LiMnOand LiNiAlyMnO（x= 0.50;y = 0.05-0.50） powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such...LiMnOand LiNiAlyMnO（x= 0.50;y = 0.05-0.50） powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such as thermo gravimetric analysis（TG/DTA）,X-ray diffraction（XRD）,Fourier transform infrared spectroscopy（FT-IR）,field-emission scanning electron microscopy（FESEM）,transmission electron microscopy（TEM） and electrochemical studies viz.,galvanostatic cycling properties,electrochemical impedance spectroscopy（EIS） and differential capacity curves（dQ/dE）.Finger print XRD patterns of LiMnOand LiNiAlMnOfortify the high degree of crystallinity with better phase purity.FESEM images of the undoped pristine spinel illustrate uniform spherical grains surface morphology with an average particle size of 0.5 μm while Ni doped particles depict the spherical grains growth（50nm） with ice-cube surface morphology.TEM images of the spinel LiMnOshows the uniform spherical morphology with particle size of（100 nm） while low level of Al-doping spinel（LiNio.5Alo.05Mn1.45O4） displaying cloudy particles with agglomerated particles of（50nm）.The LiMnOsamples calcined at 850℃ deliver the discharge capacity of 130 mAh/g in the first cycle corresponds to 94%coiumbic efficiency with capacity fade of 1.5 mAh/g/cycle over the investigated 10 cycles.Among all four dopant compositions investigated,LiNiAlMnOdelivers the maximum discharge capacity of 126 mAh/g during the first cycle and shows the stable cycling performance with low capacity fade of 1 mAh/g/cycle（capacity retention of 92%） over the investigated 10 cycles.Electrochemical impedance studies of spinel LiMnOand LiNiAlMnOdepict the high and low real polarization of 1562 and 1100 Ω.展开更多
To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vi...To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vis DRS techniques.The results showed that single or double doping did not change the crystalline structure and morphology,but the particle size decreased with Ni doping.The band gap energy absorption edge of Ni-B-BiVO4shifted to a longer wavelength compared with undoped,B or Ni single doped BiVO4.More V4+and surface hydroxyl oxygen were observed in BiVO4after Ni-B co-doping.When the optimal mass fraction of Ni is0.30%,the degradation rate of MO in50min is95%for0.3Ni-B-BiVO4sample which also can effectively degrade methyl blue(MB),acid orange(AOII)II and rhodamine B(RhB).The enhanced photocatalytic activity is attributed to the synergistic effects of B and Ni doping.展开更多
Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, p...Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, photocathodic protection and photoelectrochemical properties of TiO2 thin films were investigated. It is indicated that the photoelectrical performance of the Zn?TiO2 films is enhanced with the addition of Zn element compared with the pure-TiO2 film and the largest decline by 897 mV in the electrode potential is achieved under 300 °C heat treatment. SEM?EDS analyses show that Zn element is unevenly distributed in Zn?TiO2 films; XRD patterns reveal that the grain size of Zn?TiO2 is smaller than that of pure-TiO2; FTIR results indicate that Zn - O bond forms on Zn?TiO2 surface. Ultraviolet visible absorption spectra prove that Zn?TiO2 shifts to visible light region.Mott?Shottky curves show that the flat-band potential of Zn?TiO2 is more negative and charge carrier density is bigger than that ofpure-TiO2, implying that under the synergy of the width of the space-charge layer, carrier density and flat-band potential, Zn?TiO2 with 300 °C heat treatment displays the best photocathodic protection performance.展开更多
Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase ...Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase of calcina- tion temperature and prolonging calcination time. The photocatalytic activity was measured for the degradation of an aqueous Rhodamine-B（RhB） solution and gaseous formaldehyde（FAD）. With the increase of calcination temperature and time, the activities increased to a maximum and then decreased. ZnWO4 photocatalyst prepared at 550℃ for I0 h showed the highest activity, which is similar to the photocatalytic activity of P25TiO2 for the degradation of gase-ous FAD. High crystallinity, large surface area, and good dispersion are responsible for the high photocatalytic per- formance of the prepared ZnWO4.展开更多
The rare earth complex Eu(TTA) 3 was successfully encapsulated into MCM 41 mesoporous molecular sieve by the addition of the complex into the sol gel mixture for the synthesis of MCM 41 mesoporous material under m...The rare earth complex Eu(TTA) 3 was successfully encapsulated into MCM 41 mesoporous molecular sieve by the addition of the complex into the sol gel mixture for the synthesis of MCM 41 mesoporous material under microwave radiation. The as synthesized MCM 41 hosted Eu(TTA) 3 mesophase was confirmed to possess hexagonally ordered mesostructure and a uniform crystal size of about 30 nm with XRD and HRTEM techniques. Moreover, the IR spectrum, photoluminescence effect and fluorescence lifetime of the Eu(TTA) 3/MCM 41 hybrid were also studied. An increase in Stokes' shift and no change in luminescence lifetime were observed to the resultant mesophase in comparison with Eu(TTA) 3 in ethanol solution.展开更多
