Calculations have been made for weld depths occurring for TIG welding activated by a flux over the surface of the weld pool. In this case, the flux introduces an electrically insulating layer over the outer regions of...Calculations have been made for weld depths occurring for TIG welding activated by a flux over the surface of the weld pool. In this case, the flux introduces an electrically insulating layer over the outer regions of the weld pool surface. There is then an increase in the current density at the surface of the centre of the weld pool with a consequent increase in the J×B forces, which drive a strong convective flow of the molten metal downwards, tending to make a deep weld. For a flux which produces an insulating layer for all but a central region of radius 2 mm, the calculated weld depth is 7 mm, and an arc spot is predicted at the centre of the weld pool surface. As yet we have not resolved the reason for significant differences that exist between our measurements of weld depth and the theoretical predictions.展开更多
The effects of fluxes with single component on weld penetration depth in TIG welding of magnesium alloy were investigated. Seven kinds of halides were selected as the activating flux in the experiments. The effects of...The effects of fluxes with single component on weld penetration depth in TIG welding of magnesium alloy were investigated. Seven kinds of halides were selected as the activating flux in the experiments. The effects of coating quantity of these fluxes on weld depth-to-width ratio were also studied. The results show that all of the selected halides can increase the weld depth under the same welding conditions compared with conventional TIG welding. The increase of penetration is different for the fluxes with different component. Among them, the flux of CdCl2 is the best, which can increase up to 334% of weld depth compared with the conventional TIG welding.展开更多
The effects of process parameters on the depth-to-width ratio （D/W） of flux-cored wire underwater wet welding with a certain type of homemade .flux-cored wire are studied. It is found that the welding .speed, wire f...The effects of process parameters on the depth-to-width ratio （D/W） of flux-cored wire underwater wet welding with a certain type of homemade .flux-cored wire are studied. It is found that the welding .speed, wire feeding speed and torch oscillating amplitude hare significant effects on the dopth-to-width ratio （D/W） of welds. The D/W ratio of welds increases significantly with the increase of welding speed without the oscillating of welding torch. It increased （from 0. 14 to 0. 26 ） with the increase of wire feeding speed while the torch oscillating. And it decreased linearly with the increase of torch oscillating amplitude. However, the influelwe of oscillating speed, wire extension and welding voltage on the D/W ratio of welds was not obvious.展开更多
Through sampling and analyzing of plasma optic signals of 400-600 nm emitted from partial-penetration laser welding processes, how the penetration depth is related to the welding parameter and the plasma optic signal ...Through sampling and analyzing of plasma optic signals of 400-600 nm emitted from partial-penetration laser welding processes, how the penetration depth is related to the welding parameter and the plasma optic signal is studied, Under the experimental conditions, the plasma optic signal has good response to variety of the weld penetration, and the signal＇s RMS value increases with the penetration in a quadratic curve mode. The inherent relation between the plasma optic signal and the penetration depth is also analyzed. It is also found that, between the two common parameters of laser power and welding speed, laser power has more influence on penetration while welding speed has more influence on weld width. The research results provide theoretic and practical bases for penetration real-time monitoring or predicting in partial-penetration laser welding,展开更多
AA5454-O aluminum alloy plates with thicknesses of 1.4 and 1.0 mm were friction-stir-lap-welded (FSLWed).The influences of the tool plunge depth and welding distance on surface appearance,macrostructure and mechanical...AA5454-O aluminum alloy plates with thicknesses of 1.4 and 1.0 mm were friction-stir-lap-welded (FSLWed).The influences of the tool plunge depth and welding distance on surface appearance,macrostructure and mechanical properties of the FSLWed plates were experimentally investigated.The tensile shear load of the FSLWed plates was compared with that of the adhesive-bonded plates.Defect-free FSLWed zones were successfully obtained in all the tool plunge depths and the welding distances.The FSLWed zones exhibited the relatively smooth surface morphologies.Under all the FSLWed conditions,the FSLWed zone exhibited higher average hardness than the base metal.In addition,the upper plate exhibited a higher average hardness than the lower plate,although there was no special tendency in spite of the change in the tool plunge depth and the welding distance.The maximum tensile shear load of the FSLWed plates was much higher than that of the adhesive-bonded aluminum alloy plate.Especially,under the FSLW condition of the plunge depth of 1.8 mm and the welding distance of 40 mm,the tensile shear load of the FSLWed plate reached a level about 41% greater than that of the adhesive-bonded aluminum alloy plate.In addition,the maximum tensile shear load of the FSLWed plate was increased with the increase of the welding distance.展开更多
