Casting titanium alloy TC4(ZTC4) after hot isostatic pressing(HIP) is one of the preferred materials in the field of aerospace manufacturing. In this paper, HIPZTC4 after a long-term thermal exposure was investigated....Casting titanium alloy TC4(ZTC4) after hot isostatic pressing(HIP) is one of the preferred materials in the field of aerospace manufacturing. In this paper, HIPZTC4 after a long-term thermal exposure was investigated.In order to evaluate the variation of mechanical properties with service time, the tensile properties of this alloy after exposure at 400 °C for 100, 500, and 1,000 h were investigated. Microstructure of samples was observed by the means of optical microscopy(OM), scanning electron microscopy(SEM), and transmission electron microscopy(TEM). Tensile test was carried out under different test temperatures and fracture appearance was studied. The results show that the strength increases with exposure time due to the harder a2(Ti3Al) phase precipitated in the a phase and superficial oxygen layer formed, which results in the fact that the resistance of crack propagation could be increased and cracks first initiate between surface oxidation and the matrix. Besides, the tensile temperature also has a significant effect on the mechanical properties of HIPZTC4. The yield strength and tensile strength decrease with the increase of tensile temperature, while the total elongation increases.展开更多
In this paper, the single-pass hot compression experiment of titanium clad steel plate was carried out by Gleeble-3500 thermal mechanics simulation test machine,and the effect of deformation temperature(T), strain ra...In this paper, the single-pass hot compression experiment of titanium clad steel plate was carried out by Gleeble-3500 thermal mechanics simulation test machine,and the effect of deformation temperature(T), strain rate(ε),thickness ratio(k), and friction coefficient(l) on flow pattern of the metal and stress in the deformation zone was analyzed.The results show that the metal flow behavior and the stress during compressive deformation depend strongly on the deformation temperature. At 800 and 850 °C, the bimetal can flow uniformly, while at 900 °C, the TA2 flows faster than Q235 B, and the phenomenon of TA2 wrapping Q235 B is observed. The metal flow of the bimetal material will coordinate each other through the bonding interface. It is noted that the stress increases with the increase of the ε and l and decreases when the metal flows along the contact area.展开更多
基金financially supported by the National Natural Science Foundation of China(No.50804005)
文摘Casting titanium alloy TC4(ZTC4) after hot isostatic pressing(HIP) is one of the preferred materials in the field of aerospace manufacturing. In this paper, HIPZTC4 after a long-term thermal exposure was investigated.In order to evaluate the variation of mechanical properties with service time, the tensile properties of this alloy after exposure at 400 °C for 100, 500, and 1,000 h were investigated. Microstructure of samples was observed by the means of optical microscopy(OM), scanning electron microscopy(SEM), and transmission electron microscopy(TEM). Tensile test was carried out under different test temperatures and fracture appearance was studied. The results show that the strength increases with exposure time due to the harder a2(Ti3Al) phase precipitated in the a phase and superficial oxygen layer formed, which results in the fact that the resistance of crack propagation could be increased and cracks first initiate between surface oxidation and the matrix. Besides, the tensile temperature also has a significant effect on the mechanical properties of HIPZTC4. The yield strength and tensile strength decrease with the increase of tensile temperature, while the total elongation increases.
基金financially supported by the Ministry of Science and Technology ‘‘Twelfth Five-Year’’ Plan for Science & Technology Support (No. 2011BAE22B00)
文摘In this paper, the single-pass hot compression experiment of titanium clad steel plate was carried out by Gleeble-3500 thermal mechanics simulation test machine,and the effect of deformation temperature(T), strain rate(ε),thickness ratio(k), and friction coefficient(l) on flow pattern of the metal and stress in the deformation zone was analyzed.The results show that the metal flow behavior and the stress during compressive deformation depend strongly on the deformation temperature. At 800 and 850 °C, the bimetal can flow uniformly, while at 900 °C, the TA2 flows faster than Q235 B, and the phenomenon of TA2 wrapping Q235 B is observed. The metal flow of the bimetal material will coordinate each other through the bonding interface. It is noted that the stress increases with the increase of the ε and l and decreases when the metal flows along the contact area.