Flotation behavior of stibiconite after sulfidation roasting with sulfur at a high temperature and the sulfidation mechanisms were investigated by ultraviolet spectrophotometry,X-ray diffraction(XRD)combining with the...Flotation behavior of stibiconite after sulfidation roasting with sulfur at a high temperature and the sulfidation mechanisms were investigated by ultraviolet spectrophotometry,X-ray diffraction(XRD)combining with thermodynamic calculation,X-ray photoelectron spectroscopy(XPS)and electron probe microanalysis(EPMA).The XRD and thermodynamic analyses revealed that the Sb_(3)O_(6)(OH)was reduced into Sb_(2)O_(4)and Sb_(2)O_(3),and was transformed into Sb_(2)S_(3)after introducing sulfur at high temperatures.Flotation test results show that flotation recovery of the stibiconite after sulfidation reaches 90.3%.Ultraviolet spectrophotometry tests confirm that adsorption capacity of sodium butyl xanthate(SBX)on surface of the roasted products has a positive relationship with S/Sb mole ratio.XPS analyses indicate that Sb-bearing species including mainly Sb_(2)S_(3),Sb_(2)O_(3)and Sb_(2)(SO_(4))_(3) are formed at the surface of particle after sulfidation.The EPMA analyses verify that the Sb_(2)S_(3)is generated at the outer layer of sample after sulfidation roasting,but the particle interior is mainly composed of antimony oxides.The sulfur atmosphere induces the outward migration of oxygen to form Sb_(2)O_(4).Then,the Sb_(2)O_(4)is transformed into Sb_(2)O_(3)in two pathways,and the Sb_(2)S_(3)is formed.These findings will provide theoretical support for recovering antimony from antimony oxide ores by xanthate flotation methods.展开更多
基金Projects(52074139,51964027)supported by the National Natural Science Foundation of ChinaProject(KKS 2202152011)supported by the High-level Talents of Yunnan Province,China。
文摘Flotation behavior of stibiconite after sulfidation roasting with sulfur at a high temperature and the sulfidation mechanisms were investigated by ultraviolet spectrophotometry,X-ray diffraction(XRD)combining with thermodynamic calculation,X-ray photoelectron spectroscopy(XPS)and electron probe microanalysis(EPMA).The XRD and thermodynamic analyses revealed that the Sb_(3)O_(6)(OH)was reduced into Sb_(2)O_(4)and Sb_(2)O_(3),and was transformed into Sb_(2)S_(3)after introducing sulfur at high temperatures.Flotation test results show that flotation recovery of the stibiconite after sulfidation reaches 90.3%.Ultraviolet spectrophotometry tests confirm that adsorption capacity of sodium butyl xanthate(SBX)on surface of the roasted products has a positive relationship with S/Sb mole ratio.XPS analyses indicate that Sb-bearing species including mainly Sb_(2)S_(3),Sb_(2)O_(3)and Sb_(2)(SO_(4))_(3) are formed at the surface of particle after sulfidation.The EPMA analyses verify that the Sb_(2)S_(3)is generated at the outer layer of sample after sulfidation roasting,but the particle interior is mainly composed of antimony oxides.The sulfur atmosphere induces the outward migration of oxygen to form Sb_(2)O_(4).Then,the Sb_(2)O_(4)is transformed into Sb_(2)O_(3)in two pathways,and the Sb_(2)S_(3)is formed.These findings will provide theoretical support for recovering antimony from antimony oxide ores by xanthate flotation methods.