Concrete containing short carbon-coated-nylon fibers (0.4-2.0 vol. pct) exhibited quasi-ductile response by developing a large damage zone prior to fracture localization. In the damage zone, the material was microcrac...Concrete containing short carbon-coated-nylon fibers (0.4-2.0 vol. pct) exhibited quasi-ductile response by developing a large damage zone prior to fracture localization. In the damage zone, the material was microcracked but continued to local strain-harden. The carbon-coated-nylon-fiber-reinforced concrete composites (NFRC) were found to be an intrinsically smart concrete that could sense elastic and inelastic deformation, as well as fracture. The fibers served to bridge the cracks and the carbon coating gave the conduction path. The signal provided came from the change in electrical resistance, which was reversible for elastic deformation and irreversible for inelastic deformation and fracture. The resistance decrease was due to the reduction of surface touch resistance between fiber and matrix and the crack closure. The resistance irreversible increase resulted from the crack opening and breakage of the carbon coating on nylon fiber.展开更多
基金This work was supported by the National High Technology Research and Development Program of China under grant No.2002AA324060by the China Postdoctoral Science Foundation under grant 2003033139.
文摘Concrete containing short carbon-coated-nylon fibers (0.4-2.0 vol. pct) exhibited quasi-ductile response by developing a large damage zone prior to fracture localization. In the damage zone, the material was microcracked but continued to local strain-harden. The carbon-coated-nylon-fiber-reinforced concrete composites (NFRC) were found to be an intrinsically smart concrete that could sense elastic and inelastic deformation, as well as fracture. The fibers served to bridge the cracks and the carbon coating gave the conduction path. The signal provided came from the change in electrical resistance, which was reversible for elastic deformation and irreversible for inelastic deformation and fracture. The resistance decrease was due to the reduction of surface touch resistance between fiber and matrix and the crack closure. The resistance irreversible increase resulted from the crack opening and breakage of the carbon coating on nylon fiber.