For Al 6k21-T4 overlap weld joint,the shear-tensile strength by using the weaving laser was improved as compared to the case of linear laser.For the specimen of low strength,the porosity was distributed continuously a...For Al 6k21-T4 overlap weld joint,the shear-tensile strength by using the weaving laser was improved as compared to the case of linear laser.For the specimen of low strength,the porosity was distributed continuously along the intersection between the plates and fusion line.However,for the optimized welding condition,large oval-shaped porosities were located only in the advancing track of the concave part.Therefore,the continuity of cracks and porosities played a key role to determine the strength.And,the weaving width was also the important parameter to control the strength.Furthermore,the concave part had more significant hot and cold cracking in the weld and heat-affected zone（HAZ）,respectively,than the convex part.展开更多
Effects of the weld microstructure and inclusions on brittle fracture initiation are investigated in a thermally aged ferritic high-nickel weld of a reactor pressure vessel head from a decommissioned nuclear power pla...Effects of the weld microstructure and inclusions on brittle fracture initiation are investigated in a thermally aged ferritic high-nickel weld of a reactor pressure vessel head from a decommissioned nuclear power plant.As-welded and reheated regions mainly consist of acicular and polygonal ferrite,respectively.Fractographic examination of Charpy V-notch impact toughness specimens reveals large inclusions(0.5-2.5μm)at the brittle fracture primary initiation sites.High impact energies were measured for the specimens in which brittle fracture was initiated from a small inclusion or an inclusion away from the V-notch.The density,geometry,and chemical composition of the primary initiation inclusions were investigated.A brittle fracture crack initiates as a microcrack either within the multiphase oxide inclusions or from the debonded interfaces between the uncracked inclusions and weld metal matrix.Primary fracture sites can be determined in all the specimens tested in the lower part of the transition curve at and below the 41-J reference impact toughness energy but not above the mentioned value because of the changes in the fracture mechanism and resulting changes in the fracture appearance.展开更多
The oxide distribution and microstructure in longitudinal and transverse welding zones during the billet-to-billet extrusion process through porthole die were adequately investigated by means of finite element method,...The oxide distribution and microstructure in longitudinal and transverse welding zones during the billet-to-billet extrusion process through porthole die were adequately investigated by means of finite element method,scanning electron microscopy and optical microscopy.The results indicate that the oxides exist at the interface between the matrix and transverse welding zone rather than longitudinal welding seam.The longitudinal welding zone reveals a darker band including the largest grain with irregular shape due to the abnormal grain growth under the heavy shear deformation and high temperature.The transverse welding zone consists of equiaxed recrystallized grains which are a little finer than those in the longitudinal welding seam.展开更多
The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316L were investigated. Welding was accomplished by different types of welding wires AWS ...The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316L were investigated. Welding was accomplished by different types of welding wires AWS ER 347, AWS ER 316L and AWS ER 309L. To verify soundness of welded samples, nondestructive tests were performed. Metallographic samples were prepared from cross-section areas of weld- joints to investigate microstructure of different regions of weld-joints by optical microscopy and scanning electron microscopy. Corrosion resistance of weld-joints was evaluated in NaCI solution by potentiodynamic polarization and electrochemical impedance techniques. In the weld metal AWS ER 347, the brittle sigma phase was created, resulting in the decrease of weld-joint corrosion resistance. According to the results of metallurgical investigations and corrosion tests, welding wire AWS ER 309L was suitable for welding duplex stainless steel （SAF 2205） to austenitic stainless steel （AIS1316L） by gas tungsten arc welding （GTAW） process.展开更多
The dissimilar combinations of Inconel 625 and duplex stainless steel SAF 2205 obtained from manual GTA welding process employing ER2209 and ERNi CrMo-3 filler metals have been investigated. Formation of secondary pha...The dissimilar combinations of Inconel 625 and duplex stainless steel SAF 2205 obtained from manual GTA welding process employing ER2209 and ERNi CrMo-3 filler metals have been investigated. Formation of secondary phases at the HAZ of Inconel 625 and grain coarsening at the HAZ of SAF 2205 were witnessed while using these filler wires. The average hardness of ER2209 weldments was found to be greater than ERNi CrMo-3 weld. Tensile fracture was observed at the weld zones for both the fillers. Impact test trials showed brittle mode of fracture on employing ER2209 filler and mixed（ductile–brittle） mode of fracture while using ERNi CrMo-3 filler. Further optical microscopy and SEM/EDS analysis were carried out across the weldments to investigate the structure–property relationships.展开更多