Transparent anatase TiO2 nanometer thin films with photocatalytic activity were prepared via the sol-gel method on soda-lime glass. The thickness , crystalline phase, grain size, surface hydroxyl amount and so on were...Transparent anatase TiO2 nanometer thin films with photocatalytic activity were prepared via the sol-gel method on soda-lime glass. The thickness , crystalline phase, grain size, surface hydroxyl amount and so on were characterized by scanning electron microscopy (SEM) , X-ray diffraction (XRD), transmission electron microscopy ( TEM), X-ray photoelectron spectroscopy (XPS) and UV-visible spectrophotometer ( UV-VIS). The photocatalytic activity of TiO2 thin films was evaluated for the photocatalytic decolorization of aqueous methyl orange . The effects of film thickness on the crystalline phase, grain size, transmittance and photocatalytic activity of nanometer Ti02 thin films were discussed.展开更多
Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kind...Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kinds of BaTiO3 ceramic inks were prepared by mechanical mixing and sol-gel methods,respectively.The effect of preparation parameters,such as quantity of polyacrylic acid(PAA)and solid content,on physicochemical and rheologic properties of the ceramic inks was investigated.The results show that they satisfy the requirements of continuous ink-jet printing.The appearances of printed dots and single printed layers were observed by SEM.The SEM images indicate that dots printed with mixing method ink are in ring shape,and dots printed with sol-gel method ink are in pancake shape,so the printed layer surface with the latter ink is smoother.The causes of these phenomena were discussed.展开更多
A series of red-emitting Ca2_xA12SiOT：xEu^3＋ （x = 1 mol.%-10 tool.%） phosphors were synthesized by the sol-gel method. The effects of annealing temperature and doping concentration on the crystal structure and lum...A series of red-emitting Ca2_xA12SiOT：xEu^3＋ （x = 1 mol.%-10 tool.%） phosphors were synthesized by the sol-gel method. The effects of annealing temperature and doping concentration on the crystal structure and luminescence properties of Ca2A12SiO7：Eu^3＋ phosphors were investigated. X-ray diffraction （XRD） profiles showed that all peaks could be attributed to the tetragonal Ca2A12SiO7 phase when the sample was annealed at 1000℃. Scanning electron microscopy （SEM） micrographs indicate that the phosphors have an irregularly rounded mor- phology with particles of about 200 nm. Excitation spectra showed that the strong broad band at around 258 nm and weak sharp lines in 350-490 nm were attributed to the charge transfer band of Eu^3＋-O^2- and f-f transitions within the 4f^6 configuration of Eu^3＋ ions, respectively. Emission spectra implied that the red luminescence could be attributed to the transitions from the ^5D0 excited level to the 7Fj （J = 0, 1, 2, 3, 4） levels of Eu3＋ions with the main electric dipole transition ^5D0→^7F2 （618 and 620 nm）, and Eu^3＋ ions prefer to occupy a lower symmetry site in the crystal lattice. Moreover, the photoluminescence （PL） intensity was strongly dependent on both the sintering temperature and doping concentration, and the highest PL intensity was observed at an Eu^3＋ concentration x = 7 mol.% after annealing at ll00℃. The obtained Ca2A12SiO7：Eu^＋3＋ phosphor may have potential application for the red lamp phosphor.展开更多
The Bi3＋ doped molybdate-based red-emitting phosphors, LiEu1-xBix（MoO4）2, were successfully synthesized with a sol-gel method. The prepared LiEu1-xBix（MoO4）2 phosphors exhibited pure and intense red emission at 6...The Bi3＋ doped molybdate-based red-emitting phosphors, LiEu1-xBix（MoO4）2, were successfully synthesized with a sol-gel method. The prepared LiEu1-xBix（MoO4）2 phosphors exhibited pure and intense red emission at 613 nm under the excitation of near-UV 394 nm. It was discussed in detail that the influence of the synthesis conditions such as the doping concentration of Bi3, the dose of citric acid, pH of the precursor solution and the sintering temperature on the emission intensity of the phosphors. According to the results, the optimal condition was obtained： the doping concentration of Bi3＋ was 15 mol.%, molar ratio of citric acid to metal ions was 1.5：1, pH of the precursor solution was 1.0 and the sintering temperature was 800 ℃. The X-ray diffraction （XRD） patterns of the LiEuo.85Bi0.15（MoO4）2 phosphor prepared under the optimal condition indicated that the phosphor was single phase with tetragonal scheelite structure. The Commission Intemationale de I＇E- clairage （CIE） chromaticity coordinates of LiEuo.85Bio.15（MoO4）2 were （x=0.655, y=0.345）, which were closer to the national television stan- dard committee （NTSC） standard values （x=0.670, y=0.330） than that of a commercial red phosphor of Y202S：Eu3＋（x=0.630, y=0.350）. This LiEuo.85Bi0As（MoO4）2 red phosphor is a promising candidate for the fabrication of white light-emitting diode （W-LED） with near-UV chips.展开更多
The precursor of ultrafine In 2O 3 powder was prepared by the hydrolysis, peptization and gelation of InCl 3·4H 2O used as raw material. After calcination, ultrafine In 2O 3 powder was obtained. The particl...The precursor of ultrafine In 2O 3 powder was prepared by the hydrolysis, peptization and gelation of InCl 3·4H 2O used as raw material. After calcination, ultrafine In 2O 3 powder was obtained. The particles were characterized by the methods of thermo gravimetric and differential thermal analysis (TG DTA), X ray diffractometry (XRD) and transmission electron microscopy (TEM), respectively.展开更多
