In a fusion reactor,plasma-facing tungsten(W)materials inevitably suffer severe thermal shock,and the performance of W materials under repetitive high heat loads is one of the key concerns for long-term stable operati...In a fusion reactor,plasma-facing tungsten(W)materials inevitably suffer severe thermal shock,and the performance of W materials under repetitive high heat loads is one of the key concerns for long-term stable operation of the reactor.In this work,the microstructural evolution and thermal fatigue resistance of two representative W-0.5 wt.%ZrC(WZC)and W-1.0 wt.% Y_(2)O_(3)(WYO)composites were investigated under cyclic heat loads.Due to the intrinsic properties of ZrC and Y_(2)O_(3)particles such as coefficients of thermal expansion,particle size and distributions in W grains,the WZC composite exhibited a better thermal shock resistance than WYO.After thermal loads with the absorbed power density(APD)≥22 MW/m^(2),WYO showed obvious grain growth,Y_(2)O_(3)particles shedding and degradation of mechanical properties.While,in the case of WZC,these damage behaviors only occurred when APD≥25 MW/m^(2).Furthermore,an interesting crack mechanism in W composites was revealed due to interface debonding and progressive shedding of second-phase particles from the W matrix.The microstructures and tensile properties of the thermally loaded WZC and WYO specimens were also investigated and the correlations between the microstructure evolution and performance degradation are demonstrated.The results are useful for evaluating the thermal fatigue resistance of oxide/carbide dispersion strengthened W composites and their application in future fusion reactors.展开更多
基金supported by the National Key Research and Development Program of China(Nos.2019YFE03110200,2017YFE0302400,and 2019YFE03120001)the National Natural Science Foundation of China(Nos.11735015,52171084,52173303,U1967211)+1 种基金Anhui Provincial Natural Science Foundation(No.1908085J17)the HFIPS Director’s Fund(Nos.YZJJZX202012,YZJJ202206-CX,BJPY2021A05).
文摘In a fusion reactor,plasma-facing tungsten(W)materials inevitably suffer severe thermal shock,and the performance of W materials under repetitive high heat loads is one of the key concerns for long-term stable operation of the reactor.In this work,the microstructural evolution and thermal fatigue resistance of two representative W-0.5 wt.%ZrC(WZC)and W-1.0 wt.% Y_(2)O_(3)(WYO)composites were investigated under cyclic heat loads.Due to the intrinsic properties of ZrC and Y_(2)O_(3)particles such as coefficients of thermal expansion,particle size and distributions in W grains,the WZC composite exhibited a better thermal shock resistance than WYO.After thermal loads with the absorbed power density(APD)≥22 MW/m^(2),WYO showed obvious grain growth,Y_(2)O_(3)particles shedding and degradation of mechanical properties.While,in the case of WZC,these damage behaviors only occurred when APD≥25 MW/m^(2).Furthermore,an interesting crack mechanism in W composites was revealed due to interface debonding and progressive shedding of second-phase particles from the W matrix.The microstructures and tensile properties of the thermally loaded WZC and WYO specimens were also investigated and the correlations between the microstructure evolution and performance degradation are demonstrated.The results are useful for evaluating the thermal fatigue resistance of oxide/carbide dispersion strengthened W composites and their application in future fusion reactors.