The microstructure and mechanical properties（strength, fatigue and formability） of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone（FZ） was lath martens...The microstructure and mechanical properties（strength, fatigue and formability） of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone（FZ） was lath martensite（LM）, and alloying elements in the FZ were uniformly distributed. The hardness in the FZ of dissimilar weld joint was similar to the average value（375 HV） of the two similar weld joints. The microstructural evolution in heat affected zone（HAZ） of dissimilar/similar weld joints was as follows：LM（coarse-grained HAZ） →finer LM（fine-grained HAZ） →M-A constituent and ferrite（intercritically HAZ） →tempered martensite（TM） and ferrite（sub-critical HAZ）. Lower hardness in intercritically HAZ and sub-critical HAZ（softening zones） was observed compared to base metal（BM） in dissimilar/similar weld joints. The size of softening zone was 0.2-0.3 mm and reduction in hardness was ~7.6%-12.7% of BM in all the weld joints, which did not influence the tensile properties of weld joints such that fracture location was in BM. Formability of dissimilar weld joints was inferior compared to similar weld joints because of the softening zone, non-uniform microstructure and hardness on the two sides of FZ. The effect of microstructure on fatigue life was not influenced due to the presence of welding concavity.展开更多
In this study, 20 mm thick AA7075-T6 alloy plates were joined by friction stir welding. The microstructure and mechanical properties of the nugget zone along the thickness direction from the top to the bottom was inve...In this study, 20 mm thick AA7075-T6 alloy plates were joined by friction stir welding. The microstructure and mechanical properties of the nugget zone along the thickness direction from the top to the bottom was investigated. The results showed that the microstructure including the grain size, the degree of dynamic recrystallization, the misorientation angle distribution and the precipitation phase containing its size, type and content exhibited a gradient distribution along the thickness direction. The testing results of mechanical properties of the slices showed that the nugget was gradually weakened along the depth from the top to the bottom. The maximum ultimate tensile strength, yield strength and elongation of the slice in the nugget top-middle are obtained, which are 415 MPa, 255 MPa and 8.1%, respectively.展开更多
The fatigue performance and fracture mechanism of laser welded twinning induced plasticity（TWIP）steel joint were investigated experimentally based on the evolution of microstructure and micromechanical properties.Th...The fatigue performance and fracture mechanism of laser welded twinning induced plasticity（TWIP）steel joint were investigated experimentally based on the evolution of microstructure and micromechanical properties.The optical microscopy was used to analyze the evolution of microstructure.The variation of composition and phase structure of fusion zone were detected by energy dispersive X-ray and X-ray diffraction spectrometers.The micromechanical behaviors of the various zones were characterized using nanoindentation.The static tensile test and high cycle fatigue test were performed to evaluate the mechanical properties of welded joint and base metal.The microstructures,tensile properties and fatigue strength of base metal as well as welded metal were analyzed.The fatigue fracture surfaces of base metal and welded joint were observed by means of scanning electron microscopy,in order to identify fatigue crack initiation sites and propagation mechanisms.Moreover,the fatigue fracture characteristics and mechanisms for the laser welded TWIP steel joints were analyzed.展开更多
Butt joints between Mg alloy AZ31 B and pure Al 1 060 sheets were produced via metal inert gas welding process with Zn-Cd alloy foil. Crack-free Al/Mg butt joints between AZ31 B Mg alloy and pure Al 1060 sheets were o...Butt joints between Mg alloy AZ31 B and pure Al 1 060 sheets were produced via metal inert gas welding process with Zn-Cd alloy foil. Crack-free Al/Mg butt joints between AZ31 B Mg alloy and pure Al 1060 sheets were obtained. Intermetallic compound layer 1 and layer 2 had formed in fusion zone/Mg alloy and the average thickness of the layer 1 was about 50 μm. The intermetallic compound layer 1 consisted of Al12Mg17 and Mg2Si phases while layer 2 consisted of Al12Mg17, Mg2Si and Mg Zn2 phases. The crack started from the IMC layer at the bottom of the joint and propagated along the brittle IMC layer, then expanded into weld metal during the SEM in situ tensile test. The highest tensile strength of the dissimilar metal butt joints could reach 46.8 MPa and the effect ofinterfacial IMC layer on mechanical property of the joint was discussed in detail in the present study.展开更多
X80 pipeline steel was welded with submerged arc automatic welding, the microstructures, cavity sizes, fusion depths and plane scanning of chemical elements in the welded zone, fusion zone, heat affected zone and base...X80 pipeline steel was welded with submerged arc automatic welding, the microstructures, cavity sizes, fusion depths and plane scanning of chemical elements in the welded zone, fusion zone, heat affected zone and base steel were observed with OM（optical microscope） and SEM（scanning electron microscope）, respectively. The experimental results show that there is main acicular ferrite in the base steel and welded zone, the microscopic structure of fusion zone is a blocked bainite, and the heat affected zone is composed of multilateral ferrite and pearlite. M-A unit of the welded zone is the main factor to strengthen the welded zone, composed of acicular ferrites. The percentage of cavities in the welded joint is less than that in the base steel, which is beneficial to increasing its mechanical performance and corrosion resistance. The fusion depth in the fusion zone and welded zone is 101.13 μm and 115.85 μm, respectively, and the distribution of chemical elements in the welded zone is uniform, no enrichment phenomena.展开更多