Fracture parameters of welded joints with different strength matching and crack depth in weld metal are investigated by using the methods of elastoplastic finite element analysis and three point bend specimen test. Th...Fracture parameters of welded joints with different strength matching and crack depth in weld metal are investigated by using the methods of elastoplastic finite element analysis and three point bend specimen test. The results show that for shallow crack, the plastic zone turns large in loading process, and the fracture toughness turns high. The extent of the plastic zone of overmatched joint is larger than that of undermatched joint because it will extends to parent metal from the weld metal in loading process for the same CTOD value. The plastic zone of undermatched joint is restricted within the weld, and the size of that is small. Overmatched joint shows the fracture behaviour of shallow crack may more easily than the undermatched joint, while the two sorts of joint specimens have the same crack depth. Therefore, the fracture-resistant capability of overmatched weld is better than that of undermatched weld. when the toughness of weld metals is similar for both overmatched and undermatched joints.展开更多
Many applications of ultrasonic-assisted methods were used during metal solidification, but they could not be introduced into weld pool. In this paper, a way of ultrasonic assisted TIG welding is introduced. By direct...Many applications of ultrasonic-assisted methods were used during metal solidification, but they could not be introduced into weld pool. In this paper, a way of ultrasonic assisted TIG welding is introduced. By directly imposed ultrasonic vibration on welding arc, the vibration interacts with arc plasma and passes to the weld pool. Measurement results show that arc pressure is significantly increased with the ultrasonic vibration and the arc pressure distribution models are changed. Bead-on-plate welding tests on SUS304 confirm that this technology can influence the style of metal melting and increase weld penetration depth.展开更多
X80 pipeline steel was welded with submerged arc automatic welding, the microstructures, cavity sizes, fusion depths and plane scanning of chemical elements in the welded zone, fusion zone, heat affected zone and base...X80 pipeline steel was welded with submerged arc automatic welding, the microstructures, cavity sizes, fusion depths and plane scanning of chemical elements in the welded zone, fusion zone, heat affected zone and base steel were observed with OM（optical microscope） and SEM（scanning electron microscope）, respectively. The experimental results show that there is main acicular ferrite in the base steel and welded zone, the microscopic structure of fusion zone is a blocked bainite, and the heat affected zone is composed of multilateral ferrite and pearlite. M-A unit of the welded zone is the main factor to strengthen the welded zone, composed of acicular ferrites. The percentage of cavities in the welded joint is less than that in the base steel, which is beneficial to increasing its mechanical performance and corrosion resistance. The fusion depth in the fusion zone and welded zone is 101.13 μm and 115.85 μm, respectively, and the distribution of chemical elements in the welded zone is uniform, no enrichment phenomena.展开更多
This paper deals with the effect of water depth in the range of 10 m to 80 m upon the formation of pores produced during underwater wet welding. The results show that it is easy for the inner pores to occur owing to t...This paper deals with the effect of water depth in the range of 10 m to 80 m upon the formation of pores produced during underwater wet welding. The results show that it is easy for the inner pores to occur owing to the particularity of the molten metal solidification that the outer pores begin to appear when the water depth increases to about 60 m, that the porosity increases and pore grows up as the water depth increases, and that pores are all hydrogen-containing ones through the examination of the variation of number of pores with the residual hydrogen and oxygen content in the weld metal.展开更多
文摘Calculations have been made for weld depths occurring for TIG welding activated by a flux over the surface of the weld pool. In this case, the flux introduces an electrically insulating layer over the outer regions of the weld pool surface. There is then an increase in the current density at the surface of the centre of the weld pool with a consequent increase in the J×B forces, which drive a strong convective flow of the molten metal downwards, tending to make a deep weld. For a flux which produces an insulating layer for all but a central region of radius 2 mm, the calculated weld depth is 7 mm, and an arc spot is predicted at the centre of the weld pool surface. As yet we have not resolved the reason for significant differences that exist between our measurements of weld depth and the theoretical predictions.
文摘The effects of fluxes with single component on weld penetration depth in TIG welding of magnesium alloy were investigated. Seven kinds of halides were selected as the activating flux in the experiments. The effects of coating quantity of these fluxes on weld depth-to-width ratio were also studied. The results show that all of the selected halides can increase the weld depth under the same welding conditions compared with conventional TIG welding. The increase of penetration is different for the fluxes with different component. Among them, the flux of CdCl2 is the best, which can increase up to 334% of weld depth compared with the conventional TIG welding.
文摘The effects of process parameters on the depth-to-width ratio （D/W） of flux-cored wire underwater wet welding with a certain type of homemade .flux-cored wire are studied. It is found that the welding .speed, wire feeding speed and torch oscillating amplitude hare significant effects on the dopth-to-width ratio （D/W） of welds. The D/W ratio of welds increases significantly with the increase of welding speed without the oscillating of welding torch. It increased （from 0. 14 to 0. 26 ） with the increase of wire feeding speed while the torch oscillating. And it decreased linearly with the increase of torch oscillating amplitude. However, the influelwe of oscillating speed, wire extension and welding voltage on the D/W ratio of welds was not obvious.
基金This project is supported by National Defense Science Foundation of China (No.614010).
