Thickness of the intermetallic compounds(IMC)layer at the interface has a significant effect on the mechanical properties of Mg/Al dissimilar joints.However,the thickness of IMC layer can be only obtained by metallurg...Thickness of the intermetallic compounds(IMC)layer at the interface has a significant effect on the mechanical properties of Mg/Al dissimilar joints.However,the thickness of IMC layer can be only obtained by metallurgical microscopy,which is destructive and has to break down the weld.Therefore,it is crucial to find a reliable approach that can non-destructively predict the thickness of IMC layer in practical application.In the current study,Mg alloy and Al alloy were friction stir butt welded(FSW)under different tool rotation speeds(TRS)to obtain different thicknesses of IMC layers.As the TRS increased from 400 rpm to 1000 rpm,thickness of the IMC layer increased from 0.4μm to 1.3μm,the peak welding temperatures increased from 259℃to 402℃,and the Z-axis downforces decreased from10.5 kN to 3.2 k N during welding process.Higher TRS would generally induce higher welding heat input,which promotes the growth of the IMC layer and the softening of base materials.The IMC layer formed through solid-state diffusion and transformation instead of eutectic reaction according to the welding temperature history and interfacial microstructure,and its evolution process was clearly observed by plan view.In order to incorporate the effect of dramatic change of welding temperature which is the characteristic feature of FSW,Psd Voigt function was used to fit the welding temperature histories.A new prediction formula was then established to predict thicknesses of IMC layers with considering sharp welding temperature change.Predicted thicknesses gave good agreement with measured thicknesses obtained experimentally under different welding parameters,which confirmed the accuracy and reliability of the new prediction formula.Based on this prediction formula,the time period of temperature higher than 200℃during welding was found critical for the thickening of interfacial IMC layers.展开更多
The interface microstructures and strain distribution of dissimilar friction stir welding(FSW)of AA7075/AZ31B joints with or without ultrasonic vibration were examined.The results reveal that the ultrasonic vibrations...The interface microstructures and strain distribution of dissimilar friction stir welding(FSW)of AA7075/AZ31B joints with or without ultrasonic vibration were examined.The results reveal that the ultrasonic vibrations and tool offset greatly influence the dynamic recovery towards the Mg side by reducing the non-indexing region at the interface.Moreover,the grain recrystallization near the interface differed from the other areas due to severe deformation.Continuous dynamic recrystallization(CDRX)occurs at the AA7075 side,whereas the Mg side exhibits discontinuous dynamic recrystallization(DDRX).The higher net strain component was observed for ultrasonic-assisted FSW(UVaFSW).The strain component was changed significantly towards the AA7075 side compared with the AZ31B side.It occurred because of different recrystallization mechanisms.The strain component was well spread towards the AA7075 side,whereas the dispersed strain component was observed towards the AZ31B.Along the plate thickness direction,the intermetallic compound layer(IMC)thickness first increases,then decreases,reaching a maximum value of 1.5–1.8 mm from the top.The ultrasonic vibration reduced the overall thickness of intermetallic in the joint interface,regardless of the tool offset conditions.展开更多
Complete understanding of the evolution behaviors of the microstructures and intermetallic compounds(IMCs)along the interface materials flow path in friction stir welding(FSW)of dissimilar Al to Mg alloys is of great ...Complete understanding of the evolution behaviors of the microstructures and intermetallic compounds(IMCs)along the interface materials flow path in friction stir welding(FSW)of dissimilar Al to Mg alloys is of great significance.In this study,conventional FSW and ultrasonic vibration enhanced FSW(UVeFSW)experiments of Al/Mg alloys were performed,and the instantaneous evolution features of the interface materials around the tool were"frozen"by using the"sudden stop"and simultaneous cooling techniques.The microstructures and IMCs formation at different locations around the exit hole were observed and characterized by scanning electron microscope,energy dispersive spectrometer and transmission elec-tron microscope.It was found that before the materials started to deposit near the back of the tool,“IMC+Mg+IMC+Al”multilayer microstructure and simple IMC layer with(β+γ)sequentially emerged on the Al/Mg interface.With the application of ultrasonic vibration,the multi-layered interface structure only appeared at the middle stage of materials flow around the pin,and ultrasonic vibration just began to play a suppression role on the growth of two sub-layers IMC at a position where the materials deposit.With assistance of ultrasonic vibration in UVeFSW,the tool drove a larger volume of Mg alloy to move toward the retreating side,and the final IMCs thickness was thinner than that in FSW.展开更多
Material flow and phase transformation were studied at the interface of dissimilar joint between Al 6013 and Mg, produced by stir friction welding （FSW） experiments. Defect-free weld was obtained when aluminum and m...Material flow and phase transformation were studied at the interface of dissimilar joint between Al 6013 and Mg, produced by stir friction welding （FSW） experiments. Defect-free weld was obtained when aluminum and magnesium were placed in the advancing side and retreating side respectively and the tool was placed 1 mm off the weld centerline into the aluminum side. In order to understand the material flow during FSW, steel shots were implanted as indexes into the welding path. After welding, using X-ray images, secondary positions of the steel shots were evaluated. It was revealed that steel shots implanted in advancing side were penetrated from the advancing side into the retreating side, whereas the shots implanted in the retreating side remained in the retreating side, without penetrating into the advancing side. The welded specimens were also heat treated. The effects of heat treatment on the mechanical properties of the welds and the formation of new intermetallic layers were investigated. Two intermetallic compounds, Al3Mg2 and Al12Mg17, were formed sequentially at Al6013/Mg interface.展开更多