The AA6005A-T6 aluminum hollow extrusions were friction stir welded at a high welding speed of 2000mm/min and various axial forces. The results show that the nugget zone （NZ） is characterized by fine equiaxed grains...The AA6005A-T6 aluminum hollow extrusions were friction stir welded at a high welding speed of 2000mm/min and various axial forces. The results show that the nugget zone （NZ） is characterized by fine equiaxed grains, in which a low density of equilibrium phase β is observed. The grains in the thermo-mechanically affected zone （TMAZ） are elongated, and the highest density of dislocations and a low density of β precipitates can be found in grains. The heat affected zone （HAZ） only experiences a low thermal cycle, and a high density of β precipitates and a low density of β precipitates remain in the coarsened grains. The microhardness evolutions in the NZ, TMAZ and HAZ are governed by the grain refinement and dislocation strengthening, the dislocation and precipitation strengthening, and the precipitation and solid solution strengthening, respectively. When increasing the axial force, the changing trend of one strengthening mechanism is contrary to the other in each zone, and the microhardness increases in different zones. As a result, the tensile strength roughly increases with raising the axial force, and all joints show good tensile properties as the high welding speed inhibits the coarsening and dissolution of strengthening precipitates significantly.展开更多
Friction stir welding（FSW） was used to weld dissimilar Al-Mg-Si/Al-Zn-Mg aluminum alloys in this work.Influences of sheet configuration on microstructure and mechanical properties of the joints were mainly discussed...Friction stir welding（FSW） was used to weld dissimilar Al-Mg-Si/Al-Zn-Mg aluminum alloys in this work.Influences of sheet configuration on microstructure and mechanical properties of the joints were mainly discussed.Results showed that rather different joint cross sections were obtained when using different sheet configurations.Coarser β＇ phases can be observed at the heat affected zone（HAZ） of the Al-Mg-Si alloy side,which was the main factor affecting the tensile properties and the fatigue properties.Tensile strengths of the dissimilar Al-Mg-Si/Al-Zn-Mg joints using both configurations were higher than that of the Al-Mg-Si FSW joint.When the Al-Zn-Mg alloy was located at the advancing side（AS）,the joints owned better fatigue properties due to the bridging effect of the big secondary phase particles.展开更多
Laser fusion brazing welding was proposed.Galvanized steel/AA6061 lapped joint was obtained by laser fusion brazing welding technique using the laser-induced aluminium molten pool spreading and wetting the solid steel...Laser fusion brazing welding was proposed.Galvanized steel/AA6061 lapped joint was obtained by laser fusion brazing welding technique using the laser-induced aluminium molten pool spreading and wetting the solid steel surface.Wide joint interface was formed using the rectangular laser beam coupled with the synchronous powder feeding.The result showed that the tiny structure with the composition of a-Al and Al–Si eutectic was formed in the weld close to the Al side.And close to the steel side,a layer of compact Fe–Al–Si intermetallics,including the Al-rich FeAl3,Fe2Al5 phases and Al–Fe–Si s1 phase,was generated with the thickness of about 10–20 lm.Transverse tensile shows the brittlefractured characteristic along to the seam/steel interface with the maximum yield strength of 152.5 MPa due to the existence of hardening phases s1 and Al–Fe intermetallics.展开更多
As a primary material of the thorium molten salt reactor（TMSR） that is a suitable candidate reactor of the Generation IV nuclear reactors, GH3535 superalloy was successfully welded. The effect of laser beam welding...As a primary material of the thorium molten salt reactor（TMSR） that is a suitable candidate reactor of the Generation IV nuclear reactors, GH3535 superalloy was successfully welded. The effect of laser beam welding（LBW） on microstructure evolution of fusion zone（FZ） and heat affected zone（HAZ）, such as element segregation, precipitate behavior and grain evolution, was investigated. The microhardness and tensile properties were tested and discussed. The results of microstructure evolution showed that a number of fine M6C-y eutectic phases precipitated at solidification grain boundaries and interdendritic region in FZ. Compared to base metal zone（BMZ）, the grain size of HAZ has no obvious change. While a few of M6C-y eutectic phases were observed in partially melted zone（PMZ） of HAZ. The results of microhardness indicated that the hardness of FZ was higher than that of HAZ and BMZ. The results of tensile test showed that the ultimate tensile strength of joints at room temperature, 650 and 700？C were98%, 97% and 99% of that of BM, respectively. All the tensile specimens of joints failed in BMZ rather than in PMZ where M6 C carbides had been transformed into M6C-y eutectic phases.展开更多
The effect of base material（BM） on microstructure and crystallographic orientation evolution of a Ti–6Al–4V electron-beam welded joint was investigated. Meanwhile, the crystallographic orientation of prior b grain...The effect of base material（BM） on microstructure and crystallographic orientation evolution of a Ti–6Al–4V electron-beam welded joint was investigated. Meanwhile, the crystallographic orientation of prior b grains was studied by advanced electron backscattered diffraction data processing. The inhomogeneity of microstructure within welded joint was formed due to the different microstructures of BM. By comparing microstructure details of the welded joint, including microstructure morphology and crystallographic orientation with those of the base material, it can be found that both the microstructure morphology and crystallographic orientation of the EBW joint would be controlled by BM.展开更多
