In the present investigation, electroless Ni-Cu-P/n-TiN composite coating was prepared using alkaline citrate-based bath. X-ray diffraction （XRD）, scanning electron microscopy（SEM）, energy-dispersive spectroscopy...In the present investigation, electroless Ni-Cu-P/n-TiN composite coating was prepared using alkaline citrate-based bath. X-ray diffraction （XRD）, scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS）, electrochemical measurements, weight loss tests and Raman spectrometer were used to character the properties of the coating. As the Cu content increased from 7.3 wt% to 24.8 wt%, the corrosion current density of the Ni-Cu-P/n-TiN coating decreased from 10.80 to 4.34 ~tA. And the inclusion of Cu in NiP alloy resulted in refinement and less porosity in microstructure. The addition of TiN resulted in a slight decline in anti-corrosion property of the coating. As the mass loss test showed, Ni-24.8%Cu-P exhibited perfect corrosion resistance. Studies by Raman spectroscopy on coatings proved that Cu（II）3（PO4）（OH）3, Cu（OH）2 and CuO were examined while no compound of nickel was found, and Cu exhibited preferred corrosion in saline solution, providing cathodic protection to Ni alloy.展开更多
石油套管用钢(/%:0.26~0.29C,0.25~0.35Si,0.40~0.50Mn,≤0.009P,≤0.004S,0.95~1.05Cr,0.09~0.11V,0.02~0.04Al,0.015~0.020Ti,≤0.006 0N)的生产流程为铁水预处理-120 t BOF-吹氩-LF-喂CaSi线-RH-合金化-喂CaSi线-软吹氩-Φ220 mm圆...石油套管用钢(/%:0.26~0.29C,0.25~0.35Si,0.40~0.50Mn,≤0.009P,≤0.004S,0.95~1.05Cr,0.09~0.11V,0.02~0.04Al,0.015~0.020Ti,≤0.006 0N)的生产流程为铁水预处理-120 t BOF-吹氩-LF-喂CaSi线-RH-合金化-喂CaSi线-软吹氩-Φ220 mm圆坯连铸工艺。通过热力学分析得出钢中N含量超过50×10^(-6)以及工业试验得出生产的圆铸坯中的N含量为67×10^(-6)时,在铸坯中易形成2μm以上的TiN夹杂。通过控制BOF终点[N]≤30×10^(-6),LF终点[S]≤25×10^(-6),[O]≤25×10^(-6),[N]≤35×10^(-6),RH合金化后终点[N]≤35×10^(-6),[H]≤1.5×10^(-6),稳定喂CaSi线速度300~400 m/min,控制中间包[N]≤40×10^(-6),严格连铸保护浇铸工艺,则铸坯中的N含量≤50×10^(-6),钢中TiN夹杂数量显著下降,未发现大尺寸TiN夹杂物。展开更多
The precipitation of TiN inclusion during solidification of different carbon content of 0.72%, 0.82% and 0.95% in tire cord steel is thermodynamically studied respectively. The results show that the carbon content has...The precipitation of TiN inclusion during solidification of different carbon content of 0.72%, 0.82% and 0.95% in tire cord steel is thermodynamically studied respectively. The results show that the carbon content has obvious effect on TiN inclusion precipitated in tire cord steel of different strength levels. With the carbon content of tire cord steel increasing, the temperature before solidifying reduced gradually and the required activity product of titanium and nitrogen for TiN inclusion precipitation also declined gradually. With the same condition of initial Ti and N content in liquid steel, the size of TiN inclusion precipitated in tire cord steel of higher carbon content is bigger than that of lower carbon content. In order to control the harmful effects on processability of TiN inclusion precipitated in hypereutectoid tire cord steel of the ultra high strength level, the measures of smelting process must be taken to further reduce the titanium and nitrogen content in liquid steel.展开更多
基金Project(K1403375-11)supported by Science and Technology Planning Project of Changsha,ChinaProject(2015D009)supported by the Planned Science and Technology Project of Qingyuan City,ChinaProject(2015B04)supported by the Planned Science and Technology Project of Qingcheng District,Qingyuan City,China
文摘In the present investigation, electroless Ni-Cu-P/n-TiN composite coating was prepared using alkaline citrate-based bath. X-ray diffraction （XRD）, scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS）, electrochemical measurements, weight loss tests and Raman spectrometer were used to character the properties of the coating. As the Cu content increased from 7.3 wt% to 24.8 wt%, the corrosion current density of the Ni-Cu-P/n-TiN coating decreased from 10.80 to 4.34 ~tA. And the inclusion of Cu in NiP alloy resulted in refinement and less porosity in microstructure. The addition of TiN resulted in a slight decline in anti-corrosion property of the coating. As the mass loss test showed, Ni-24.8%Cu-P exhibited perfect corrosion resistance. Studies by Raman spectroscopy on coatings proved that Cu（II）3（PO4）（OH）3, Cu（OH）2 and CuO were examined while no compound of nickel was found, and Cu exhibited preferred corrosion in saline solution, providing cathodic protection to Ni alloy.
文摘The precipitation of TiN inclusion during solidification of different carbon content of 0.72%, 0.82% and 0.95% in tire cord steel is thermodynamically studied respectively. The results show that the carbon content has obvious effect on TiN inclusion precipitated in tire cord steel of different strength levels. With the carbon content of tire cord steel increasing, the temperature before solidifying reduced gradually and the required activity product of titanium and nitrogen for TiN inclusion precipitation also declined gradually. With the same condition of initial Ti and N content in liquid steel, the size of TiN inclusion precipitated in tire cord steel of higher carbon content is bigger than that of lower carbon content. In order to control the harmful effects on processability of TiN inclusion precipitated in hypereutectoid tire cord steel of the ultra high strength level, the measures of smelting process must be taken to further reduce the titanium and nitrogen content in liquid steel.