Vanadium carbide/titanium carbide （VC/TiC） superlattice films were synthesized by magnetron sputtering method. The effects of modulation period on the microstructure evolution and mechanical properties were investig...Vanadium carbide/titanium carbide （VC/TiC） superlattice films were synthesized by magnetron sputtering method. The effects of modulation period on the microstructure evolution and mechanical properties were investigated by EDXA, XRD, HRTEM and nano-indentation. The results reveal that the VC/TiC superlattice films form an epitaxial structure when their modulation period is less than a critical value, accompanied with a remarkable increase in hardness. Further increasing the modulation period, the hardness of superlattices decreases slowly to the rule-of-mixture value due to the destruction of epitaxial structures. The XRD results reveal that three-directional strains are generated in superlattices when the epitaxial structure is formed, which may change the modulus of constituent layers. This may explain the remarkable hardness enhancement of VC/TiC superlattices.展开更多
VAlN coating is of particular interest for dry cutting applications owing to its low-friction and excellent abrasiveness.Nano-multilayer structure is designed to tailor the properties of VAlN coating.In this work,a se...VAlN coating is of particular interest for dry cutting applications owing to its low-friction and excellent abrasiveness.Nano-multilayer structure is designed to tailor the properties of VAlN coating.In this work,a series of VAlN/Si_(3)N_(4) nano-multilayer coatings with varied Si_(3)N_(4) layer thicknesses were prepared by reactive sputtering method.The microstructure and mechanical properties of the coatings were both investigated.It is revealed that Si_(3)N_(4) with a shallow thickness(~0.4 nm)was crystallized and grown coherently with VAlN,showing a remarkable increase in hardness compared to VAlN monolayer coating.The hardness of coherently VAlN/Si_(3)N_(4) nano-multilayer coatings reached to 48.7 GPa.With further increase of Si_(3)N_(4) layer thickness,the coherent growth of nano-multilayers was terminated,showing amorphous structure formed in nano-multilayers and the hardness was declined.On the other hand,when Si_(3)N_(4) layer thickness was 0.4 nm,the friction coefficient of VAlN/Si_(3)N_(4) nano-multilayer coating was almost equal to that of VAlN monolayer coating,which was attributed to the crystallization of Si_(3)N_(4) and the produced coherent interfaces between VAlN and Si_(3)N_(4) for the hardening effect of nano-multilayer coatings.Upon further increase of Si_(3)N_(4) layer thickness,pronounced improvement of friction coefficient in VAlN/Si_(3)N_(4) nano-multilayer coating was observed.展开更多
基金Project(51201187)supported by the National Natural Science Foundation of China
文摘Vanadium carbide/titanium carbide （VC/TiC） superlattice films were synthesized by magnetron sputtering method. The effects of modulation period on the microstructure evolution and mechanical properties were investigated by EDXA, XRD, HRTEM and nano-indentation. The results reveal that the VC/TiC superlattice films form an epitaxial structure when their modulation period is less than a critical value, accompanied with a remarkable increase in hardness. Further increasing the modulation period, the hardness of superlattices decreases slowly to the rule-of-mixture value due to the destruction of epitaxial structures. The XRD results reveal that three-directional strains are generated in superlattices when the epitaxial structure is formed, which may change the modulus of constituent layers. This may explain the remarkable hardness enhancement of VC/TiC superlattices.
基金Project(51201187)supported by the National Natural Science Foundation of China。
文摘VAlN coating is of particular interest for dry cutting applications owing to its low-friction and excellent abrasiveness.Nano-multilayer structure is designed to tailor the properties of VAlN coating.In this work,a series of VAlN/Si_(3)N_(4) nano-multilayer coatings with varied Si_(3)N_(4) layer thicknesses were prepared by reactive sputtering method.The microstructure and mechanical properties of the coatings were both investigated.It is revealed that Si_(3)N_(4) with a shallow thickness(~0.4 nm)was crystallized and grown coherently with VAlN,showing a remarkable increase in hardness compared to VAlN monolayer coating.The hardness of coherently VAlN/Si_(3)N_(4) nano-multilayer coatings reached to 48.7 GPa.With further increase of Si_(3)N_(4) layer thickness,the coherent growth of nano-multilayers was terminated,showing amorphous structure formed in nano-multilayers and the hardness was declined.On the other hand,when Si_(3)N_(4) layer thickness was 0.4 nm,the friction coefficient of VAlN/Si_(3)N_(4) nano-multilayer coating was almost equal to that of VAlN monolayer coating,which was attributed to the crystallization of Si_(3)N_(4) and the produced coherent interfaces between VAlN and Si_(3)N_(4) for the hardening effect of nano-multilayer coatings.Upon further increase of Si_(3)N_(4) layer thickness,pronounced improvement of friction coefficient in VAlN/Si_(3)N_(4) nano-multilayer coating was observed.