Advanced A-TIG method was conducted to increase the weld penetration and compared with the conventional TIG welding process.A two-pipeline setup was designed to apply Ar ＋ CO_2 mixed gas as the outer layer,while pure...Advanced A-TIG method was conducted to increase the weld penetration and compared with the conventional TIG welding process.A two-pipeline setup was designed to apply Ar ＋ CO_2 mixed gas as the outer layer,while pure argon was applied as the inner layer to prevent any consumption of the tungsten electrode.The results indicate that the presence of active gas in the molten pool led to the change in the temperature coefficient of surface tension so that the Marangoni convection turns inward and forms a deep weld zone.The increase in gas flow rate causes a decrease in the weld efficiency which is attributed to the increase in oxygen content in the weld pool and the formation o f a thicker oxide layer on the weld surface.Moreover,the stir and the temperature fluctuation,led by double shielding gas,create more homogeneous nucleation sites in the molten pool so that a fine grain micros true ture was obtained.展开更多
Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone...Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone （HAZ） with that of cold worked alloy. Peak of the residual strain was observed to approach to the fusion boundary in HAZ while the strain increased from the top of the weld to the root. Strain distribution in the HAZ was found to be concentrated adjacent to grain boundaries （GBs）, with a peak of approximately three times of that in grain. Further, triple junctions of the GB appear to cause a higher strain concentration than single GBs. The microstructure of HAZ consists of partially tangled dislocations, which is different from slip bands of high density dislocations in cold worked alloy. This may cause a relatively higher intergranular cracking resistance of HAZ due to the difficulty in transferring tangled dislocations to GB in HAZ under deformation.展开更多
Microstructure and alloy element distribution in the welded joint between austenitic stainless steel (1Cr18Ni9Ti) and pearlitic heat-resistant steel (1Cr5Mo) were researched by means of light microscopy, scanning elec...Microstructure and alloy element distribution in the welded joint between austenitic stainless steel (1Cr18Ni9Ti) and pearlitic heat-resistant steel (1Cr5Mo) were researched by means of light microscopy, scanning electron microscopy (SEM) and electron probe microanalysis (EPMA). Microstructure, divisions of the fusion zone and elemental diffusion distributions in the welded joints were investigated. Furthermore, solidification microstructure and S-ferrite distribution in the weld metal of these steels are also discussed.展开更多
Friction stir welding is a new and innovative welding method used to fuse materials. In this welding method, the heat generated by friction and plastic flow causes significant changes in the microstructure of the mate...Friction stir welding is a new and innovative welding method used to fuse materials. In this welding method, the heat generated by friction and plastic flow causes significant changes in the microstructure of the material, which leads to local changes in the mechanical properties of the weld. In this study, the effects of various welding parameters such as the rotational and traverse speeds of the tool on the microstructural and mechanical properties of copper plates were investigated; additionally, Charpy tests were performed on copper plates for the first time. Also, the effect of the number of welding passes on the aforementioned properties has not been investigated in previous studies. The results indicated that better welds with superior properties are produced when less heat is transferred to the workpiece during the welding process. It was also found that although the properties of the stir zone improved with an increasing number of weld passes, the properties of its weakest zone, the heat-affected zone, deteriorated.展开更多
The effect of post weld heat treatment on the microstructure and fracture toughness of friction welded joints of Ti-6.5Al-1Mo-1V-2Zr alloy was studied. The experimental results show that equiaxial grains were formed a...The effect of post weld heat treatment on the microstructure and fracture toughness of friction welded joints of Ti-6.5Al-1Mo-1V-2Zr alloy was studied. The experimental results show that equiaxial grains were formed at the center of the weld metal while highly deformed grains were observed in the thermomechanically affected zone. The fracture toughness of the weld metal was lower than that of the thermomechanically affected zone under as-weld and post weld heat treatment conditions. With increasing temperature of post weld heat treatment, the fracture toughness of weld center and thermomechanically affected zone increased. The fractographic observation revealed that the friction welded joints fractured in a ductile mode.展开更多
基金supported by a grant from the Ministry of Knowledge Economy,Republic of Koreaby NCRC (National Core Research Center) Program through the National Research Foundation of Korea funded by the Ministry of Education,Science and Technology (2010-0001-222)
文摘For Al 6k21-T4 overlap weld joint,the shear-tensile strength by using the weaving laser was improved as compared to the case of linear laser.For the specimen of low strength,the porosity was distributed continuously along the intersection between the plates and fusion line.However,for the optimized welding condition,large oval-shaped porosities were located only in the advancing track of the concave part.Therefore,the continuity of cracks and porosities played a key role to determine the strength.And,the weaving width was also the important parameter to control the strength.Furthermore,the concave part had more significant hot and cold cracking in the weld and heat-affected zone（HAZ）,respectively,than the convex part.