基金supported by the National Natural Science Foundation of China(No.52075330)the Interdisciplinary Program of Shanghai Jiao Tong University(No.YG2019QNA15)the Foundation of National Facility for Translational Medicine(Shanghai)(No.TMSK-2020-107)。
文摘Thickness of the intermetallic compounds(IMC)layer at the interface has a significant effect on the mechanical properties of Mg/Al dissimilar joints.However,the thickness of IMC layer can be only obtained by metallurgical microscopy,which is destructive and has to break down the weld.Therefore,it is crucial to find a reliable approach that can non-destructively predict the thickness of IMC layer in practical application.In the current study,Mg alloy and Al alloy were friction stir butt welded(FSW)under different tool rotation speeds(TRS)to obtain different thicknesses of IMC layers.As the TRS increased from 400 rpm to 1000 rpm,thickness of the IMC layer increased from 0.4μm to 1.3μm,the peak welding temperatures increased from 259℃to 402℃,and the Z-axis downforces decreased from10.5 kN to 3.2 k N during welding process.Higher TRS would generally induce higher welding heat input,which promotes the growth of the IMC layer and the softening of base materials.The IMC layer formed through solid-state diffusion and transformation instead of eutectic reaction according to the welding temperature history and interfacial microstructure,and its evolution process was clearly observed by plan view.In order to incorporate the effect of dramatic change of welding temperature which is the characteristic feature of FSW,Psd Voigt function was used to fit the welding temperature histories.A new prediction formula was then established to predict thicknesses of IMC layers with considering sharp welding temperature change.Predicted thicknesses gave good agreement with measured thicknesses obtained experimentally under different welding parameters,which confirmed the accuracy and reliability of the new prediction formula.Based on this prediction formula,the time period of temperature higher than 200℃during welding was found critical for the thickening of interfacial IMC layers.
基金supported by postdoctoral program of Shandong University,Jinan,Chinathe financial support from the National Natural Science Foundation of China(Grant Nos.52035005)the Key R&D Program of Shandong Province in China(Grant No.2021ZLGX01)。
文摘The interface microstructures and strain distribution of dissimilar friction stir welding(FSW)of AA7075/AZ31B joints with or without ultrasonic vibration were examined.The results reveal that the ultrasonic vibrations and tool offset greatly influence the dynamic recovery towards the Mg side by reducing the non-indexing region at the interface.Moreover,the grain recrystallization near the interface differed from the other areas due to severe deformation.Continuous dynamic recrystallization(CDRX)occurs at the AA7075 side,whereas the Mg side exhibits discontinuous dynamic recrystallization(DDRX).The higher net strain component was observed for ultrasonic-assisted FSW(UVaFSW).The strain component was changed significantly towards the AA7075 side compared with the AZ31B side.It occurred because of different recrystallization mechanisms.The strain component was well spread towards the AA7075 side,whereas the dispersed strain component was observed towards the AZ31B.Along the plate thickness direction,the intermetallic compound layer(IMC)thickness first increases,then decreases,reaching a maximum value of 1.5–1.8 mm from the top.The ultrasonic vibration reduced the overall thickness of intermetallic in the joint interface,regardless of the tool offset conditions.
基金This work was financially supported by the National Natural Science Foundation of China(No.52035005).
文摘Complete understanding of the evolution behaviors of the microstructures and intermetallic compounds(IMCs)along the interface materials flow path in friction stir welding(FSW)of dissimilar Al to Mg alloys is of great significance.In this study,conventional FSW and ultrasonic vibration enhanced FSW(UVeFSW)experiments of Al/Mg alloys were performed,and the instantaneous evolution features of the interface materials around the tool were"frozen"by using the"sudden stop"and simultaneous cooling techniques.The microstructures and IMCs formation at different locations around the exit hole were observed and characterized by scanning electron microscope,energy dispersive spectrometer and transmission elec-tron microscope.It was found that before the materials started to deposit near the back of the tool,“IMC+Mg+IMC+Al”multilayer microstructure and simple IMC layer with(β+γ)sequentially emerged on the Al/Mg interface.With the application of ultrasonic vibration,the multi-layered interface structure only appeared at the middle stage of materials flow around the pin,and ultrasonic vibration just began to play a suppression role on the growth of two sub-layers IMC at a position where the materials deposit.With assistance of ultrasonic vibration in UVeFSW,the tool drove a larger volume of Mg alloy to move toward the retreating side,and the final IMCs thickness was thinner than that in FSW.
文摘Material flow and phase transformation were studied at the interface of dissimilar joint between Al 6013 and Mg, produced by stir friction welding （FSW） experiments. Defect-free weld was obtained when aluminum and magnesium were placed in the advancing side and retreating side respectively and the tool was placed 1 mm off the weld centerline into the aluminum side. In order to understand the material flow during FSW, steel shots were implanted as indexes into the welding path. After welding, using X-ray images, secondary positions of the steel shots were evaluated. It was revealed that steel shots implanted in advancing side were penetrated from the advancing side into the retreating side, whereas the shots implanted in the retreating side remained in the retreating side, without penetrating into the advancing side. The welded specimens were also heat treated. The effects of heat treatment on the mechanical properties of the welds and the formation of new intermetallic layers were investigated. Two intermetallic compounds, Al3Mg2 and Al12Mg17, were formed sequentially at Al6013/Mg interface.