In this work, a set of GTN （Gurson-Tvergaard-Needleman） parameters of the Alloy52M dissimilar metal welded joint （DMWJ） have been calibrated, and a micromechanical analysis of in-plane constraint effects on the lo...In this work, a set of GTN （Gurson-Tvergaard-Needleman） parameters of the Alloy52M dissimilar metal welded joint （DMWJ） have been calibrated, and a micromechanical analysis of in-plane constraint effects on the local fracture behavior of two cracks, which located in the weakest regions of the DMWJ, has been investigated by the local approach based on the GTN damage model. The results show that the partition of the material and the variation of the q2 parameter make the J-resistance curves obtained by numerical simulations close to the experimental values. The numerical J-resistance curves and crack growth paths are consistent with the experiment results, which show that the GTN damage model can incorporate the in-plane constraint effect. Furthermore, after the stress, strain and damage fields at the crack tip during the crack propagation process have been calculated, and the change of the J-resistance curves, crack growth paths and fracture mechanism with in-plane constraint have been analyzed.展开更多
Based on the tests of a build-up welding at plate edge (BWPE) and amulti-layer build-up welding on plate (MBWP), the article studies on the solid-state phasetransformations which affect welding distortion process and ...Based on the tests of a build-up welding at plate edge (BWPE) and amulti-layer build-up welding on plate (MBWP), the article studies on the solid-state phasetransformations which affect welding distortion process and on the influence rule of transformationstarting temperature (TST) of welded metal to the welding residual distortion. The weldingdistortion can be decreased or controlled by the transformation volume expansion caused bysolid-state phase transformation of welded metal during the cooling. The test results of BWPE showthat when TST is at about 190 deg C, the bending distortion of welded specimen is the smallest, andits displacements at free end are decreased to 58 percent and 67 percent compared with those ofconventional welding electrodes A102 and E5015, which TST are less than room temperature and equalto 758 deg C respectively. The test results of MBWP show that when TST were at 100 approx 250 deg C.the welded specimen would appear reversible bending distortion compared with those of A102 andE5015. The maximum deflection value of reversible bending distortion in 8 mm thick plate is -2.94 mmat about 170 deg C of TST. The test results provide a valuable method to decrease or to controlwelding residual distortion.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51605292)the Natural Science Foundation of Shanghai(Grant No.15ZR1429000)the Youth Foundation of Shanghai(Grant No.ZZslg15013)
文摘In this work, a set of GTN （Gurson-Tvergaard-Needleman） parameters of the Alloy52M dissimilar metal welded joint （DMWJ） have been calibrated, and a micromechanical analysis of in-plane constraint effects on the local fracture behavior of two cracks, which located in the weakest regions of the DMWJ, has been investigated by the local approach based on the GTN damage model. The results show that the partition of the material and the variation of the q2 parameter make the J-resistance curves obtained by numerical simulations close to the experimental values. The numerical J-resistance curves and crack growth paths are consistent with the experiment results, which show that the GTN damage model can incorporate the in-plane constraint effect. Furthermore, after the stress, strain and damage fields at the crack tip during the crack propagation process have been calculated, and the change of the J-resistance curves, crack growth paths and fracture mechanism with in-plane constraint have been analyzed.
基金This project is supported by National Natural Science Foundation of China (No.50175079) China Postdoctoral Science Foundation (No.2003033348).
文摘Based on the tests of a build-up welding at plate edge (BWPE) and amulti-layer build-up welding on plate (MBWP), the article studies on the solid-state phasetransformations which affect welding distortion process and on the influence rule of transformationstarting temperature (TST) of welded metal to the welding residual distortion. The weldingdistortion can be decreased or controlled by the transformation volume expansion caused bysolid-state phase transformation of welded metal during the cooling. The test results of BWPE showthat when TST is at about 190 deg C, the bending distortion of welded specimen is the smallest, andits displacements at free end are decreased to 58 percent and 67 percent compared with those ofconventional welding electrodes A102 and E5015, which TST are less than room temperature and equalto 758 deg C respectively. The test results of MBWP show that when TST were at 100 approx 250 deg C.the welded specimen would appear reversible bending distortion compared with those of A102 andE5015. The maximum deflection value of reversible bending distortion in 8 mm thick plate is -2.94 mmat about 170 deg C of TST. The test results provide a valuable method to decrease or to controlwelding residual distortion.