Mixed strontium-yttrium borate phosphor Sr3Y2（BO3）4 doped with Eu^3＋ ions was obtained by the sol-gel Pechini method. Crystal structure of the synthesized compound was analyzed by X-ray powder diffraction. Optimal ...Mixed strontium-yttrium borate phosphor Sr3Y2（BO3）4 doped with Eu^3＋ ions was obtained by the sol-gel Pechini method. Crystal structure of the synthesized compound was analyzed by X-ray powder diffraction. Optimal conditions for the synthesis were found. Photophysical properties of the phosphor samples were investigated by collecting excitation and luminescence spectra as well as measuring lumi- nescence lifetime. Judd-Ofelt analysis showed that Eu^3＋ ions occupied Y^3＋ sites in the crystalline network. The studied compound showed a red emission with the quantum yield of 54%-55% and can be potentially used as phosphor for plasma display panels and luminescent tubes.展开更多
TiO2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface w...TiO2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface water, we herein examined the preparation of a P25-TiO2 composite film on a cement substrate via a sol–gel method. In this case, Rhodamine B（Rh B）was employed as the target organic pollutant. The self-generated TiO2 film and the P25-TiO2 composite film were characterized by X-ray diffraction（XRD）, N2 adsorption/desorption measurements, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, and diffuse reflectance spectroscopy（DRS）. The photodegradation efficiencies of the two films were studied by Rh B removal in water under UV（ultraviolet） irradiation. Over 4 day exposure, the P25-TiO2 composite film exhibited higher photocatalytic performance than the self-generated TiO2 film. The photodegradation rate indicated that the efficiency of the P25-TiO2 composite film was enhanced by the addition of the rutile phase Degussa P25 powder. As such, cooperation between the anatase TiO2 and rutile P25 nanoparticles was beneficial for separation of the photo-induced electrons and holes. In addition, the influence of P25 doping on the P25-TiO2 composite films was evaluated. We found that up to a certain saturation point, increased doping enhanced the photodegradation ability of the composite film. Thus, we herein demonstrated that the doping of P25 powders is a simple but effective strategy to prepare a P25-TiO2 composite film on a cement substrate, and the resulting film exhibits excellent removal efficiency in the degradation of organic pollutants.展开更多
Titanium dioxide nanoparticles modified with neodymium in the range of 1 mol% to 5 mol% were prepared with template-free sol-gel method.The structures of obtained samples were characterized by X-ray powder diffraction...Titanium dioxide nanoparticles modified with neodymium in the range of 1 mol% to 5 mol% were prepared with template-free sol-gel method.The structures of obtained samples were characterized by X-ray powder diffraction analysis.X-ray photoelectron spectroscopy,scanning electron microscopy,transmission electron microscopy and diffuse reflectance spectroscopy.The photocatalytic activity of the obtained samples was evaluated by photodegradation of methyl orange in aqueous solution under ultraviolet-visible(λ> 350 nm) and visible(λ> 420 nm) irradiation.The experimental results show that the 1 mol% Nd-doped TiO2 exhibits the highest photocatalytic activity,of which the degradation can reach to 96.5% under visible irradiation.According to the XRD results,the pristine samples are combined with anatase TiO2 and rutile TiO2.while the Nd-doped TiO2 samples are anatase TiO2 only.This transformation has made an obvious promotion of photocatalyst activity after modification.展开更多
The nickel-based catalysts were prepared by the sol-gel method and used for the CH4 reforming with CO2. The effects of the sol-gel method on the specific surface area, catalytic activity, desorption, and reduction per...The nickel-based catalysts were prepared by the sol-gel method and used for the CH4 reforming with CO2. The effects of the sol-gel method on the specific surface area, catalytic activity, desorption, and reduction performances of catalysts were investigated with BET, TPR, and TPD. Compared with the catalyst prepared by the impregnation method, the results indicated that the catalysts prepared by the sol-gel method had larger specific surface area, showing higher catalytic activities and exhibiting perfect desorption and reduction performances. In addition, the modification effects of adding La were studied, and it was found that the 0.75NLBT catalyst constituted of 5wt.%Ni-0.75wt.%La was optimal.展开更多
Nanometer Al_2O_3 is one of new types of functional materials with broad application and development prospects in the future. The basic principle and ways of nanometer Al_2O_3 fabricated using sol-gel technique were i...Nanometer Al_2O_3 is one of new types of functional materials with broad application and development prospects in the future. The basic principle and ways of nanometer Al_2O_3 fabricated using sol-gel technique were introduced, and the factors affecting nanometer Al_2O_3 fabricated using sol-gel method were analyzed. The progress in research on nanometer Al_2O_3 and the application fields of nanometer Al_2O_3 were reviewed. The existing problems and the problems prospect for nanometer Al_2O_3 were pointed out.展开更多
