The selective recovery of lead from the zinc oxide dust using an alkaline Na2EDTA solution was investigated. The effects of temperature, leaching time, Na2EDTA concentration and initial NaOH concentration on the leach...The selective recovery of lead from the zinc oxide dust using an alkaline Na2EDTA solution was investigated. The effects of temperature, leaching time, Na2EDTA concentration and initial NaOH concentration on the leaching rates of lead and zinc were studied. The following optimized leaching conditions were obtained： liquid-to-solid ratio 5：1 mL/g, stirring speed 650 r/min, Na2EDTA concentration 0.12 mol/L, initial NaOH concentration 0.5 mol/L, leaching temperature 70 ℃, leaching time 120 min. Under the optimized conditions, the average leaching rates of lead, zinc, fluoride and chloride are 89.92%, 0.94%, 62.84% and 90.02%, respectively. The filtrate was used to electrowin lead powders. The average current efficiency of electrowinning is about 93% and lead content is higher than 98% under the conditions of temperature of 60 ℃, current density of 200 A/m2, H3PO4 concentration of 1.5 g/L, and lead ion concentration of above 5 g/L. The consumption of Na2EDTA and the direct current are about respectively 0.218 kg and 0.958 kW·h for per kilogram of lead powder.展开更多
Pb?Ag?PbO2 composite anodes with different mass fractions(1%,2%,3%,4%and 5%)ofβ-PbO2 were prepared by powder-pressed(PP)method.The galvanostatic polarization curves,Tafel curves and anodic polarization curves were te...Pb?Ag?PbO2 composite anodes with different mass fractions(1%,2%,3%,4%and 5%)ofβ-PbO2 were prepared by powder-pressed(PP)method.The galvanostatic polarization curves,Tafel curves and anodic polarization curves were tested in sulfuric acid solution.The morphologies and phase compositions of the anodic layers formed after galvanostatic polarization were investigated by using scanning electron microscope(SEM)and X-ray diffractometer(XRD),respectively.The results showed thatβ-PbO2 can improve the electrocatalytic activity of anodic oxide.The anode containing 3%β-PbO2 had the lowest overpotential of oxygen evolution reaction(OER)and the best corrosion resistance.The morphologies of the anode surfaces were gradually transformed from regular crystals to amorphous ones as the content ofβ-PbO2 increased in anodes.展开更多
基金Project (50974138) supported by the National Natural Science Foundation of ChinaProject (2010ssxt158) supported by Graduate Student Innovation Foundation of Central South University,China
文摘The selective recovery of lead from the zinc oxide dust using an alkaline Na2EDTA solution was investigated. The effects of temperature, leaching time, Na2EDTA concentration and initial NaOH concentration on the leaching rates of lead and zinc were studied. The following optimized leaching conditions were obtained： liquid-to-solid ratio 5：1 mL/g, stirring speed 650 r/min, Na2EDTA concentration 0.12 mol/L, initial NaOH concentration 0.5 mol/L, leaching temperature 70 ℃, leaching time 120 min. Under the optimized conditions, the average leaching rates of lead, zinc, fluoride and chloride are 89.92%, 0.94%, 62.84% and 90.02%, respectively. The filtrate was used to electrowin lead powders. The average current efficiency of electrowinning is about 93% and lead content is higher than 98% under the conditions of temperature of 60 ℃, current density of 200 A/m2, H3PO4 concentration of 1.5 g/L, and lead ion concentration of above 5 g/L. The consumption of Na2EDTA and the direct current are about respectively 0.218 kg and 0.958 kW·h for per kilogram of lead powder.
基金Project(2017YFB0305401)supported by the National Key R&D Program of ChinaProjects(51874369,51474245,51871249)supported by the National Natural Science Foundation of China+1 种基金Project(2018JJ3659)supported by the Natural Science Foundation of Hunan Province,ChinaProject(2018RS3007)supported by Huxiang Young Talents Plan,China
文摘Pb?Ag?PbO2 composite anodes with different mass fractions(1%,2%,3%,4%and 5%)ofβ-PbO2 were prepared by powder-pressed(PP)method.The galvanostatic polarization curves,Tafel curves and anodic polarization curves were tested in sulfuric acid solution.The morphologies and phase compositions of the anodic layers formed after galvanostatic polarization were investigated by using scanning electron microscope(SEM)and X-ray diffractometer(XRD),respectively.The results showed thatβ-PbO2 can improve the electrocatalytic activity of anodic oxide.The anode containing 3%β-PbO2 had the lowest overpotential of oxygen evolution reaction(OER)and the best corrosion resistance.The morphologies of the anode surfaces were gradually transformed from regular crystals to amorphous ones as the content ofβ-PbO2 increased in anodes.