LSR-treated sample propitious the passivity on the surface also reduced the corrosion phenomena. Wherefore, this type of laser-treated alloy can be applied in the aerospace, aeronautic and automobilist industries.展开更多
文摘The laser surface remelting (LSR) treatment was performed to Al-2.0 wt% Fe alloy with a 2 kW Yb-fiber laser (IPG YLR-2000S). The substrate and laser-treated material characterization were executed using different techniques. Among them, the microstructure was analyzed by optical microscope, SEM, low-angle X-ray diffraction (LAXRD) and the corrosion test was made in aerated solution of 0.1 M H2SO4 at a temperature of 25°C ± 0.5°C. As result was shown, the micrograph of LSR-treated material displaying can be a fine cellular structure and the existence of certain nano-porosities and a similar to a nano-dendritic growth was observed too. The characteristic of melted zone was constituted of metastable phases according to the result of x-rays and the behavior corrosion as a result of the LSR-treated sample, which it was shown to be more resistant to corrosion than the untreated sample. A comparative study was carried out of the cyclic polarization of the laser-treated and untreated samples, demonstrating that the reduction and oxidation reverse peaks were not observed and being the cyclic polarization behavior was of irreversible character in both samples, however, the LSR-treated sample propitious the passivity on the surface also reduced the corrosion phenomena. Wherefore, this type of laser-treated alloy can be applied in the aerospace, aeronautic and automobilist industries.