TeOx-SiO2 composite films having third-order nonlinearities were prepared by electrochemically induced sol-gel deposition method on ITO substrate.The third-order optical nonlinearities of the films were measured by Z-...TeOx-SiO2 composite films having third-order nonlinearities were prepared by electrochemically induced sol-gel deposition method on ITO substrate.The third-order optical nonlinearities of the films were measured by Z-scan technique.The third-order nonlinear susceptibilities（χ^（（3））） of the as-prepared films are 5.9×10^（-7） to 4.29×10^（-6）esu.The surface morphology and composition of the films were characterized by SEM/EDX,which identified that Te metallic particles well dispersed in TeO_x-SiO_2 gel films.展开更多
Highly ordered nanowire/tube arrays of Ni0.5Zn0.5Fe2O4were fabricated by the sol-gel method in the pores of anodic alumina membrane （AAM）. Whether nanowires or nanotubes were fabricated depends on immersion time. Th...Highly ordered nanowire/tube arrays of Ni0.5Zn0.5Fe2O4were fabricated by the sol-gel method in the pores of anodic alumina membrane （AAM）. Whether nanowires or nanotubes were fabricated depends on immersion time. The immersion time was 15- 40 s for nanotubes and over 60 s for nanowires. The topography and crystalline structure of the nanowire arrays were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. It was found that the length and diameter of the Ni0.5Zn0.5Fe2O4 nanowires are related to the thickness of the AAM and the diameter of the pores. The results indicated that the Ni0.5Zn0.5Fe2O4 nanowires are uniform and parallel to each other.展开更多
Nanocrystal SmBO3 powders were synthesized by nitrate-citrate sol-gel combustion method. The phase evolution, morphologies and absorbency of the synthesized powders were characterized by X-ray diffraction （XRD）, Fie...Nanocrystal SmBO3 powders were synthesized by nitrate-citrate sol-gel combustion method. The phase evolution, morphologies and absorbency of the synthesized powders were characterized by X-ray diffraction （XRD）, Field emission scanning electronic microscope （FESEM）, Fourier transform infrared spectroscopy （FFIR） and UV-3101PC spectrophotometer （UVPC）, respectively. XRD and FESEM results showed that pure SmBO3 phase was obtained at 750 ℃, with an average original particle size of about 100 nm. FTIR showed that there were apparently concentrated absorbent peaks between 500 and 1400 cm^-1. Moreover, the reflectivity of the powders apparently decreased at the wavelength between 1.05 and 1.15 μm. Therefore, SmBO3 might be a kind of absorbent material for infrared laser.展开更多
Eu 2+, Dy 3+ co-doped nanocrystalline strontium aluminate phosphor powders with brightness and long afterglow were synthesized by the sol-gel method at 1200 ℃ for 2 h. The samples were characterized by X-ray diffract...Eu 2+, Dy 3+ co-doped nanocrystalline strontium aluminate phosphor powders with brightness and long afterglow were synthesized by the sol-gel method at 1200 ℃ for 2 h. The samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results of XRD show that the single crystalline phase is α-SrAl_2O_4. According to the observation of SEM, the particles of the samples are needle-like. Compared with the samples synthesized by solid state reaction, the grain size of the sol-gel method is to nanometer grade. A clear blue shift occurs in the excitation and emission spectra. The blue shift in nanocrystalline SrAl_2O_4∶Eu, Dy phosphor can be attributed to the quantum-size-effect of the luminescent particles.展开更多
SiO2-CaO-MgO glass and glass-ceramic powder doped with Nd3＋ were synthesized with sol-gel method. Tetraethylorthosilicate （TEOS）, Ca（NO3）2？4H2O, Mg（NO3）2？6H2O, Nd（NO3）3？6H2O, ethanol, distilled water, and ...SiO2-CaO-MgO glass and glass-ceramic powder doped with Nd3＋ were synthesized with sol-gel method. Tetraethylorthosilicate （TEOS）, Ca（NO3）2？4H2O, Mg（NO3）2？6H2O, Nd（NO3）3？6H2O, ethanol, distilled water, and HNO3 were used as starting materials. The synthesized powder’s properties were examined with simultaneous thermal analysis （STA）, X-ray diffraction （XRD）, photoluminescence （PL） and scanning electron microscopy （SEM） analysis. The STA curves showed that the softening point and crystallization temperatures were shifted to higher temperatures with increasing dopant content. Regarding XRD patterns of glass samples, Nd was found to act as an intermediate oxide in glass matrix. The XRD patterns of glass-ceramic samples indicated that bredigite and akermanite crystallized in the glass matrix after heat treating at 900 oC. The fluorescence spectra showed that glass-ceramics emitted much stronger irradiation than glasses with the same dopant content. The SEM images illustrated uniform and homogeneous distribution of applied oxides in glass and glass-ceramic compositions.展开更多
基金support given under the "Brain Pool Program of the Korean Federation of Science and Technology Societies" (KOFST), Republic of South Koreasupported by the Human Resources Development Program (No. 20124010203270) of the Korea Institute of Energy Technology EvaluationPlanning (KETEP) grant funded by the Korea Government Ministry of Trade, Industry and Energy
