A series of experiments of investigating the recrystallization of single crystal DD3 superalloy were carried out. The threshold temperature for recrystallization and the effect of annealing temperature on recrystalliz...A series of experiments of investigating the recrystallization of single crystal DD3 superalloy were carried out. The threshold temperature for recrystallization and the effect of annealing temperature on recrystallization were studied. The results show that the threshold temperature for recrystallization of the shot-peened DD3 samples is between 1 000 ℃ and 1 050 ℃ under the condition of annealing for 2 h, and the recrystallization depth increases with the rise of the annealing temperature. Below 1 150 ℃, the recrystallization depth increases slowly with the temperature climbing, while above 1 150 ℃, the recrystallization depth increases quickly with the rise of the temperature. The solution of the γ＇ phase is a critical factor of the recrystallization behavior of DD3 superalloy. In addition, the kinetics and microstructural evolution of recrystallization at 1 200 ℃ were also studied. It is found that the recrystallization progresses rapidly at 1 200 ℃ through the growth of fully developed recrystallized grains, and the recrystallization process on the shot-peened surface is similar to that of wrought materials, including nucleation of recrystallization, growth of new grains into the matrix, and growth of new grains by swallowing up each other.展开更多
As-cast SRR99 specimens were shot-peened and then annealed at 1250 and 1300°C for different times to investigate the kinetics of recrystallization.It was found that the relationship between annealing time and vol...As-cast SRR99 specimens were shot-peened and then annealed at 1250 and 1300°C for different times to investigate the kinetics of recrystallization.It was found that the relationship between annealing time and volume fraction of recrystallized grains could be described by the Johnson-Mehl-Avrami equation.Based on the kinetics analysis of the recrystallization process,the apparent activation energy for recrystallization was determined.In addition,the microstructural evolution during the recrystallization process at 1300°C was studied.Inwards,recrystallization first occurs in the dendritic core regions at the shot-peened surface.With the dissolution of coarse γ＇ particles in the interdendritic regions,the recrystallized grain boundaries move through the interdendritic regions.Finally,the fully developed grains nearly have a uniform depth.The recrystallization process at the shot-peened surface is similar to that of wrought materials,which includes nucleation of recrystallization,growth of recrystallized nuclei into the matrix,and growth of recrystallized grains by swallowing up each other.展开更多
基金Item Sponsored by Open Foundation of Nondestructive Test Key Laboratory of Chinese Ministry of Education(ZD200729011)
文摘A series of experiments of investigating the recrystallization of single crystal DD3 superalloy were carried out. The threshold temperature for recrystallization and the effect of annealing temperature on recrystallization were studied. The results show that the threshold temperature for recrystallization of the shot-peened DD3 samples is between 1 000 ℃ and 1 050 ℃ under the condition of annealing for 2 h, and the recrystallization depth increases with the rise of the annealing temperature. Below 1 150 ℃, the recrystallization depth increases slowly with the temperature climbing, while above 1 150 ℃, the recrystallization depth increases quickly with the rise of the temperature. The solution of the γ＇ phase is a critical factor of the recrystallization behavior of DD3 superalloy. In addition, the kinetics and microstructural evolution of recrystallization at 1 200 ℃ were also studied. It is found that the recrystallization progresses rapidly at 1 200 ℃ through the growth of fully developed recrystallized grains, and the recrystallization process on the shot-peened surface is similar to that of wrought materials, including nucleation of recrystallization, growth of new grains into the matrix, and growth of new grains by swallowing up each other.
文摘As-cast SRR99 specimens were shot-peened and then annealed at 1250 and 1300°C for different times to investigate the kinetics of recrystallization.It was found that the relationship between annealing time and volume fraction of recrystallized grains could be described by the Johnson-Mehl-Avrami equation.Based on the kinetics analysis of the recrystallization process,the apparent activation energy for recrystallization was determined.In addition,the microstructural evolution during the recrystallization process at 1300°C was studied.Inwards,recrystallization first occurs in the dendritic core regions at the shot-peened surface.With the dissolution of coarse γ＇ particles in the interdendritic regions,the recrystallized grain boundaries move through the interdendritic regions.Finally,the fully developed grains nearly have a uniform depth.The recrystallization process at the shot-peened surface is similar to that of wrought materials,which includes nucleation of recrystallization,growth of recrystallized nuclei into the matrix,and growth of recrystallized grains by swallowing up each other.