Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi^3＋and Ce^（4＋）containing aqueous solution.Techniques of X-ray diffraction（XRD）,transmission electron microscopic（TEM...Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi^3＋and Ce^（4＋）containing aqueous solution.Techniques of X-ray diffraction（XRD）,transmission electron microscopic（TEM）and Fourier transform infrared spectroscopy（FTIR）were employed to characterize the as-synthesized materials.The XRD patterns indicated that the peaks can be easily indexed toβ-Bi2O3 and no diffraction peaks of Ce or other impurity phases were detected in the prepared samples.The calculated average crystalline size decreased from 31.72 to 11.96 nm when the Ce content increased from 1 wt%to 10 wt%.The morphology changed from flake-like into the spherical-like with increase in Ce content.The electric conductivity of Ce-doped Bi2O3 electrolyte was also investigated by two probe DC method.Conductivity analysis exhibited that the rate of conductivity increased with increasing Ce^2＋ratio,when the Ce concentration was up to 5 wt%,the as-synthesized Ce-doped Bi2O3 electrolyte showed the maximum value of conductivity（0.295 S？cm^（–1））.展开更多
基金Funded by Changzhou Science and Technology Innovation Project(Nos.CC20140048,CC20130204)National Natural Science Foundation of China(No.51273027)2015 Research and Innovation Project for College Graduates of Jiangsu Province
文摘Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi^3＋and Ce^（4＋）containing aqueous solution.Techniques of X-ray diffraction（XRD）,transmission electron microscopic（TEM）and Fourier transform infrared spectroscopy（FTIR）were employed to characterize the as-synthesized materials.The XRD patterns indicated that the peaks can be easily indexed toβ-Bi2O3 and no diffraction peaks of Ce or other impurity phases were detected in the prepared samples.The calculated average crystalline size decreased from 31.72 to 11.96 nm when the Ce content increased from 1 wt%to 10 wt%.The morphology changed from flake-like into the spherical-like with increase in Ce content.The electric conductivity of Ce-doped Bi2O3 electrolyte was also investigated by two probe DC method.Conductivity analysis exhibited that the rate of conductivity increased with increasing Ce^2＋ratio,when the Ce concentration was up to 5 wt%,the as-synthesized Ce-doped Bi2O3 electrolyte showed the maximum value of conductivity（0.295 S？cm^（–1））.