文摘LiMnOand LiNiAlyMnO（x= 0.50;y = 0.05-0.50） powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such as thermo gravimetric analysis（TG/DTA）,X-ray diffraction（XRD）,Fourier transform infrared spectroscopy（FT-IR）,field-emission scanning electron microscopy（FESEM）,transmission electron microscopy（TEM） and electrochemical studies viz.,galvanostatic cycling properties,electrochemical impedance spectroscopy（EIS） and differential capacity curves（dQ/dE）.Finger print XRD patterns of LiMnOand LiNiAlMnOfortify the high degree of crystallinity with better phase purity.FESEM images of the undoped pristine spinel illustrate uniform spherical grains surface morphology with an average particle size of 0.5 μm while Ni doped particles depict the spherical grains growth（50nm） with ice-cube surface morphology.TEM images of the spinel LiMnOshows the uniform spherical morphology with particle size of（100 nm） while low level of Al-doping spinel（LiNio.5Alo.05Mn1.45O4） displaying cloudy particles with agglomerated particles of（50nm）.The LiMnOsamples calcined at 850℃ deliver the discharge capacity of 130 mAh/g in the first cycle corresponds to 94%coiumbic efficiency with capacity fade of 1.5 mAh/g/cycle over the investigated 10 cycles.Among all four dopant compositions investigated,LiNiAlMnOdelivers the maximum discharge capacity of 126 mAh/g during the first cycle and shows the stable cycling performance with low capacity fade of 1 mAh/g/cycle（capacity retention of 92%） over the investigated 10 cycles.Electrochemical impedance studies of spinel LiMnOand LiNiAlMnOdepict the high and low real polarization of 1562 and 1100 Ω.
基金Projects (21207093,51004072) supported by the National Natural Science Foundation of China for YouthProject (LJQ2014023) supported by the Liaoning Excellent Talents in University,China+1 种基金Project (L20150178) supported by the General Scientific Research Projects Foundation of Liaoning Educational Committee,ChinaProject (N140303002) supported by the Fundamental Research Funds for the Central Universities,China
文摘To enhance the photocatalytic activity of B-BiVO4,Ni-doped B?BiVO4photocatalyst(Ni-B-BiVO4)was synthesized through sol-gel and impregnation method.The photocatalysts were characterized by XPS,XRD,SEM,EDS,BET and UV-Vis DRS techniques.The results showed that single or double doping did not change the crystalline structure and morphology,but the particle size decreased with Ni doping.The band gap energy absorption edge of Ni-B-BiVO4shifted to a longer wavelength compared with undoped,B or Ni single doped BiVO4.More V4+and surface hydroxyl oxygen were observed in BiVO4after Ni-B co-doping.When the optimal mass fraction of Ni is0.30%,the degradation rate of MO in50min is95%for0.3Ni-B-BiVO4sample which also can effectively degrade methyl blue(MB),acid orange(AOII)II and rhodamine B(RhB).The enhanced photocatalytic activity is attributed to the synergistic effects of B and Ni doping.
基金Project(cstc2011jj A50008)supported by the Natural Science Foundation of Chongqing,ChinaProject(14ZB0025)supported by Education Department of Sichuan Province,China
文摘Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, photocathodic protection and photoelectrochemical properties of TiO2 thin films were investigated. It is indicated that the photoelectrical performance of the Zn?TiO2 films is enhanced with the addition of Zn element compared with the pure-TiO2 film and the largest decline by 897 mV in the electrode potential is achieved under 300 °C heat treatment. SEM?EDS analyses show that Zn element is unevenly distributed in Zn?TiO2 films; XRD patterns reveal that the grain size of Zn?TiO2 is smaller than that of pure-TiO2; FTIR results indicate that Zn - O bond forms on Zn?TiO2 surface. Ultraviolet visible absorption spectra prove that Zn?TiO2 shifts to visible light region.Mott?Shottky curves show that the flat-band potential of Zn?TiO2 is more negative and charge carrier density is bigger than that ofpure-TiO2, implying that under the synergy of the width of the space-charge layer, carrier density and flat-band potential, Zn?TiO2 with 300 °C heat treatment displays the best photocathodic protection performance.
基金Supported by the National Natural Science Foundation of China(Nos.20433010and20571047)Specialized Research Fundfor the Doctoral Program of Higher Education(No.20060003082).
文摘Nanosized ZnWO4 photocatalysts were successfully synthesized via the sol-gel process in a temperature range of 450-800℃. The grain size, crystal size, and crystallinity of ZnWO4 particles increased with the increase of calcina- tion temperature and prolonging calcination time. The photocatalytic activity was measured for the degradation of an aqueous Rhodamine-B（RhB） solution and gaseous formaldehyde（FAD）. With the increase of calcination temperature and time, the activities increased to a maximum and then decreased. ZnWO4 photocatalyst prepared at 550℃ for I0 h showed the highest activity, which is similar to the photocatalytic activity of P25TiO2 for the degradation of gase-ous FAD. High crystallinity, large surface area, and good dispersion are responsible for the high photocatalytic per- formance of the prepared ZnWO4.