基金the SAFIR2022 BRUTE project (Barseback RPV material used for true evaluation of embrittlement) for funding the study
文摘Effects of the weld microstructure and inclusions on brittle fracture initiation are investigated in a thermally aged ferritic high-nickel weld of a reactor pressure vessel head from a decommissioned nuclear power plant.As-welded and reheated regions mainly consist of acicular and polygonal ferrite,respectively.Fractographic examination of Charpy V-notch impact toughness specimens reveals large inclusions(0.5-2.5μm)at the brittle fracture primary initiation sites.High impact energies were measured for the specimens in which brittle fracture was initiated from a small inclusion or an inclusion away from the V-notch.The density,geometry,and chemical composition of the primary initiation inclusions were investigated.A brittle fracture crack initiates as a microcrack either within the multiphase oxide inclusions or from the debonded interfaces between the uncracked inclusions and weld metal matrix.Primary fracture sites can be determined in all the specimens tested in the lower part of the transition curve at and below the 41-J reference impact toughness energy but not above the mentioned value because of the changes in the fracture mechanism and resulting changes in the fracture appearance.
基金Project(2012CB619501) supported by the National Basic Research Program of ChinaProject supported by the Chinese Defence Advance Research Program of Science and Technology
文摘The oxide distribution and microstructure in longitudinal and transverse welding zones during the billet-to-billet extrusion process through porthole die were adequately investigated by means of finite element method,scanning electron microscopy and optical microscopy.The results indicate that the oxides exist at the interface between the matrix and transverse welding zone rather than longitudinal welding seam.The longitudinal welding zone reveals a darker band including the largest grain with irregular shape due to the abnormal grain growth under the heavy shear deformation and high temperature.The transverse welding zone consists of equiaxed recrystallized grains which are a little finer than those in the longitudinal welding seam.
文摘The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316L were investigated. Welding was accomplished by different types of welding wires AWS ER 347, AWS ER 316L and AWS ER 309L. To verify soundness of welded samples, nondestructive tests were performed. Metallographic samples were prepared from cross-section areas of weld- joints to investigate microstructure of different regions of weld-joints by optical microscopy and scanning electron microscopy. Corrosion resistance of weld-joints was evaluated in NaCI solution by potentiodynamic polarization and electrochemical impedance techniques. In the weld metal AWS ER 347, the brittle sigma phase was created, resulting in the decrease of weld-joint corrosion resistance. According to the results of metallurgical investigations and corrosion tests, welding wire AWS ER 309L was suitable for welding duplex stainless steel （SAF 2205） to austenitic stainless steel （AIS1316L） by gas tungsten arc welding （GTAW） process.
文摘The dissimilar combinations of Inconel 625 and duplex stainless steel SAF 2205 obtained from manual GTA welding process employing ER2209 and ERNi CrMo-3 filler metals have been investigated. Formation of secondary phases at the HAZ of Inconel 625 and grain coarsening at the HAZ of SAF 2205 were witnessed while using these filler wires. The average hardness of ER2209 weldments was found to be greater than ERNi CrMo-3 weld. Tensile fracture was observed at the weld zones for both the fillers. Impact test trials showed brittle mode of fracture on employing ER2209 filler and mixed（ductile–brittle） mode of fracture while using ERNi CrMo-3 filler. Further optical microscopy and SEM/EDS analysis were carried out across the weldments to investigate the structure–property relationships.
