In this study,the controlled nucleation and growth of gold nanoparticles(GNPs)were investigated using a self-repelled mist in a liquid chemical reaction environment.An electrospray-based chemical reduction method was ...In this study,the controlled nucleation and growth of gold nanoparticles(GNPs)were investigated using a self-repelled mist in a liquid chemical reaction environment.An electrospray-based chemical reduction method was conducted in the aqueous region and at room temperature to synthesize the polymeric-stabilized gold nanoparticles.The electrospray technique was used to atomize a hydrogen tetrachloraurate(III)(HAuCl4)precursor solution into electrostatically charged droplets.The atomized droplets were dispersed in an aqueous reaction bath containing L-ascorbic acid as a reducing agent and polyvinylpyrrolidone(PVP)as a stabilizer.The effect of the electrospray parameters,specifically the flow rate and electrospray droplet size,as well as the reaction conditions such as the concentration of reactants,pH,and stabilizer(PVP),were investigated.The mean diameter of the GNPs increased from around 4 to 9 nm with an increase in the electrospray flow rate,droplet size,and current passing through the electrospray jet.Spherical and monodispersed GNPs were synthesized at a relatively high flow rate of 2 mL/h and a moderate concentration of 2 mM of precursor solution.The smallest-sized GNP with a high monodispersity was obtained in the reaction bath at a high pH of 10.5 and in the presence of PVP.It is expected that continuous and mass production of the engineered GNPs and other noble metal nanoparticles could be established for scaling up nanoparticle production via the proposed electrospray-based chemical reduction method.展开更多
基金This paper was supported by the Natural Science Foundation of Jiangsu Province of China(Grant No.BK20191019)the Natural Science Research Project in Colleges and Universities in Jiangsu Province of China(Grant No.19KJB470022)+1 种基金the Scientific Research Start-up Foundation funding of High-level Introduction Talents of Nanjing Institute of Technology(Grant No.YKJ201912)the Open Fund Project of the Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education of Southeast University.
文摘In this study,the controlled nucleation and growth of gold nanoparticles(GNPs)were investigated using a self-repelled mist in a liquid chemical reaction environment.An electrospray-based chemical reduction method was conducted in the aqueous region and at room temperature to synthesize the polymeric-stabilized gold nanoparticles.The electrospray technique was used to atomize a hydrogen tetrachloraurate(III)(HAuCl4)precursor solution into electrostatically charged droplets.The atomized droplets were dispersed in an aqueous reaction bath containing L-ascorbic acid as a reducing agent and polyvinylpyrrolidone(PVP)as a stabilizer.The effect of the electrospray parameters,specifically the flow rate and electrospray droplet size,as well as the reaction conditions such as the concentration of reactants,pH,and stabilizer(PVP),were investigated.The mean diameter of the GNPs increased from around 4 to 9 nm with an increase in the electrospray flow rate,droplet size,and current passing through the electrospray jet.Spherical and monodispersed GNPs were synthesized at a relatively high flow rate of 2 mL/h and a moderate concentration of 2 mM of precursor solution.The smallest-sized GNP with a high monodispersity was obtained in the reaction bath at a high pH of 10.5 and in the presence of PVP.It is expected that continuous and mass production of the engineered GNPs and other noble metal nanoparticles could be established for scaling up nanoparticle production via the proposed electrospray-based chemical reduction method.