文摘The rare earth complex Eu(TTA) 3 was successfully encapsulated into MCM 41 mesoporous molecular sieve by the addition of the complex into the sol gel mixture for the synthesis of MCM 41 mesoporous material under microwave radiation. The as synthesized MCM 41 hosted Eu(TTA) 3 mesophase was confirmed to possess hexagonally ordered mesostructure and a uniform crystal size of about 30 nm with XRD and HRTEM techniques. Moreover, the IR spectrum, photoluminescence effect and fluorescence lifetime of the Eu(TTA) 3/MCM 41 hybrid were also studied. An increase in Stokes' shift and no change in luminescence lifetime were observed to the resultant mesophase in comparison with Eu(TTA) 3 in ethanol solution.
基金This work was financially supported by Foundation for Uni-versity Key Teacher by the Ministry of Education, the National Natu-ral Science Foundation of China (No. 50072016) and the Key Re-search Project of the Ministry of Education(No.99087)
文摘Transparent anatase TiO2 nanometer thin films with photocatalytic activity were prepared via the sol-gel method on soda-lime glass. The thickness , crystalline phase, grain size, surface hydroxyl amount and so on were characterized by scanning electron microscopy (SEM) , X-ray diffraction (XRD), transmission electron microscopy ( TEM), X-ray photoelectron spectroscopy (XPS) and UV-visible spectrophotometer ( UV-VIS). The photocatalytic activity of TiO2 thin films was evaluated for the photocatalytic decolorization of aqueous methyl orange . The effects of film thickness on the crystalline phase, grain size, transmittance and photocatalytic activity of nanometer Ti02 thin films were discussed.
基金Project(106151)supported by the Major Program of the Ministry of Education of ChinaProject(59842001)supported by the National Natural Science Foundation of China
文摘Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kinds of BaTiO3 ceramic inks were prepared by mechanical mixing and sol-gel methods,respectively.The effect of preparation parameters,such as quantity of polyacrylic acid(PAA)and solid content,on physicochemical and rheologic properties of the ceramic inks was investigated.The results show that they satisfy the requirements of continuous ink-jet printing.The appearances of printed dots and single printed layers were observed by SEM.The SEM images indicate that dots printed with mixing method ink are in ring shape,and dots printed with sol-gel method ink are in pancake shape,so the printed layer surface with the latter ink is smoother.The causes of these phenomena were discussed.
基金supported by the National Natural Science Foundation of China (No. 10874160)the Science and Technology Foundation of Guangdong Province,China (No. 2007173)the Science and Technology Foundation of Jiangmen City, China (No. 2007028)
文摘A series of red-emitting Ca2_xA12SiOT：xEu^3＋ （x = 1 mol.%-10 tool.%） phosphors were synthesized by the sol-gel method. The effects of annealing temperature and doping concentration on the crystal structure and luminescence properties of Ca2A12SiO7：Eu^3＋ phosphors were investigated. X-ray diffraction （XRD） profiles showed that all peaks could be attributed to the tetragonal Ca2A12SiO7 phase when the sample was annealed at 1000℃. Scanning electron microscopy （SEM） micrographs indicate that the phosphors have an irregularly rounded mor- phology with particles of about 200 nm. Excitation spectra showed that the strong broad band at around 258 nm and weak sharp lines in 350-490 nm were attributed to the charge transfer band of Eu^3＋-O^2- and f-f transitions within the 4f^6 configuration of Eu^3＋ ions, respectively. Emission spectra implied that the red luminescence could be attributed to the transitions from the ^5D0 excited level to the 7Fj （J = 0, 1, 2, 3, 4） levels of Eu3＋ions with the main electric dipole transition ^5D0→^7F2 （618 and 620 nm）, and Eu^3＋ ions prefer to occupy a lower symmetry site in the crystal lattice. Moreover, the photoluminescence （PL） intensity was strongly dependent on both the sintering temperature and doping concentration, and the highest PL intensity was observed at an Eu^3＋ concentration x = 7 mol.% after annealing at ll00℃. The obtained Ca2A12SiO7：Eu^＋3＋ phosphor may have potential application for the red lamp phosphor.