基金financially supported by the National Natural Science Foundation of China(Grant Nos.51274063 and 51305285)the National Program on Key Basic Research Project(Grant No.2011CB606306-2)+1 种基金the Open Research Fund from the State Key Laboratory of Rolling and Automation,Northeastern University(Grant No.2016005)the Project Funded by China Postdoctoral Science Foundation(Grant No.2016M601877)
文摘The microstructure and mechanical properties（strength, fatigue and formability） of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone（FZ） was lath martensite（LM）, and alloying elements in the FZ were uniformly distributed. The hardness in the FZ of dissimilar weld joint was similar to the average value（375 HV） of the two similar weld joints. The microstructural evolution in heat affected zone（HAZ） of dissimilar/similar weld joints was as follows：LM（coarse-grained HAZ） →finer LM（fine-grained HAZ） →M-A constituent and ferrite（intercritically HAZ） →tempered martensite（TM） and ferrite（sub-critical HAZ）. Lower hardness in intercritically HAZ and sub-critical HAZ（softening zones） was observed compared to base metal（BM） in dissimilar/similar weld joints. The size of softening zone was 0.2-0.3 mm and reduction in hardness was ~7.6%-12.7% of BM in all the weld joints, which did not influence the tensile properties of weld joints such that fracture location was in BM. Formability of dissimilar weld joints was inferior compared to similar weld joints because of the softening zone, non-uniform microstructure and hardness on the two sides of FZ. The effect of microstructure on fatigue life was not influenced due to the presence of welding concavity.
基金supported by the National Natural Science Foundation of China(NSFC)(No.51265043 and 51265042)the Special Construction Project of Advanced Science and Technology Innovation Team of Jiangxi Province(No.20171BCB24007)
文摘In this study, 20 mm thick AA7075-T6 alloy plates were joined by friction stir welding. The microstructure and mechanical properties of the nugget zone along the thickness direction from the top to the bottom was investigated. The results showed that the microstructure including the grain size, the degree of dynamic recrystallization, the misorientation angle distribution and the precipitation phase containing its size, type and content exhibited a gradient distribution along the thickness direction. The testing results of mechanical properties of the slices showed that the nugget was gradually weakened along the depth from the top to the bottom. The maximum ultimate tensile strength, yield strength and elongation of the slice in the nugget top-middle are obtained, which are 415 MPa, 255 MPa and 8.1%, respectively.
基金Item Sponsored by National Natural Science Foundation of China(51374151,21201129)Science and Technology Major Project of Shanxi Province of China(20111101053)Natural Science Foundation of Shanxi Province of China(2011011020-2)
文摘The fatigue performance and fracture mechanism of laser welded twinning induced plasticity（TWIP）steel joint were investigated experimentally based on the evolution of microstructure and micromechanical properties.The optical microscopy was used to analyze the evolution of microstructure.The variation of composition and phase structure of fusion zone were detected by energy dispersive X-ray and X-ray diffraction spectrometers.The micromechanical behaviors of the various zones were characterized using nanoindentation.The static tensile test and high cycle fatigue test were performed to evaluate the mechanical properties of welded joint and base metal.The microstructures,tensile properties and fatigue strength of base metal as well as welded metal were analyzed.The fatigue fracture surfaces of base metal and welded joint were observed by means of scanning electron microscopy,in order to identify fatigue crack initiation sites and propagation mechanisms.Moreover,the fatigue fracture characteristics and mechanisms for the laser welded TWIP steel joints were analyzed.
文摘Butt joints between Mg alloy AZ31 B and pure Al 1 060 sheets were produced via metal inert gas welding process with Zn-Cd alloy foil. Crack-free Al/Mg butt joints between AZ31 B Mg alloy and pure Al 1060 sheets were obtained. Intermetallic compound layer 1 and layer 2 had formed in fusion zone/Mg alloy and the average thickness of the layer 1 was about 50 μm. The intermetallic compound layer 1 consisted of Al12Mg17 and Mg2Si phases while layer 2 consisted of Al12Mg17, Mg2Si and Mg Zn2 phases. The crack started from the IMC layer at the bottom of the joint and propagated along the brittle IMC layer, then expanded into weld metal during the SEM in situ tensile test. The highest tensile strength of the dissimilar metal butt joints could reach 46.8 MPa and the effect ofinterfacial IMC layer on mechanical property of the joint was discussed in detail in the present study.
