This study discusses the experimental result of the viscoplastic response and col- lapse of sharp-notched 316L stainless steel tubes with different notched depths subjected to cyclic bending. The tube bending machine ...This study discusses the experimental result of the viscoplastic response and col- lapse of sharp-notched 316L stainless steel tubes with different notched depths subjected to cyclic bending. The tube bending machine and curvature-ovalization measurement apparatus were used for conducting the symmetric curvature-controlled cyclic bending. To highlight the viscoplastic behavior, three different curvature-rates, 0.0035, 0.035 and 0.35 m-1s-1, were controlled. Ob- servations of a certain curvature-rate reveal that five almost parallel lines corresponding to five different notch-depth （0.2, 0.4, 0.6, 0.8 and 1.0 mm） tubes were presented in the experimental relationship between the cyclic controlled curvature and the number of cycles needed to pro- duce buckling on a log-log scale. However, the slopes for the three different curvature-rates are different. An empirical formulation was proposed to simulate the aforementioned relationship. When comparing with the experimental findings, the simulation was in good agreement with the experimental data.展开更多
In this paper, the mechanical behavior and buckling failure of SUS304 stainless steel tubes with different local sharp-notched depths subjected to cyclic bending were experimentally investigated. It can be seen that t...In this paper, the mechanical behavior and buckling failure of SUS304 stainless steel tubes with different local sharp-notched depths subjected to cyclic bending were experimentally investigated. It can be seen that the experimental moment-curvature relationship exhibits cyclic hardening and becomes a steady loop after a few cycles. However, the experimental ovalization-curvature relationship exhibits an increasing and ratcheting manner with the number of the bending cycles. In addition, higher notch depth of a tube leads to a more severe unsymmetrical trend of the ovalization-curvature relationship. It has been observed that the notch depth has almost no influence on the moment-curvature relationship. But, it has a strong influence on the ovalization-curvature relationship. Finally, the theoretical model proposed by Kyriakides and Shaw [1] was used in this study for simulating the controlled curvature-number of cycles to produce buckling relationship. Through comparison with the experimental data, the theoretical model can properly simulate the experimental展开更多
基金the support of the National Science Council under grant NSC 98-2221-E006-058
文摘This study discusses the experimental result of the viscoplastic response and col- lapse of sharp-notched 316L stainless steel tubes with different notched depths subjected to cyclic bending. The tube bending machine and curvature-ovalization measurement apparatus were used for conducting the symmetric curvature-controlled cyclic bending. To highlight the viscoplastic behavior, three different curvature-rates, 0.0035, 0.035 and 0.35 m-1s-1, were controlled. Ob- servations of a certain curvature-rate reveal that five almost parallel lines corresponding to five different notch-depth （0.2, 0.4, 0.6, 0.8 and 1.0 mm） tubes were presented in the experimental relationship between the cyclic controlled curvature and the number of cycles needed to pro- duce buckling on a log-log scale. However, the slopes for the three different curvature-rates are different. An empirical formulation was proposed to simulate the aforementioned relationship. When comparing with the experimental findings, the simulation was in good agreement with the experimental data.
文摘In this paper, the mechanical behavior and buckling failure of SUS304 stainless steel tubes with different local sharp-notched depths subjected to cyclic bending were experimentally investigated. It can be seen that the experimental moment-curvature relationship exhibits cyclic hardening and becomes a steady loop after a few cycles. However, the experimental ovalization-curvature relationship exhibits an increasing and ratcheting manner with the number of the bending cycles. In addition, higher notch depth of a tube leads to a more severe unsymmetrical trend of the ovalization-curvature relationship. It has been observed that the notch depth has almost no influence on the moment-curvature relationship. But, it has a strong influence on the ovalization-curvature relationship. Finally, the theoretical model proposed by Kyriakides and Shaw [1] was used in this study for simulating the controlled curvature-number of cycles to produce buckling relationship. Through comparison with the experimental data, the theoretical model can properly simulate the experimental
基金Supported by The National Natural Science Foundation of China(Grant No.51479153)The Fundamental Research Funds for the Central Universities(No.2013-JL-007)