基金Project supported by National Natural Science Foundation of China (NSFC20803097, NSFC20603049)Natural Science Foundation of Chongqing (CSTC2011AB4056, CSTC2009BA4023)the Fundamental Research Funds for the Central Universities (CDJZR10220005 and CDJRC10220002)
文摘The Bi3＋ doped molybdate-based red-emitting phosphors, LiEu1-xBix（MoO4）2, were successfully synthesized with a sol-gel method. The prepared LiEu1-xBix（MoO4）2 phosphors exhibited pure and intense red emission at 613 nm under the excitation of near-UV 394 nm. It was discussed in detail that the influence of the synthesis conditions such as the doping concentration of Bi3, the dose of citric acid, pH of the precursor solution and the sintering temperature on the emission intensity of the phosphors. According to the results, the optimal condition was obtained： the doping concentration of Bi3＋ was 15 mol.%, molar ratio of citric acid to metal ions was 1.5：1, pH of the precursor solution was 1.0 and the sintering temperature was 800 ℃. The X-ray diffraction （XRD） patterns of the LiEuo.85Bi0.15（MoO4）2 phosphor prepared under the optimal condition indicated that the phosphor was single phase with tetragonal scheelite structure. The Commission Intemationale de I＇E- clairage （CIE） chromaticity coordinates of LiEuo.85Bio.15（MoO4）2 were （x=0.655, y=0.345）, which were closer to the national television stan- dard committee （NTSC） standard values （x=0.670, y=0.330） than that of a commercial red phosphor of Y202S：Eu3＋（x=0.630, y=0.350）. This LiEuo.85Bi0As（MoO4）2 red phosphor is a promising candidate for the fabrication of white light-emitting diode （W-LED） with near-UV chips.
文摘The precursor of ultrafine In 2O 3 powder was prepared by the hydrolysis, peptization and gelation of InCl 3·4H 2O used as raw material. After calcination, ultrafine In 2O 3 powder was obtained. The particles were characterized by the methods of thermo gravimetric and differential thermal analysis (TG DTA), X ray diffractometry (XRD) and transmission electron microscopy (TEM), respectively.
基金Project supported by International Visegrad Fund (51000547 (2010-2011))
文摘Mixed strontium-yttrium borate phosphor Sr3Y2（BO3）4 doped with Eu^3＋ ions was obtained by the sol-gel Pechini method. Crystal structure of the synthesized compound was analyzed by X-ray powder diffraction. Optimal conditions for the synthesis were found. Photophysical properties of the phosphor samples were investigated by collecting excitation and luminescence spectra as well as measuring lumi- nescence lifetime. Judd-Ofelt analysis showed that Eu^3＋ ions occupied Y^3＋ sites in the crystalline network. The studied compound showed a red emission with the quantum yield of 54%-55% and can be potentially used as phosphor for plasma display panels and luminescent tubes.
基金supported by the National Science Funds for Creative Research Groups of China (No. 51421006)the National Major Projects of Water Pollution Control and Management Technology (No. 2017ZX07204003)+2 种基金the National Key Plan for Research and Development of China (2016YFC0502203)the Key Program of National Natural Science Foundation of China (No. 91647206)the Qing Lan Project of Jiangsu Province, and PAPD
文摘TiO2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface water, we herein examined the preparation of a P25-TiO2 composite film on a cement substrate via a sol–gel method. In this case, Rhodamine B（Rh B）was employed as the target organic pollutant. The self-generated TiO2 film and the P25-TiO2 composite film were characterized by X-ray diffraction（XRD）, N2 adsorption/desorption measurements, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, and diffuse reflectance spectroscopy（DRS）. The photodegradation efficiencies of the two films were studied by Rh B removal in water under UV（ultraviolet） irradiation. Over 4 day exposure, the P25-TiO2 composite film exhibited higher photocatalytic performance than the self-generated TiO2 film. The photodegradation rate indicated that the efficiency of the P25-TiO2 composite film was enhanced by the addition of the rutile phase Degussa P25 powder. As such, cooperation between the anatase TiO2 and rutile P25 nanoparticles was beneficial for separation of the photo-induced electrons and holes. In addition, the influence of P25 doping on the P25-TiO2 composite films was evaluated. We found that up to a certain saturation point, increased doping enhanced the photodegradation ability of the composite film. Thus, we herein demonstrated that the doping of P25 powders is a simple but effective strategy to prepare a P25-TiO2 composite film on a cement substrate, and the resulting film exhibits excellent removal efficiency in the degradation of organic pollutants.
基金supported by the National Natural Science Foundation of China(51275203)Key Scientific and Technological Project of Jilin Province(20140204052GX,20180201074GX)+2 种基金China Postdoctoral Science Foundation(2017M611321)Project of Education Department of Jilin Province(JJKH20180130KJ)Open Project of State Key Laboratory of Inorganic Synthesis and Preparative Chemistry,College of Chemistry,Jilin University(2019-8).
文摘Titanium dioxide nanoparticles modified with neodymium in the range of 1 mol% to 5 mol% were prepared with template-free sol-gel method.The structures of obtained samples were characterized by X-ray powder diffraction analysis.X-ray photoelectron spectroscopy,scanning electron microscopy,transmission electron microscopy and diffuse reflectance spectroscopy.The photocatalytic activity of the obtained samples was evaluated by photodegradation of methyl orange in aqueous solution under ultraviolet-visible(λ> 350 nm) and visible(λ> 420 nm) irradiation.The experimental results show that the 1 mol% Nd-doped TiO2 exhibits the highest photocatalytic activity,of which the degradation can reach to 96.5% under visible irradiation.According to the XRD results,the pristine samples are combined with anatase TiO2 and rutile TiO2.while the Nd-doped TiO2 samples are anatase TiO2 only.This transformation has made an obvious promotion of photocatalyst activity after modification.