基金Funded by the Chief Expert (Engineer) Project of Jiangsu Provincial Association for Science(No.2013-216)the Innovation Program of Graduated Student of Jiangsu Province(CXLX2014-1098)
文摘X80 pipeline steel was welded with submerged arc automatic welding, the microstructures, cavity sizes, fusion depths and plane scanning of chemical elements in the welded zone, fusion zone, heat affected zone and base steel were observed with OM（optical microscope） and SEM（scanning electron microscope）, respectively. The experimental results show that there is main acicular ferrite in the base steel and welded zone, the microscopic structure of fusion zone is a blocked bainite, and the heat affected zone is composed of multilateral ferrite and pearlite. M-A unit of the welded zone is the main factor to strengthen the welded zone, composed of acicular ferrites. The percentage of cavities in the welded joint is less than that in the base steel, which is beneficial to increasing its mechanical performance and corrosion resistance. The fusion depth in the fusion zone and welded zone is 101.13 μm and 115.85 μm, respectively, and the distribution of chemical elements in the welded zone is uniform, no enrichment phenomena.
基金supported by the National Natural Science Foundation of China(51435004,51175117,U1404502)by the National Science and Technology Major Project of China(2010ZX04007-011)
文摘The AA6005A-T6 aluminum hollow extrusions were friction stir welded at a high welding speed of 2000mm/min and various axial forces. The results show that the nugget zone （NZ） is characterized by fine equiaxed grains, in which a low density of equilibrium phase β is observed. The grains in the thermo-mechanically affected zone （TMAZ） are elongated, and the highest density of dislocations and a low density of β precipitates can be found in grains. The heat affected zone （HAZ） only experiences a low thermal cycle, and a high density of β precipitates and a low density of β precipitates remain in the coarsened grains. The microhardness evolutions in the NZ, TMAZ and HAZ are governed by the grain refinement and dislocation strengthening, the dislocation and precipitation strengthening, and the precipitation and solid solution strengthening, respectively. When increasing the axial force, the changing trend of one strengthening mechanism is contrary to the other in each zone, and the microhardness increases in different zones. As a result, the tensile strength roughly increases with raising the axial force, and all joints show good tensile properties as the high welding speed inhibits the coarsening and dissolution of strengthening precipitates significantly.
基金supported by the International S&T Cooperation Program of China(ISTCP) under grant No.2012DFR50580
文摘Friction stir welding（FSW） was used to weld dissimilar Al-Mg-Si/Al-Zn-Mg aluminum alloys in this work.Influences of sheet configuration on microstructure and mechanical properties of the joints were mainly discussed.Results showed that rather different joint cross sections were obtained when using different sheet configurations.Coarser β＇ phases can be observed at the heat affected zone（HAZ） of the Al-Mg-Si alloy side,which was the main factor affecting the tensile properties and the fatigue properties.Tensile strengths of the dissimilar Al-Mg-Si/Al-Zn-Mg joints using both configurations were higher than that of the Al-Mg-Si FSW joint.When the Al-Zn-Mg alloy was located at the advancing side（AS）,the joints owned better fatigue properties due to the bridging effect of the big secondary phase particles.
基金financially supported by the National Natural Science Foundation of China (No.50875005)Beijing Natural Science Foundation (No.3102005)
文摘Laser fusion brazing welding was proposed.Galvanized steel/AA6061 lapped joint was obtained by laser fusion brazing welding technique using the laser-induced aluminium molten pool spreading and wetting the solid steel surface.Wide joint interface was formed using the rectangular laser beam coupled with the synchronous powder feeding.The result showed that the tiny structure with the composition of a-Al and Al–Si eutectic was formed in the weld close to the Al side.And close to the steel side,a layer of compact Fe–Al–Si intermetallics,including the Al-rich FeAl3,Fe2Al5 phases and Al–Fe–Si s1 phase,was generated with the thickness of about 10–20 lm.Transverse tensile shows the brittlefractured characteristic along to the seam/steel interface with the maximum yield strength of 152.5 MPa due to the existence of hardening phases s1 and Al–Fe intermetallics.
基金supported by National Key Research and Development Program of China (Grant No. 2016YFB0700404)the National Natural Science Foundation of China (Grant Nos. 51371188, 51671122, 51671154, 51501216, 51601213)the Strategic Priority Research Program of the Chinese Academy of Sciences (Grant No. XDA02004210)
文摘As a primary material of the thorium molten salt reactor（TMSR） that is a suitable candidate reactor of the Generation IV nuclear reactors, GH3535 superalloy was successfully welded. The effect of laser beam welding（LBW） on microstructure evolution of fusion zone（FZ） and heat affected zone（HAZ）, such as element segregation, precipitate behavior and grain evolution, was investigated. The microhardness and tensile properties were tested and discussed. The results of microstructure evolution showed that a number of fine M6C-y eutectic phases precipitated at solidification grain boundaries and interdendritic region in FZ. Compared to base metal zone（BMZ）, the grain size of HAZ has no obvious change. While a few of M6C-y eutectic phases were observed in partially melted zone（PMZ） of HAZ. The results of microhardness indicated that the hardness of FZ was higher than that of HAZ and BMZ. The results of tensile test showed that the ultimate tensile strength of joints at room temperature, 650 and 700？C were98%, 97% and 99% of that of BM, respectively. All the tensile specimens of joints failed in BMZ rather than in PMZ where M6 C carbides had been transformed into M6C-y eutectic phases.