文摘Through sampling and analyzing of plasma optic signals of 400-600 nm emitted from partial-penetration laser welding processes, how the penetration depth is related to the welding parameter and the plasma optic signal is studied, Under the experimental conditions, the plasma optic signal has good response to variety of the weld penetration, and the signal＇s RMS value increases with the penetration in a quadratic curve mode. The inherent relation between the plasma optic signal and the penetration depth is also analyzed. It is also found that, between the two common parameters of laser power and welding speed, laser power has more influence on penetration while welding speed has more influence on weld width. The research results provide theoretic and practical bases for penetration real-time monitoring or predicting in partial-penetration laser welding,
基金financially supported by the Ministry of Education,Science Technology(MEST)and National Research Foundation of Korea(NRF)through the Human Resource Training Project for Regional Innovationby the development program of local science park funded by the ULSAN Metropolitan City and the MEST(Ministry of Education,Science and Technology)
文摘AA5454-O aluminum alloy plates with thicknesses of 1.4 and 1.0 mm were friction-stir-lap-welded (FSLWed).The influences of the tool plunge depth and welding distance on surface appearance,macrostructure and mechanical properties of the FSLWed plates were experimentally investigated.The tensile shear load of the FSLWed plates was compared with that of the adhesive-bonded plates.Defect-free FSLWed zones were successfully obtained in all the tool plunge depths and the welding distances.The FSLWed zones exhibited the relatively smooth surface morphologies.Under all the FSLWed conditions,the FSLWed zone exhibited higher average hardness than the base metal.In addition,the upper plate exhibited a higher average hardness than the lower plate,although there was no special tendency in spite of the change in the tool plunge depth and the welding distance.The maximum tensile shear load of the FSLWed plates was much higher than that of the adhesive-bonded aluminum alloy plate.Especially,under the FSLW condition of the plunge depth of 1.8 mm and the welding distance of 40 mm,the tensile shear load of the FSLWed plate reached a level about 41% greater than that of the adhesive-bonded aluminum alloy plate.In addition,the maximum tensile shear load of the FSLWed plate was increased with the increase of the welding distance.
文摘Fracture parameters of welded joints with different strength matching and crack depth in weld metal are investigated by using the methods of elastoplastic finite element analysis and three point bend specimen test. The results show that for shallow crack, the plastic zone turns large in loading process, and the fracture toughness turns high. The extent of the plastic zone of overmatched joint is larger than that of undermatched joint because it will extends to parent metal from the weld metal in loading process for the same CTOD value. The plastic zone of undermatched joint is restricted within the weld, and the size of that is small. Overmatched joint shows the fracture behaviour of shallow crack may more easily than the undermatched joint, while the two sorts of joint specimens have the same crack depth. Therefore, the fracture-resistant capability of overmatched weld is better than that of undermatched weld. when the toughness of weld metals is similar for both overmatched and undermatched joints.
文摘Many applications of ultrasonic-assisted methods were used during metal solidification, but they could not be introduced into weld pool. In this paper, a way of ultrasonic assisted TIG welding is introduced. By directly imposed ultrasonic vibration on welding arc, the vibration interacts with arc plasma and passes to the weld pool. Measurement results show that arc pressure is significantly increased with the ultrasonic vibration and the arc pressure distribution models are changed. Bead-on-plate welding tests on SUS304 confirm that this technology can influence the style of metal melting and increase weld penetration depth.
基金Funded by the Chief Expert (Engineer) Project of Jiangsu Provincial Association for Science(No.2013-216)the Innovation Program of Graduated Student of Jiangsu Province(CXLX2014-1098)
文摘X80 pipeline steel was welded with submerged arc automatic welding, the microstructures, cavity sizes, fusion depths and plane scanning of chemical elements in the welded zone, fusion zone, heat affected zone and base steel were observed with OM（optical microscope） and SEM（scanning electron microscope）, respectively. The experimental results show that there is main acicular ferrite in the base steel and welded zone, the microscopic structure of fusion zone is a blocked bainite, and the heat affected zone is composed of multilateral ferrite and pearlite. M-A unit of the welded zone is the main factor to strengthen the welded zone, composed of acicular ferrites. The percentage of cavities in the welded joint is less than that in the base steel, which is beneficial to increasing its mechanical performance and corrosion resistance. The fusion depth in the fusion zone and welded zone is 101.13 μm and 115.85 μm, respectively, and the distribution of chemical elements in the welded zone is uniform, no enrichment phenomena.
文摘This paper deals with the effect of water depth in the range of 10 m to 80 m upon the formation of pores produced during underwater wet welding. The results show that it is easy for the inner pores to occur owing to the particularity of the molten metal solidification that the outer pores begin to appear when the water depth increases to about 60 m, that the porosity increases and pore grows up as the water depth increases, and that pores are all hydrogen-containing ones through the examination of the variation of number of pores with the residual hydrogen and oxygen content in the weld metal.