基金supported by the Jiangxi Provincial Department of Education
文摘The nickel-based catalysts were prepared by the sol-gel method and used for the CH4 reforming with CO2. The effects of the sol-gel method on the specific surface area, catalytic activity, desorption, and reduction performances of catalysts were investigated with BET, TPR, and TPD. Compared with the catalyst prepared by the impregnation method, the results indicated that the catalysts prepared by the sol-gel method had larger specific surface area, showing higher catalytic activities and exhibiting perfect desorption and reduction performances. In addition, the modification effects of adding La were studied, and it was found that the 0.75NLBT catalyst constituted of 5wt.%Ni-0.75wt.%La was optimal.
文摘Nanometer Al_2O_3 is one of new types of functional materials with broad application and development prospects in the future. The basic principle and ways of nanometer Al_2O_3 fabricated using sol-gel technique were introduced, and the factors affecting nanometer Al_2O_3 fabricated using sol-gel method were analyzed. The progress in research on nanometer Al_2O_3 and the application fields of nanometer Al_2O_3 were reviewed. The existing problems and the problems prospect for nanometer Al_2O_3 were pointed out.
基金supported by Academic Program of Natural Science Foundation Project of CQ CSTC(No 2008BC4003)the Foundation of State Key Laboratory of Physical Chemistry of Solid Surfaces of Xiamen University(No2007)
文摘TeOx-SiO2 composite films having third-order nonlinearities were prepared by electrochemically induced sol-gel deposition method on ITO substrate.The third-order optical nonlinearities of the films were measured by Z-scan technique.The third-order nonlinear susceptibilities（χ^（（3））） of the as-prepared films are 5.9×10^（-7） to 4.29×10^（-6）esu.The surface morphology and composition of the films were characterized by SEM/EDX,which identified that Te metallic particles well dispersed in TeO_x-SiO_2 gel films.
文摘Highly ordered nanowire/tube arrays of Ni0.5Zn0.5Fe2O4were fabricated by the sol-gel method in the pores of anodic alumina membrane （AAM）. Whether nanowires or nanotubes were fabricated depends on immersion time. The immersion time was 15- 40 s for nanotubes and over 60 s for nanowires. The topography and crystalline structure of the nanowire arrays were characterized by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and X-ray diffraction （XRD）. It was found that the length and diameter of the Ni0.5Zn0.5Fe2O4 nanowires are related to the thickness of the AAM and the diameter of the pores. The results indicated that the Ni0.5Zn0.5Fe2O4 nanowires are uniform and parallel to each other.
基金supported by the 973 Research Project of China (6134502)
文摘Nanocrystal SmBO3 powders were synthesized by nitrate-citrate sol-gel combustion method. The phase evolution, morphologies and absorbency of the synthesized powders were characterized by X-ray diffraction （XRD）, Field emission scanning electronic microscope （FESEM）, Fourier transform infrared spectroscopy （FFIR） and UV-3101PC spectrophotometer （UVPC）, respectively. XRD and FESEM results showed that pure SmBO3 phase was obtained at 750 ℃, with an average original particle size of about 100 nm. FTIR showed that there were apparently concentrated absorbent peaks between 500 and 1400 cm^-1. Moreover, the reflectivity of the powders apparently decreased at the wavelength between 1.05 and 1.15 μm. Therefore, SmBO3 might be a kind of absorbent material for infrared laser.
文摘Eu 2+, Dy 3+ co-doped nanocrystalline strontium aluminate phosphor powders with brightness and long afterglow were synthesized by the sol-gel method at 1200 ℃ for 2 h. The samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results of XRD show that the single crystalline phase is α-SrAl_2O_4. According to the observation of SEM, the particles of the samples are needle-like. Compared with the samples synthesized by solid state reaction, the grain size of the sol-gel method is to nanometer grade. A clear blue shift occurs in the excitation and emission spectra. The blue shift in nanocrystalline SrAl_2O_4∶Eu, Dy phosphor can be attributed to the quantum-size-effect of the luminescent particles.
基金supported by the Iran Nanotechnology Initiative Council(INIC)
文摘SiO2-CaO-MgO glass and glass-ceramic powder doped with Nd3＋ were synthesized with sol-gel method. Tetraethylorthosilicate （TEOS）, Ca（NO3）2？4H2O, Mg（NO3）2？6H2O, Nd（NO3）3？6H2O, ethanol, distilled water, and HNO3 were used as starting materials. The synthesized powder’s properties were examined with simultaneous thermal analysis （STA）, X-ray diffraction （XRD）, photoluminescence （PL） and scanning electron microscopy （SEM） analysis. The STA curves showed that the softening point and crystallization temperatures were shifted to higher temperatures with increasing dopant content. Regarding XRD patterns of glass samples, Nd was found to act as an intermediate oxide in glass matrix. The XRD patterns of glass-ceramic samples indicated that bredigite and akermanite crystallized in the glass matrix after heat treating at 900 oC. The fluorescence spectra showed that glass-ceramics emitted much stronger irradiation than glasses with the same dopant content. The SEM images illustrated uniform and homogeneous distribution of applied oxides in glass and glass-ceramic compositions.