文摘The effect of base material（BM） on microstructure and crystallographic orientation evolution of a Ti–6Al–4V electron-beam welded joint was investigated. Meanwhile, the crystallographic orientation of prior b grains was studied by advanced electron backscattered diffraction data processing. The inhomogeneity of microstructure within welded joint was formed due to the different microstructures of BM. By comparing microstructure details of the welded joint, including microstructure morphology and crystallographic orientation with those of the base material, it can be found that both the microstructure morphology and crystallographic orientation of the EBW joint would be controlled by BM.
文摘Advanced A-TIG method was conducted to increase the weld penetration and compared with the conventional TIG welding process.A two-pipeline setup was designed to apply Ar ＋ CO_2 mixed gas as the outer layer,while pure argon was applied as the inner layer to prevent any consumption of the tungsten electrode.The results indicate that the presence of active gas in the molten pool led to the change in the temperature coefficient of surface tension so that the Marangoni convection turns inward and forms a deep weld zone.The increase in gas flow rate causes a decrease in the weld efficiency which is attributed to the increase in oxygen content in the weld pool and the formation o f a thicker oxide layer on the weld surface.Moreover,the stir and the temperature fluctuation,led by double shielding gas,create more homogeneous nucleation sites in the molten pool so that a fine grain micros true ture was obtained.
基金financially supported by the Hundred-Talent Program of Chinese Academy of Sciences
文摘Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone （HAZ） with that of cold worked alloy. Peak of the residual strain was observed to approach to the fusion boundary in HAZ while the strain increased from the top of the weld to the root. Strain distribution in the HAZ was found to be concentrated adjacent to grain boundaries （GBs）, with a peak of approximately three times of that in grain. Further, triple junctions of the GB appear to cause a higher strain concentration than single GBs. The microstructure of HAZ consists of partially tangled dislocations, which is different from slip bands of high density dislocations in cold worked alloy. This may cause a relatively higher intergranular cracking resistance of HAZ due to the difficulty in transferring tangled dislocations to GB in HAZ under deformation.
基金The work was supported by the Foundation of KeyLaboratory of Liquid Structure and Heredity of Materi-als, Ministry of Educat
文摘Microstructure and alloy element distribution in the welded joint between austenitic stainless steel (1Cr18Ni9Ti) and pearlitic heat-resistant steel (1Cr5Mo) were researched by means of light microscopy, scanning electron microscopy (SEM) and electron probe microanalysis (EPMA). Microstructure, divisions of the fusion zone and elemental diffusion distributions in the welded joints were investigated. Furthermore, solidification microstructure and S-ferrite distribution in the weld metal of these steels are also discussed.
文摘Friction stir welding is a new and innovative welding method used to fuse materials. In this welding method, the heat generated by friction and plastic flow causes significant changes in the microstructure of the material, which leads to local changes in the mechanical properties of the weld. In this study, the effects of various welding parameters such as the rotational and traverse speeds of the tool on the microstructural and mechanical properties of copper plates were investigated; additionally, Charpy tests were performed on copper plates for the first time. Also, the effect of the number of welding passes on the aforementioned properties has not been investigated in previous studies. The results indicated that better welds with superior properties are produced when less heat is transferred to the workpiece during the welding process. It was also found that although the properties of the stir zone improved with an increasing number of weld passes, the properties of its weakest zone, the heat-affected zone, deteriorated.
基金Funded by the Commission of Science,Techonology and Industry for National Defense(No.AXXD1818)
文摘The effect of post weld heat treatment on the microstructure and fracture toughness of friction welded joints of Ti-6.5Al-1Mo-1V-2Zr alloy was studied. The experimental results show that equiaxial grains were formed at the center of the weld metal while highly deformed grains were observed in the thermomechanically affected zone. The fracture toughness of the weld metal was lower than that of the thermomechanically affected zone under as-weld and post weld heat treatment conditions. With increasing temperature of post weld heat treatment, the fracture toughness of weld center and thermomechanically affected zone increased. The fractographic observation revealed that the friction welded joints fractured in a ductile mode.